High-temperature stripping agent of curing membrane for printed nickel net, its preparation and use

A high-temperature curing and stripping agent technology, which is applied in the processing of photosensitive materials, can solve the problems of high cost, environmental pollution, and low efficiency, and achieve the effects of low corrosion, high stripping efficiency, and low stripping cost

Inactive Publication Date: 2005-12-28
朱守诚
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above micro-nozzle ultra-high pressure water gun equipment is expensive
China Zhejiang Jinchang Company adopts the principle of high-energy laser incineration of cured film, and also manufactures and launches a laser film peeling equipment prototype. This prototype can peel off the cured film, but its efficiency is too low. A nickel mesh with a width of 1850mm can be peeled off in 4-5 hours. , and laser incineration produces a large amount of harmful gas, polluting the environment
It belongs to the two-step process of rotary screen release and bulkhead dissociation, and it is still not popularized and used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The printed nickel screen high-temperature curing film stripping agent in the present embodiment is compounded with organic acid, corrosion inhibitor, surfactant and expansion agent; Its raw material composition by weight:

[0033] Lactic acid 5-10 parts,

[0034] 5-10 parts of gluconic acid,

[0035] 1-2 parts of 2-phosphonic acid-1,2,4-tricarboxylic acid (PBTCA),

[0036] Amino trimethylene phosphonic acid (ATMP) 2-4 parts;

[0037] 2-8 parts of corrosion inhibitors for aluminum and nickel metals,

[0038] Nonionic surfactant: 2-4 parts of alkyl polyglycosides;

[0039] Phenolic expansion agent: 10-15 parts;

[0040] Water: 38-68 parts.

[0041] The specific implementation also includes:

[0042] In order to reduce or suppress volatilization, 5-8 parts of diethylene glycol can be added in its raw material composition by weight.

[0043] The corrosion inhibitor adopts a mixed corrosion inhibitor, and its composition by weight is:

[0044] 1-5 parts of cyclohexa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A stripper of high temperature cured film on printing Ni screen is prepared from organic acid, corrosion inhibitor, surface active agent and expander. Its preparing method can be finalized by one step process of socking for de-filming and de-blinding so reuse for printing Ni screen in circulation can be effectively realized.

Description

Technical field: [0001] The invention relates to a technology for stripping a high-temperature cured film of a printed nickel screen used in rotary screen printing, including a stripping agent and a stripping method. Background technique: [0002] At present, textile printing methods include: copper roller printing, flat screen printing, rotary screen printing, manual platen printing, computer inkjet printing, etc., among which rotary screen printing is developing rapidly. With the mass production of small batches, multiple varieties, and fast delivery export orders, the demand for nickel screens of different specifications will increase significantly. At present, the national consumption of rotary screens is about 2-2.5 million per year. [0003] Due to the use of polymer photosensitive materials in the process of cylinder screen making, a layer of dense and elastic polymer film is formed on the surface of the nickel mesh blank. This layer of film has high strength after cu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G03F7/42
Inventor 朱守诚漆静秋
Owner 朱守诚
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap