Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Composite zeolite catalyst for preparing alcohol and ether compounds and preparation thereof

A combination of zeolite and catalyst technology, applied in the direction of preparation of ether by addition of unsaturated compounds, physical/chemical process catalyst, ether preparation, etc., can solve the problems of easy hydrolysis deactivation, low production capacity, complicated preparation, etc., and achieve good repeatability , easy operation and simple preparation process

Inactive Publication Date: 2005-09-14
DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although strong acid resin has high catalytic activity, due to its disadvantages such as complex preparation, easy hydrolysis deactivation, non-regeneration, and low production capacity, many companies are currently working on the research of zeolite catalysts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0027] Example 1: Take SiO 2 / Al 2 o 3 is 5.5, the relative crystallinity is 97%, the unit cell parameter is 2.468nm, Na 2 O is 200 grams of NaY zeolite with a weight content of 10.3%, crushed to less than 20 mesh, and containing 160 grams of NH in 1.6 liters 4 NO 3 The solution was stirred at 90-95°C for 2 hours, cooled to 45°C, filtered off the mother liquor, and repeated 3 times, then 2 liters of deionized water was added to wash the filter cake, and finally the filter cake was placed in a hydrothermal treatment furnace. Under the condition of 600°C, control the system pressure at 0.08MPa, and process for 3 hours. The resulting product unit cell parameters are 2.444nm, SiO 2 / Al 2 o 3 The ratio is 5.7, Na 2 The O weight content is 2.5%, and the relative crystallinity is 82%.

example 2

[0028] Example 2: Take SiO 2 / Al 2 o 3 is 5.5, the relative crystallinity is 97%, the unit cell parameter is 2.468nm, Na 2 O weight content is that 200 grams of NaY zeolite of 10.3% are pulverized to be less than 20 orders, with the NH of 1.5N 4 1 liter of CI solution was exchanged at 90-95°C for 2 hours, cooled to less than 45°C, filtered off the mother liquor, and repeated 3 times, then added 2 liters of deionized water to wash the filter cake, and finally placed the filter cake in a hydrothermal treatment furnace. Control the partial pressure of water vapor to less than 0.15MPa, supply electricity to raise the temperature to 650°C, and keep it for 1 hour. The unit cell constant of the obtained product is 2.442~2.445nm, SiO 2 / Al 2 o 3 The ratio is 5.8, Na 2 The O weight content is 2.2%, and the relative crystallinity is 83%.

example 3

[0030] SiO will be synthesized under hydrothermal conditions 2 / Al 2 o 3 100 grams of ZSM-5 zeolite raw powder with a temperature of 45-60 is put into a muffle furnace, and air preheated to 500° C. is introduced, and the temperature in the furnace is controlled at 650° C. for 24 hours. The product properties are: the relative crystallinity is 82%, Na 2 O content is 3.2% by weight, SiO 2 / Al 2 o 3 It is 58.2, and the restraint index is 1.8.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention provides is a combinational zeolite catalyst making alcohol and aether kinds compounds and the preparation method. The zeolites of the invention are the zeolite Y with 2.420-2.462nm parameter and ZSM-5 zeolite through burning and with the organic module agent removed. Mix the two kinds of zeolites and use the mixing agent containing H+ and NH4+ for the treatment and then implement drying treatment. The combinational zeolites are the acid components, and are matched with one or some of P, B and Zn and use Al2O3, SiO2-Al2O3 or the clay to form. The catalyst of the invention has high activity, fine selection and flexible operation.

Description

technical field [0001] The present invention relates to a combined zeolite catalyst for the preparation of compounds such as alcohol or ether by hydration of olefins, specifically a zeolite composed of ZSM-5 zeolite and Y zeolite, which is used for the catalysis of the reaction of olefins with water or alcohol to prepare alcohol or ether active ingredient. Background technique [0002] In the catalytic cracking process of the refinery, due to the addition of ZSM-5 additives, while increasing the octane number of gasoline, it also produces a large amount of C 2 -C 7 Olefin mixture, and olefin hydration is an important way to consume olefins, and it is also an important method for industrial production of alcohol. Olefin hydration reaction is a typical acid-catalyzed reaction, and its catalyst is generally H 2 SO 4 and H 3 PO 4 / SiO 2 , due to the corrosion, loss and other problems of the above two catalysts, they have been gradually replaced by zeolite catalysts and st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J29/06B01J29/08B01J29/40C07C29/04C07C41/06
Inventor 高进周焕文徐杰王峰周利鹏李晓强
Owner DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com