Soil firming agent

A technology of soil stabilizer and chemical activator, which is applied in the direction of soil conditioning materials, chemical instruments and methods, organic fertilizers, etc., and can solve problems such as large energy consumption and mineral resources, poor soil adaptability, and poor soil fixation effect. Achieve strong soil adaptability, good durability, and good soil-fixing effect

Inactive Publication Date: 2003-09-17
TIANZHUJIE SPECIAL BUILDING MATERIAL TECH DEV BEIJING
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional soil reinforcement materials are mainly lime and cement. Lime can be used for shallow roadbeds or house foundations, but not for soft soil layers with high water content; although cement can be used to reinforce soft soil layers, cement is used to strengthen soil The soil effect is not good, and the adaptability to the soil quality is poor. In addition, the cement production process consumes a lot of energy and mineral resources, which seriously pollutes the surrounding environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Carbide slag, granulated blast furnace slag, sodium hydroxide and potassium hydroxide are respectively ground to a Blaine specific surface area of ​​400m 2 / kg, in parts by weight: 89 parts of calcium carbide slag, 10 parts of granulated blast furnace slag, 0.5 part of sodium hydroxide, and 0.5 part of potassium hydroxide are mixed to obtain the soil curing agent of the present invention, which can replace lime as soil reinforcement Material. Wherein the calcium carbide slag can be replaced by quicklime or slaked lime or lime paste or any combination thereof in equal parts by weight, and the granulated blast furnace slag can be replaced by granulated electric furnace phosphorous slag or granulated ferrochrome slag or granulated titanium slag in equal parts by weight Slag or granulated copper slag or granulated nickel slag or any combination thereof instead.

Embodiment 2

[0016] Grind carbide slag, granulated blast furnace slag, fluidized slag, and calcium sulfate separately until the Blaine specific surface area is 400m 2 / kg, in parts by weight: 40 parts of carbide slag, 35 parts of granulated blast furnace slag, 24 parts of boiling slag, and 1 part of calcium sulfate are mixed to obtain the soil curing agent of the present invention, which can replace cement as soil reinforcement material.

Embodiment 3

[0018] Grind calcium carbide slag, granulated blast furnace slag, fly ash and calcium sulfate to a Blaine specific surface area of ​​400m 2 / kg, in parts by weight: 40 parts of calcium carbide slag, 35 parts of granulated blast furnace slag, 24 parts of fly ash, 1 part of calcium sulfate mixed to obtain the soil curing agent of the present invention, which can replace cement as soil reinforcement material .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

A soil solidifying agent is prepared from calcium carbide dregs (25-90 portions), granualr slags (10-75 portions) of blast furnace and chemical trigger (0.1-5 portions) through grinding, and proportional mixing. Its advantages are broad spectrum, and high effect and durability.

Description

technical field [0001] The invention relates to a soil curing agent in the field of building materials. Background technique [0002] Traditional soil reinforcement materials are mainly lime and cement. Lime can be used for shallow roadbeds or house foundations, but not for soft soil layers with high water content; although cement can be used to reinforce soft soil layers, cement is used to strengthen soil The soil effect is not good, and the adaptability to the soil quality is poor. In addition, the cement production process consumes a lot of energy and mineral resources, which seriously pollutes the surrounding environment. Contents of the invention [0003] The object of the present invention is to overcome the deficiencies of the above-mentioned prior art, and provide a kind of soil solidifying agent which has strong adaptability to various soils, good soil-fixing effect, good durability of solidified soil, and can utilize industrial waste. [0004] The soil solidifyi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K17/02
Inventor 郑娟荣周同和吴杰
Owner TIANZHUJIE SPECIAL BUILDING MATERIAL TECH DEV BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap