Manufacturing process of chain wheel for chain saw

A manufacturing method and sprocket technology, which is applied in the direction of manufacturing tools, wheels, heat treatment process control, etc., can solve the problems of heat treatment deformation, long blank cycle, low gear density, etc., to control product quality and precision, improve production efficiency, and facilitate Promoted app performance

Inactive Publication Date: 2007-06-06
宓建英
View PDF0 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 1. The cycle of cold stamping, cold extrusion and machining of gear blanks is long, the efficiency is low, and the cost is high;
[0007] 2. Two-step heat treatment is required in the manufacturing process of the sprocket (carburizing heat treatment is required after gear processing; hardening heat treatment is required after brazing), which is costly and increases the deformation caused by heat treatment, especially after the sprocket and hub are brazed. Causes a lot of defor...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process of chain wheel for chain saw

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] Below in conjunction with specific embodiment the present invention is described in further detail:

[0035] Referring to Fig. 1, an embodiment of a manufacturing method of a chain saw sprocket, including the manufacture of the gear 1, the manufacture of the hub 2, the assembly and brazing of the gear 1 and the hub 2, and post-processing procedures, the manufacturing of the sprocket is mainly through closed-room precision It is completed by forging powder metallurgy gear blanks, and its specific technical scheme is as follows:

[0036] Example: STIHL MS170 Chainsaw Sprocket

[0037] 1) Gear blank material formula: carbon: 0.71%; nickel: 1.72%; molybdenum: 0.55%; copper: 2.3%, manganese sulfide is less than 0.2% (if subsequent machining is required, manganese sulfide should be added, otherwise manganese sulfide is not required ); hub material is 25CrMo4.

[0038] 2) The weight of the gear blank is controlled at 29.0-29.6g;

[0039] 3) The gear blank is immersed in gra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The manufacture process of chain wheel for chain saw includes the following steps: powder metallurgy process to produce gear blank with sorted materials; precise forging through soaking graphite milk or coating graphite or setting in nitrogen protection, fast induction heating to 815-950 deg.c for less than 20 sec, fast forging in closed mold and demolding to reach gear density greater than 7.7 g/cu cm; assembling the gear to hub; and brazing and hardening in the protection of nitrogen with small amount of hydrogen inside a brazing furnace with fast cooling gas system for gas quenching to harden through phase change to reach hardness over HRC58. The manufacture process is simple, and has high production efficiency, low cost and high product precision and quality.

Description

technical field [0001] The invention belongs to the technical field of mechanical manufacturing, in particular to a method for manufacturing a chain saw chain wheel. Background technique [0002] The chain saw sprocket is an important part of the chain saw, and its function is to drive the saw chain to cut wood. The sprocket is generally assembled and welded by the sprocket gear and the hub. The traditional sprocket gear manufacturing technology is machined by mechanical processing. Machining low-carbon low-alloy steel cold punched or cold-extruded gear blanks with gear profiles, and then completing carburizing heat treatment; the hub of the sprocket is generally completed by stamping. The materials of the gear and the hub are different, and the gear material is low carbon. Low alloy steel, for example: 17CrNi6; hub material is 25CrMo4. [0003] The assembly process of the sprocket is as follows: the gear is assembled with the hub after carburizing heat treatment → brazin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23P15/14C22C38/18B21K1/30B21J1/06B23K1/008C21D9/32C21D11/00
Inventor 杨高明
Owner 宓建英
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap