Method for producing alcohols by hydrogenating carbong/compounds

A carbonyl compound, hydrogenation catalyst technology, applied in the production of sugar alcohols, the field of compounds containing O=C-O groups, can solve the problems not mentioned, and achieve the effect of low bulk density

Inactive Publication Date: 2004-04-07
DEGUSSA AG
View PDF8 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this patent document does not mention the use of the catalyst to produce alcohols by hydrogenation of carbonyl compounds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] 1730g of alloy particles containing 53%Ni and 47%Al (this alloy is melted in an electromagnetic induction furnace, poured into a crucible, cooled in air, the size of the particles is reduced, and the particle size distribution of the particles<65 μm) and 130 g of pure nickel powder (99% Ni and d50 = 21 μm) was suspended in 1557 ml of an aqueous solution containing about 2% by weight of polyvinyl alcohol to prepare a coating solution. The suspension was then sprayed onto 1,000 ml of polystyrene spheres approximately 2 mm in diameter while suspending the spheres in an upward flow of air. 1 L of these balls were additionally coated with the alloy solution. The solution that is used for coating for the second time is made of alloy particles containing 53%Ni and 47%Al of 1203g (this alloy is melted in electromagnetic induction furnace, is poured in the crucible, cools in air, reduces the size of particle, The particle size distribution of the particles is <65 μm), consistin...

Embodiment 2

[0068] 1730g of alloy particles containing 53%Ni and 47%Al (this alloy is melted in an electromagnetic induction furnace, then sprayed into water to make alloy particles, the particle size distribution of the particles<65μm) and 130g pure nickel powder (99% Ni and d50=21 μm) were suspended in 1557 ml of an aqueous solution containing about 2% by weight of polyvinyl alcohol to prepare a coating solution. The suspension was then sprayed onto 1,000 ml of polystyrene spheres approximately 2 mm in diameter while suspending the spheres in an upward flow of air. 1 L of these balls were additionally coated with the alloy solution. The solution that is used for coating for the second time contains 53%Ni and the alloy particle of 47%Al (this alloy is melted in the electromagnetic induction furnace, is sprayed into water to make alloy particle then, the particle size distribution of particle<65μm by 1203g ), 90g of pure nickel powder (99%Ni and d50=21μm) and 1083ml of an aqueous solutio...

Embodiment 3

[0071] 1730g of alloy particles containing 53%Ni and 47%Al (this alloy is melted in an electromagnetic induction furnace, atomized into alloy particles in nitrogen, the particle size distribution of the particles<65μm) and 130g pure nickel powder (99%Ni and d50=21 μm) were suspended in 1557 ml of an aqueous solution containing about 2% by weight of polyvinyl alcohol to prepare a coating solution. The suspension was then sprayed onto 1,000 ml of polystyrene spheres approximately 2 mm in diameter while suspending the spheres in an upward flow of air. 1 L of these balls were additionally coated with the alloy solution. The solution that is used for the second coating consists of 1203g alloy particles containing 53%Ni and 47%Al (this alloy is melted in an electromagnetic induction furnace, atomized into alloy particles in nitrogen, and the particle size distribution of the particles<65μm) , 90 g of pure nickel powder (99% Ni and d50=21 μm) and 1083 ml of an aqueous solution conta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

A method for preparation of alcohols by catalytic hydrogenation of carbonyl compounds with hydrogen or hydrogen-containing gases in the presence of a hydrogenation catalyst of Raney type, where the catalyst is used in the form of hollow bodies, Preferred as catalytically active components are nickel, cobalt, copper, iron, platinum, palladium or ruthenium.

Description

technical field [0001] The present invention relates to an improved process for the production of alcohols from carbonyl compounds which comprises the catalytic hydrogenation of carbonyl compounds with hydrogen or a hydrogen-containing gas in the presence of shaped Raney-type hydrogenation catalysts. Specifically, the present invention includes methods for producing sugar alcohols. Compared with the currently known methods, the method can use a relatively small amount of catalyst in the process of producing alcohol, and has the same or higher yield. [0002] According to the invention, the term carbonyl compounds refers to all organic compounds containing the =CO group, in other words also compounds containing the O=C-O group. Thus, the term carbonyl compound stands for ketones, aldehydes, carboxylic acids, carboxylates, anhydrides, esters of carboxylic acids, amides of carboxylic acids and halides of carboxylic acids. Background technique [0003] Alcoh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C07H15/04B01J25/00B01J25/02B01J35/04B01J35/08C07B61/00C07C29/141C07C29/145C07C29/149C07C31/10C07C31/26C07D307/08C07D315/00
CPCC07D307/08C07C29/141C07D315/00C07C29/149C07B2200/07C07C31/08C07C31/26C07C31/12C07C31/125C07C31/02C07C31/10C07C31/207
Inventor 丹尼尔·奥斯特卡德莫尼卡·贝尔魏勒斯特凡·勒德
Owner DEGUSSA AG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap