Leadfree fritted glaze suitable for secondary sintering

A lead-free frit and secondary firing technology, applied in the field of improved lead-free frit glaze, can solve the problems of many glaze defects, limited adaptability, dullness, etc., and achieve good glaze quality, high strength and The effect of thermal stability and high yield

Inactive Publication Date: 2008-03-26
淄博硅元投资控股有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some have quality problems of their own products, many glaze defects, serious blistering and dull phenomena, which have always been the main obstacles to the production of high-grade porcelain after secondary firing; some have limited adaptability, and some lead-free glazes are only limited to bone china. , It is suitable for high quartz porcelain, but not for steatite porcelain, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Leadfree fritted glaze suitable for secondary sintering
  • Leadfree fritted glaze suitable for secondary sintering
  • Leadfree fritted glaze suitable for secondary sintering

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 5

[0044] The present invention is applicable to the lead-free frit glaze that second firing is used, and the weight percentage of its batching raw material is composed of:

[0045] Feldspar 35.5%, Quartz 15.0%, Talc 3.5%, Light Calcium Carbonate 6.0%, Zinc Oxide 3.0%, Borax 8.0%, Boric Acid 2.0%, Lithium Carbonate 2.0%, Barium Carbonate 8.0%, Kaolin 10.0% and Zirconia 7.0% %.

Embodiment 6

[0047] The present invention is applicable to the lead-free frit glaze that second firing is used, and the weight percentage of its batching raw material is composed of:

[0048]Feldspar 38.0%, Quartz 12.0%, Aluminum Hydroxide 5.0%, Talc 5.0%, Light Calcium Carbonate 5.0%, Zinc Oxide 2.0%, Borax 10.0%, Boric Acid 4.0%, Strontium Carbonate 2.0%, Barium Carbonate 3.0%, Kaolin 6.0% and zirconia 8.0%.

Embodiment 7

[0050] The present invention is applicable to the lead-free frit glaze that second firing is used, and the weight percentage of its batching raw material is composed of:

[0051] Feldspar 52.0%, Quartz 7.0%, Talc 1.0%, Light Calcium Carbonate 5.5%, Zinc Oxide 1.0%, Borax 6.0%, Boric Acid 2.0%, Strontium Carbonate 0.5%, Barium Carbonate 5.0%, Kaolin 15.0% and Zirconia 5.0 %.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a leadless fritted glaze, which comprises the following parts: 35.0-60.0%SiO2, 14.0-18.0%Al2O3, 3.0-10.0%CaO, 0.0-5.0%MgO, 5.0-10.0%K2O, 2.0-5.0%Na2O, 5.0-10.0%ZnO, 4.0-12.0%B2O3, 1.0-5.0%SrO, 0.0-1.0 %Li2O, 0.0-8.0%BaO and 5.0-9.0%ZrO2. The invention solves masking problem for magnesium ceramic glaze surface, which prevents environmental pollution due to overcoming to flow lead and cadmium.

Description

technical field [0001] The invention relates to an improved lead-free frit glaze, which is suitable for secondary firing of various porcelains. Background technique [0002] With the improvement of people's awareness of nature and living standards, many sources of pollution in our daily life have been discovered. In order to ensure a healthier life for human beings and the sustainable development of the earth on which human beings depend, people have formulated various restrictions and standards, including daily-use ceramic products that are closely related to human life. [0003] In the international high-grade daily-use fine porcelain characterized by secondary firing (high-temperature plain firing, low-temperature glaze firing), bone china is the mainstream variety, with a history of more than 200 years. In the 1970s and 1980s, talc porcelain and high-quartz porcelain were successfully developed in Shandong. By the end of the 20th century, high-grade daily-use fine porce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/02C04B41/86
CPCC03C3/062C03C3/066C03C3/087C03C3/16C03C3/093C03C3/097
Inventor 张儒岭王磊尚庆刚任允鹏
Owner 淄博硅元投资控股有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products