Preparation of double axial structured CeO2 film from inorganic salt as raw material by liquid phase chemical process

A thin film technology and inorganic salt technology are applied in the field of preparation of biaxially textured CeO2 thin films, which can solve the problems of high cost of organic cerium salts, inability to prepare dense, uniform and flat biaxially textured thin films, etc. Good quality, good sol stability, cost reduction effect

Inactive Publication Date: 2007-11-07
TSINGHUA UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] The present invention aims at preparing CeO at home and abroad at present 2 The use of organic cerium salts in thin films is costly, or the use of inorganic cerium salts cannot prepare dense, uniform, flat, and biaxially textured films. A liquid-phase chemical method using inorganic salt raw materials to prepare biaxially textured CeO 2 Thin film technology; the specific process is:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation of double axial structured CeO2 film from inorganic salt as raw material by liquid phase chemical process
  • Preparation of double axial structured CeO2 film from inorganic salt as raw material by liquid phase chemical process
  • Preparation of double axial structured CeO2 film from inorganic salt as raw material by liquid phase chemical process

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] 3. CeO 2 Film preparation

[0037] 1) Spin coating, dip coating or spray drying method is used to coat the surface of the substrate to form a film. Spin coating method: the speed of spin coating is from 1000 rpm to 6000 rpm, and the spin coating time is 6 seconds to 3 minutes; When coating, the substrate stays in the sol for 3 seconds to 1 minute, and the pulling speed is 10 to 150 mm / min;

[0038] 2) The film-coated substrate was placed in Ar-4%H 2 Heating in the atmosphere or air, the temperature is from 60°C to 500°C, and the time is from 30 seconds to 24 hours for pyrolysis to remove the organic solvent in the film.

[0039] 3) Sintering heat treatment. Heat the pyrolyzed film at a rate of 1-200°C / min to 500°C-1200°C and keep it warm for 3 minutes to 120 hours. By cooling at a rate of 1 / min, CeO with a biaxial texture, uniform and dense, and a thickness of tens of nanometers to several microns can be obtained. 2 film.

[0040] The above metal or ceramic substr...

Embodiment 1

[0043] Take cerous nitrate hexahydrate [Ce(NO 3 ) 3 ·6H 2 O] 4.34 g, dried under vacuum at 60°C for 24 hours. Add 6 grams of anhydrous acetylacetone, add zeolite, reflux at 100°C for 24 hours, then add anhydrous ethylene glycol methyl ether to bring the total volume to 40 ml, reflux for 24 hours, finally add anhydrous methanol, reflux for 24 hours, and Filter and then add methanol to make the total sol concentration reach 0.25 mol / L. Filter the above sol, seal it and let it stand for more than 48 hours, then it can be used for film coating. Use the above-mentioned sol to coat the film on the YSZ single crystal by spin coating method, and the film spin parameter is 1000rpm×6 seconds+6000rpm×30 seconds. The prepared gel film was dried on a hot table at 400°C for 10 minutes, and then the pyrolyzed film was placed in a three-stage tube furnace with a heating rate of 10°C / min and heat-treated at 1000°C. 1 hour, then the furnace is cooled and the atmosphere is air throughout th...

Embodiment 2

[0045] The preparation process steps are the same as those in Example 1, except that, in the thin film preparation process, the dip coating method is used instead of the spin coating method to coat the film. The process of the dip coating method is to place about 50 ml of the prepared solution in a beaker, clamp the cleaned substrate with the chuck of the dip coating machine, slowly immerse it in the solution, and let it stand for 10 seconds. Pull out from the solution at a uniform speed of 1 mm / s, then perform pyrolysis and heat treatment, and the process is exactly the same as in Example 1. CeO with a thickness of about 100 nm was obtained 2 film.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A process for preparing biaxial-texture CeO2 thin film by inorganic salt material liquid phase chemical method includes: dehydrating and pre-treating for inorganic salt and organic solvent, preparing coating liquid, coating CeO2 on base, and pyrolyzing and sintering to obtain biaxial-texture CeO2. Its advantages include good crystal lattice matching performance and chemical stability, and good oxygen dispersing resistant ability.

Description

technical field [0001] The invention belongs to the technical scope of preparation of superconducting thin film materials, in particular to a method of preparing biaxially textured CeO by using an inorganic salt raw material liquid phase chemical method 2 Thin film process. Background technique [0002] Cerium oxide (CeO 2 ) is a multifunctional material with broad application prospects, and has been used in many fields such as optics, chemical catalysis, chemical pigments, high-temperature superconductivity, chemical sensors, and fuel cells. For general applications, CeO 2 The film only needs to have a certain thickness, good uniformity, compactness and surface smoothness. These applications are very important for CeO 2 There is no special requirement for the orientation of the film. However, in the preparation process of YBCO coated conductor, which is a hot spot in the research of superconducting materials, CeO 2 The film has both good surface condition and good biax...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C18/12
Inventor 陈胜王三胜史锴刘庆韩征和
Owner TSINGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap