Rapid repairing materials for ultrathin layer on the surface of road and airfield runway

An airport runway and repair material technology, applied in the field of building materials, can solve problems such as unsuitable road repair, and achieve the effect of high cost performance and less interference.

Inactive Publication Date: 2005-08-17
桂永全
View PDF5 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The composite material is only suitable for the repair and maintenance of concrete and asphalt pavement surface, not suitable for road repair

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] Now take the rubber powder and process 100 parts by weight of this restoration material as an example, and the non-limiting examples are described as follows:

[0035] 1. Take 90 parts of sulfoaluminate cement (hereinafter referred to as gelling I), 0.1 part of pure acrylic rubber powder, 8 parts of fine sand, and 1.9 parts of activated silica, and fully stir and mix evenly.

[0036] 2. Take 30 parts of Portland rapid-hardening cement (hereinafter referred to as gelling II), 40 parts of styrene-acrylic rubber powder, 15 parts of fine sand, and 15 parts of fly ash, and fully stir and mix evenly.

[0037] 3. Take 45 parts of gelatin I, 30 parts of styrene-butadiene rubber powder, 15 parts of fine sand, and 10 parts of volcanic ash, and fully stir and mix evenly.

[0038] 4. Take 30 parts of gelatin I, 7 parts of pure acrylic powder, 60 parts of fine sand, and 3 parts of active silica, and stir and mix well.

[0039] 5. Take 80 parts of gelatin I, 3 parts of pure acrylic po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
curing timeaaaaaaaaaa
Login to view more

Abstract

The super thin fast repair material for highway and airport runway consists of early strengthened hydraulic cementing material 30-90 wt%, polymer resin emulsion or water dispersible polymer powder 0.1-40 wt%, fine sand 8-60 wt% and inorganic modifier 0.1-15 wt%. The repair material is suitable for thin layer and super thin layer repairing of concrete and asphalt road surface, may be also used for repairing damaged part when sand, crushed stone and other aggregate are added. It is also suitable for repairing inner and outer walls of building. The finishing super thin cement mortar layer has the breaking strength reaching 2-4 MPa in 2-3 hr and compression strength up to 20-30 MPa. The present invention can raise the antiwear performance, weather resistance and engine oil and hydraulic oil corrosion resistance.

Description

1. Technical field [0001] The invention relates to a building material for road maintenance, in particular to a building material for fast repairing of the thin layer and ultra-thin layer on the surface thereof, more precisely, a material for quick repairing of the ultra-thin layer on the surface of roads and airport runways. 2. Background technology [0002] The surfaces of airport pavements, high-grade highways, bridge pavements and industrial buildings are mostly concrete or asphalt materials, and the surfaces need to be repaired and maintained during use. For example, repairing cracks or damages, and in most cases, repairing and maintaining the surface with thin or ultra-thin layers. Its patching or restoration requires rapid curing in order to keep traffic flowing. The thickness of the overlay restorative layer changes gradually with the progress of materials science. For traditional concrete, the standard of the US Department of Transportation in the early days was &...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B14/04C04B26/02C04B28/00
Inventor 桂永全
Owner 桂永全
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap