Compression-resistant waterproof environment-friendly coating

An environmentally friendly coating, pigment and filler technology, applied in the direction of anti-corrosion coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as adverse effects on people and the environment, poor elongation of heat-insulating coatings, general anti-corrosion effects, etc., to achieve excellent Stretch ability, improve stretch and waterproof performance, improve the effect of anti-corrosion performance

Active Publication Date: 2022-08-05
海威(海南)环境科技有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, relatively mature foreign technologies include Japanese patent JP98-120946 heat insulation coating, although the effect is good, but it is an oily coating, which will have adverse effects on people and the environment during production and use, and the anti-corrosion effect is general
In addition, in cold regions, exposed metal pipes are prone to bursting accidents in winter, especially the thermal insulation filler contains more inorganic fillers, and there is no good way to avoid problems such as poor elongation of the coating.
[0004] In order to overcome the problem of poor elongation of the existing heat-insulating coating, the present invention discloses a pressure-resistant and waterproof water-resistant coating based on compounded acrylic resin and polyurea resin combined with various heat-insulating fillers and graphene nanosheets. Coating formula and preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compression-resistant waterproof environment-friendly coating
  • Compression-resistant waterproof environment-friendly coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 100g of titanium dioxide, 70g of magnesium sulfate, 40g of calcium carbonate, 10g of bentonite and 10g of dispersant were added to 200g of deionized water, and the stirring speed was 1000 rpm for 1 hour, and then 120g of nano-ceramic microbeads and 100g of hollow glass 1g toughening agent (liquid nitrile rubber), 300g acrylic resin, 40g 2,4-toluene diisocyanate, 20g ethylenediamine, and 20g graphene nanosheets were added to the mixture, and the stirring speed was reduced to 500 rpm and continued stirring for 50 minute. 10g of defoaming agent, 12g of film-forming agent, 4g of leveling agent and 4g of preservative were continuously stirred for 30 minutes to obtain a pressure-resistant waterproof and environmentally friendly coating, and 0.4g of dibutyltin dilaurate was added during construction.

Embodiment 2

[0025] 100g of titanium dioxide, 70g of magnesium sulfate, 40g of calcium carbonate, 10g of bentonite and 10g of dispersant were added to 200g of deionized water, and the stirring speed was 1000 rpm for 1 hour, and then 120g of nano-ceramic microbeads and 100g of hollow glass 300g of acrylic resin, 40g of 2,4-toluene diisocyanate, 20g of ethylenediamine, and 20g of graphene were added to the mixed solution, and the stirring speed was reduced to 500 rpm and continued stirring for 50 minutes. 10g of defoamer, 12g of film-forming agent, 4g of A leveling agent and 4 g of a preservative are added, and stirring is continued for 30 minutes to obtain a pressure-resistant, waterproof and environmentally friendly paint. 0.4 g of dibutyltin dilaurate was added during construction.

Embodiment 3

[0027] Add 100g titanium dioxide, 70g magnesium sulfate, 40g calcium carbonate, 10g bentonite and 10g dispersant to 200g deionized water, stir at 1000 rpm, stir for 1 hour, then add 120g ceramic microbeads, 100g glass microbeads, 300g acrylic acid Resin, 4g 2,4-toluene diisocyanate, 20g ethylenediamine, 20g graphene were added to the mixed solution, the stirring speed was reduced to 500 rpm and stirring was continued for 50 minutes, 10g defoamer, 12g film-forming agent, 4g leveling agent and 4 g of preservatives, and continued stirring for 30 minutes to obtain a pressure-resistant, waterproof and environmentally friendly paint. No dibutyltin dilaurate was added during construction.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a compression-resistant waterproof environment-friendly coating which is prepared from 20 to 40 parts of film-forming resin, 3 to 5 parts of 2, 4-toluene diisocyanate, 1 to 2 parts of ethylenediamine, 15 to 35 parts of pigment and filler, 2 to 4 parts of auxiliaries, 0.05 to 0.1 part of flexibilizer, 2 parts of graphene nanosheets, 8 to 12 parts of nano ceramic, 5 to 10 parts of hollow glass beads and 10 to 20 parts of deionized water, and discloses a preparation method of the compression-resistant waterproof environment-friendly coating. The invention has the following beneficial effects: the coating can realize heat insulation in a manner of reflecting sunlight, the reflectivity to sunlight is up to 90%, the hemispherical emissivity is 0.9, the ductility reaches 105%, and the coating has excellent waterproof performance, outstanding corrosion resistance, strong weatherability and chemical corrosion resistance. The coating can be used for heat insulation of chemical storage tanks, heat insulation of buildings, water resistance, explosion prevention of pipelines in winter and the like, and has the characteristics of strong adhesive force, good flexibility, long service life and the like.

Description

technical field [0001] The invention relates to a pressure-resistant, waterproof and environment-friendly paint and a preparation method thereof, which are suitable for anti-corrosion, waterproof and thermal insulation of chemical storage tanks and civil buildings and explosion-proof of metal pipes in winter. Background technique [0002] In recent years, the demand and consumption of energy in various countries in the world have increased year by year, which is in contradiction with the shortage of energy. As one of the best countries in global economic development, my country's dependence on energy is also increasing. In my country's energy consumption sector, building and industrial energy consumption is the highest. Therefore, the development of new energy-saving materials is of great significance for building and industrial energy conservation. [0003] As an effective material for preventing storage tank and building temperature, thermal insulation coatings have attr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D175/02C09D7/61C09D5/08
CPCC09D133/00C09D7/61C09D7/70C09D5/08C08K2201/011C08L2203/18C08L75/02C08K7/18C08K7/28C08K3/042
Inventor 郑毅姜淑娟
Owner 海威(海南)环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com