Manufacturing method of high performance antioxidation environmental protection copper raft

A manufacturing method and anti-oxidation technology, applied in the direction of manufacturing tools, other manufacturing equipment/tools, etc., can solve the problems of consumption of non-ferrous metal raw materials, poor bending performance of products, poor working environment, etc., and achieve saving of non-ferrous metal resources and electrical conductivity Good, good heat dissipation effect

Inactive Publication Date: 2006-01-11
江阴市汇金铜业有限公司
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is that the working environment of the workers is poor and the surface quality is slightly poor
[0008] The advantage of the second method is that the surface quality is slightly better and the working environment of workers is improved, but t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of high performance antioxidation environmental protection copper raft

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0034] Embodiment: The manufacturing method of the high-performance anti-oxidation environment-friendly copper bar of the present invention comprises the following steps:

[0035] Take 5mm×80mm×5500mm bright copper bar as an example:

[0036] Step 1, continuous casting of ingots of 120mm×280mm. Place well-known brands of domestic electrolytic copper or imported Chilean copper in a submerged conjoined low-frequency induction furnace with a capacity of one ton per hour. The crystallizer is made of graphite, covered with roasted dry charcoal and dace flake graphite, and the casting temperature is 1140-1160 °C , Casting speed (15-18) m / h.

[0037] Step two, water seal extrusion. The product size after water seal extrusion is 7.3mm×83.3mm. Put the ingot obtained in step 1 into the extrusion die, and extrude it on a 800-ton double-acting hydraulic press with a water seal at an extrusion temperature of 850-900°C. In order to ensure the surface quality and dimensional stability of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A method for preparing the high-performance antioxidizing copper bus includes such steps as smelting electrolytic copper in LF induction furnace with graphite crystallizer and charcoal covering, casting, water-sealing extruding, acid washing for neutralizing, washing with hot water, rough drawing, removing surfacial skin, brightening annealing in the mixture of N2, and H2, and fine drawing.

Description

Technical field: [0001] The invention relates to a method for manufacturing a high-performance anti-oxidation environment-friendly electrical copper bar with a bright surface, which can maintain the brightness for a long period of time and has excellent bending properties. Background technique: [0002] Electrical copper bars are generally used to conduct large currents, and are suitable for the manufacture of motor windings, high and low voltage electrical appliances, switch contacts, power distribution equipment and other electrical engineering, and are indispensable conductive materials for installation wires. It is also widely used in ultra-high current electrolytic smelting projects such as metal smelting, metal electrolysis, electroplating, and chemical caustic soda. There are GB5585-85 requirements, such as resistivity at 20 °C ≤ (0.01724Ω.mm 2 / m), and has a variety of sizes and specifications. Generally speaking, electrical copper bars have the advantages of low re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23P23/04
Inventor 赵仁才
Owner 江阴市汇金铜业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap