Halogenless composite fire retardant for polyolefine plastic

A technology of compound flame retardant and polyolefin, which is applied to the flame retardant of polypropylene. , Halogen-free composite flame retardants for polyolefin plastics, polyethylene field, can solve the problems of flame retardants that cannot be recycled, threaten human health, the environment and the next generation of descendants, and achieve the goal of suppressing smoke and hydrogen chloride generation, non-corrosive prices Effect

Inactive Publication Date: 2009-10-07
SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The reason why halogen-based flame retardants are banned in plastic materials is that such flame retardants cannot be recycled and will release harmful substances during combustion and heating, threatening human health, the environment and future generations

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Take 10 kg of aluminum hydroxide according to the proportioning ratio; 40 kg of brucite powder; 5 kg of whiteness coated red phosphorus; 2 kg of resorcinol diphosphate; Formulated as a halogen-free composite flame retardant.

Embodiment 2

[0020] Take 20 kg of aluminum hydroxide according to the proportioning ratio; 60 kg of brucite powder; 10 kg of whiteness coating red phosphorus; 3 kg of resorcinol diphosphate; 15 kg of ammonium polyphosphate; Formulated as a halogen-free composite flame retardant.

Embodiment 3

[0022] Take 30 kg of aluminum hydroxide according to the proportioning ratio; 80 kg of brucite powder; 15 kg of red phosphorus coated with whiteness; 5 kg of resorcinol diphosphate; Formulated as a halogen-free composite flame retardant.

[0023] The flame retardant works differently at different temperatures:

[0024] 1. Ammonium polyphosphate is heated and decomposed at 225°C to release ammonia and water vapor. The water vapor and non-combustible gas produced by the reaction make the molten system expand and foam, which can promote the formation of a non-flammable three-dimensional carbon layer on the surface of organic matter, which can reduce thermal decomposition. The generated combustible tar and low-molecular combustibles promote the generation of non-combustible gases. At the same time, pentaerythritol and acid are dehydrated and carbonized to form inorganic substances and charcoal residues. In addition, the non-volatile phosphorus oxide and polyphosphoric acid produc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A non-halogen composite flame-retarding agent for polyolefine plastics is proportionally prepared from aluminum hydroxide, brucite powder, whitened coated red phosphorue, resorcin biphosphate, ammonium polyphosphate and zinc borate.

Description

technical field [0001] The invention relates to a flame retardant, in particular to a halogen-free composite flame retardant for polyolefin plastics, which is mainly used for flame retardancy of polyethylene and polypropylene. technical background [0002] Materials are the pillars of the relationship between modern science and social development. Polymer materials have many incomparable properties with other materials, and have become indispensable materials in various fields of cutting-edge technology, national defense construction and national economy. However, most polymer compounds are flammable and combustible materials. Once caught on fire, they burn quickly and are not easy to extinguish. Some will produce thick smoke and toxic gases, pollute the environment, endanger people's lives, and cause property losses. In recent decades, a considerable part of the fires that have occurred in the world is related to the burning of polymer materials. Therefore, how to improve ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/521C08L23/00C08K3/22C08K3/32C08K3/38
Inventor 梁兵
Owner SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com