Method for producing microcrystalline glass plaque using phosphor slag

A technology of glass-ceramic and phosphorus slag, which is applied in the field of producing glass-ceramic plaques to achieve the effects of uniform texture, less pollution and high strength

Inactive Publication Date: 2006-05-10
贵州合力化工有限责任公司
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But so far, the production of glass-ceramic decorative panels with phosphorus slag has not been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] Embodiment: get the phosphorus slag of certain enterprise discharge in Guizhou Province as raw material, its chemical composition (mass fraction) is as shown in the following table after testing:

[0031] Composition SiO 2 al 2 o 3 Fe 2 o 3 CaO MgO P 2 o 5 Loss on ignition Total

[0032] Content % 41.56 3.64 0.97 44.88 1.63 1.50 5.82 100.00

[0033] The first step, prepare materials:

[0034] Take 100kg of phosphorus slag, 55.25kg of quartz sand, 7.15kg of soda ash, 1.13kg of borax, 3.25kg of aluminum oxide, 3.25kg of zinc oxide, and 1kg of colorant. Remove impurities such as iron and coal ash in phosphorus slag by conventional methods, then dry it with hot air, and ball mill it into powder with a fineness of 100±50 mesh for later use; the quartz sand should also be ball-milled into powder with a fineness of 100±50 mesh. spare.

[0035] Step two, ingredients:

[0036] After the above materials are accurately weighed, mixed, forced to stir evenly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for producing microcrystalline glass plaque with phosphorus residue, which contains the following steps: firstly, preparing materials, which means preparing phosphorus residue, quartzite, soda, borax, alumina, zinc oxide and colorant agent according to the formulation; secondly, matching materials, which means mixing uniformly the material; thirdly, burning fused block materials; fourthly, heating to crystallize to prepare the rough board of microcrystalline glass plaque; fifthly, polishing, cutting, polishing and manufacturing to prepare the end product. Microcrystalline glass plaque manufactured by this method is characterized in that the physical mechanical performance is perfect, the texture is uniform and exquisiteú¼the brightness and color is durable, it is pollution tolerant, and the technique for preparation is mature and simple. Using this method it can reduce effectively environmental pollution caused by phosphor residue and yellow-phosphorus furnace end gas, and it is favorable to improve environment, as well as providing high grade and safe decorating materials for buildings, and it has nice social and environmental, also has nice economic benefit.

Description

technical field [0001] The invention relates to glass-ceramic, in particular to a method for producing a glass-ceramic decorative plate using phosphorus slag as a raw material. Background technique [0002] Glass-ceramics, also called crystallized glass, is a new type of glass frit made of inorganic non-metallic materials and crystallized at an appropriate heat treatment temperature by using controlled crystallization technology. building materials. The glass-ceramic decorative plate combines the superior physical and chemical properties and mechanical properties of glass and ceramics. It has beautiful color, exquisite surface pattern, high strength and hardness, no fading, good corrosion resistance, low water absorption, no radioactivity, and is more natural. The brightness of the stone is good. This decorative panel is suitable for the decoration of the interior and exterior walls, floors, columns, furniture, kitchen and bathroom countertops of buildings, etc. It is a hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C10/14C03B32/02C03C6/06
Inventor 岑春华吴玉平刘国安刘建波莫君杰黄升华刘应刚
Owner 贵州合力化工有限责任公司