Method for manufacturing non-expansion type halogen-free organic fireproof block material

A technology of fireproof blocking material and manufacturing method, which is applied in the direction of fireproof coatings, etc., can solve problems such as hindering firefighters and rescuers from extinguishing fires and rescue work, suffocation, irritating human eyes and respiratory system, etc., so as to avoid damage to the human body, Good oil resistance

Inactive Publication Date: 2008-02-27
嵊州市电缆防火附件厂
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the known organic fireproof blockages are mainly obtained by adding halogen flame retardants to obtain excellent flame retardancy. Although halogen materials have good flame retardancy effects, they will release a large amount of smoke and hydrogen halide gas when a fire occurs. , these smoke and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] (1) Formula: 30% aluminum hydroxide, 25% zinc borate, 13% porcelain powder, 4% aluminum silicate fiber, 3% iron oxide red, 1.5% coumarone resin, 1.5% xylene resin, phthalate Dibutyl formate 4%, polyester resin 16%, functional additives 2%.

[0010] (2) Process steps and process conditions:

[0011] 1. Preparation of bonding resin: Soak Coumarone resin and xylene resin in dibutyl phthalate for 24 hours, add polyester resin and functional additives into the soaking resin, and stir for 10 minutes to obtain a bonding resin. knot resin;

[0012] 2. Premix filler: Put aluminum hydroxide, zinc borate, porcelain powder, aluminum silicate fiber, and iron oxide red into the mixer and stir for 10 minutes;

[0013] 3. Mixing and stirring: Add the binder resin to the pre-mixed filler and mix and stir to form a viscous soft mass. The stirring time is 10 minutes;

[0014] 4. Extrusion molding: Put the viscous soft mass in the previous process into the extruder for extrusion molding...

Embodiment 2

[0016] (1) Formula: 32% magnesium hydroxide, 12% zinc borate, 25% porcelain powder, 3% aluminum silicate fiber, 3% iron oxide red, 1.5% coumarone resin, 1.5% xylene resin, phthalate Dibutyl formate 4%, polyester resin 16%, functional additives 2%.

[0017] (2) Process steps and process conditions:

[0018] With embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a making method of non-expansion non-bittern organic fireproof block material, which comprises the following steps: dispensing the raw material according to weight percent with 20%-50% aluminum hydroxide, 10%-25% zinc borate, 20%-40% porcelain powder, 5%-10% alumina silicate fiber, 2%-8% iron oxide red, 13%-20% polyester resin, 1%-2% coumarone resin, 1%-2% xylenol resin, 3%-6% dibutylphthalate, 1%-5% functional agent, soaking the coumarone resin 1%-2% and the xylenol resin in the dibutylphthalate for 24 hours; adding the polyester resin and the functional agent to stir to be sticking resin; adding the aluminum hydroxide, the zinc borate, the porcelain powder, the alumina silicate fiber, the iron oxide red into stirrer to stir for 10-15 minutes to form premix stuffing; squeezing to form shaping through force out machine after blending and stirring the sticking resin and the premix stuffing to form mission of viscous soft. The invention overcomes the problem that current fire-proof block can be produced irritating gas and smog under effect of fire hazard, which avoids toxic hydrogen halide gas to injury human body and corrode device effectively.

Description

1. Technical field [0001] The invention relates to a fireproof blockage, in particular to a method for manufacturing a non-expandable halogen-free organic fireproof blockage. 2. Background technology [0002] At present, the known organic fireproof blockages are mainly obtained by adding halogen flame retardants to obtain excellent flame retardancy. Although halogen materials have good flame retardancy effects, they will release a large amount of smoke and hydrogen halide gas when a fire occurs. , these smoke and hydrogen halide gases will irritate the human eyes and respiratory system, causing symptoms such as dizziness, coma, difficulty breathing, suffocation and death, and also hinder the fire fighting and rescue work of firefighters and rescuers, and can cause electrical system switches and other metal objects of corrosion. 3. Contents of the invention [0003] In order to overcome the disadvantages of existing organic fireproof blockages containing halogens and toxic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K21/14C08L67/00C08K7/02C08K3/38C08K3/22C08K5/10C08L65/00
Inventor 丁其龙舒长盛胡新华舒宇松
Owner 嵊州市电缆防火附件厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products