Production method for dihydric phenol type high fire-retardancy benzoxazine resin containing phosphor

A benzoxazine and dihydric phenol-type technology, which is applied in the field of thermosetting resin preparation to achieve good thermal performance, high heat resistance, and good flame retardancy

Inactive Publication Date: 2008-07-16
SHANDONG UNIV
View PDF1 Cites 56 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, no benzoxazine resin has been reported that contains phosphorus itself and does not need to be modified. We designed a benzoxazine intermediate with high phosphorus content by using monoamine, phosphorus-containing dihydric phenol and formaldehyde as reaction raw materials. Body and high flame retardant benzoxazine resin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method for dihydric phenol type high fire-retardancy benzoxazine resin containing phosphor
  • Production method for dihydric phenol type high fire-retardancy benzoxazine resin containing phosphor
  • Production method for dihydric phenol type high fire-retardancy benzoxazine resin containing phosphor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Synthesis of 6,6'-2(3-phenyl-3,4-dihydro-2H-1,3-benzoxazinyl)phenylphosphate.

[0037] The preparation process of synthesizing benzoxazine intermediate and its resin with aniline, 2 (4-hydroxyphenyl) phosphorus oxide and formaldehyde as raw materials,

[0038] Add 75ml of chloroform, 0.7g of triethylamine and 24ml of 35% formaldehyde aqueous solution in sequence into a 250ml three-neck flask equipped with a stirrer and a condenser, and stir to mix. Slowly add 13.4g of aniline, control the reaction temperature not to exceed 30°C, control the pH value to 7 by triethylamine, generate N-dimethylol compound and keep it stable in the solution;

[0039] After reacting for 15 minutes, add 25.7g of 2 (4-hydroxyphenyl) phosphorus oxide, heat up to reflux, and stop the reaction after the mixed solution reacts at reflux temperature for 5 hours, so that the N-dimethylol compound and the phenolic hydroxyl group and its benzene ring A condensation reaction occurs at the ortho positio...

Embodiment 2

[0044] Synthesis of 6,6'-2(3-phenyl-3,4-dihydro-2H-1,3-benzoxazinyl)phenylphosphate.

[0045] The preparation process of synthesizing benzoxazine intermediate and its resin with aniline, 2 (4-hydroxyphenyl) phosphorus oxide and formaldehyde as raw materials,

[0046] Add 90ml of chloroform, 0.84g of triethylamine and 28.8ml of 40% formaldehyde aqueous solution in sequence into a 250ml three-necked flask equipped with a stirrer and a condenser, and stir to mix. Slowly add 16.1g of aniline, control the reaction temperature not to exceed 30°C, control the pH value to 8 by triethylamine, generate N-dimethylol compound and keep it stable in the solution;

[0047] After reacting for 15 minutes, add 30.8g of 2 (4-hydroxyphenyl) phosphorus oxide, heat up to reflux, and stop the reaction after the mixed solution reacts at reflux temperature for 5 hours, so that the N-dimethylol compound and the phenolic hydroxyl group and its benzene ring A condensation reaction occurs at the ortho po...

Embodiment 3

[0052] Synthesis of 6,6'-2(3-methyl-3,4-dihydro-2H-1,3-benzoxazinyl)phenylphosphate.

[0053] The preparation process of synthesizing benzoxazine intermediate and its resin with methylamine, 2 (4-hydroxyphenyl) phosphorus oxide and formaldehyde as raw materials,

[0054] Add 75ml of chloroform, 0.7g of triethylamine and 24ml of 36% formaldehyde aqueous solution in sequence to a 250ml three-neck flask equipped with a stirrer and a condenser, and stir to mix. Slowly add 4.5g of methylamine, control the reaction temperature not to exceed 30°C, and control the pH value to 7.5 by triethylamine to generate N-dimethylol compound and keep it stable in the solution;

[0055] After reacting for 15 minutes, add 25.7g of 2 (4-hydroxyphenyl) phosphorus oxide, heat up to reflux, and stop the reaction after the mixed solution reacts at reflux temperature for 5 hours, so that the N-dimethylol compound and the phenolic hydroxyl group and its benzene ring A condensation reaction occurs at the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing diphenol type phosphor-containing high flameproofing benzene-oxaxine resin, which uses monoamine, phosphor-containing diphenol formaldehyde as raw reaction materials. A benzene-oxaxine midbody is introduced with a compound containing phosphor to synthesize a phosphor-containing flameproofing benzene-oxaxine midbody which is solidified and crosslinked to obtain thermalsetting phosphor-containing high flameproofing benzene-oxaxine resin. Other fire retardants are not required to be added into the flameproofing materials which adopt the phosphor-containing flameproofing benzene-oxaxine resin of the invention as the basic flameproofing material; the flameproofing material using the resin has excellent flameproofing capacity, the flameproofing level can reach V-0, the thermal capacity is rather good and the vitrification transforming temperature can reach 225 DEG C. The phosphor-containing flameproofing benzene-oxaxine midbody which is prepared by the method of the invention can be individually used or used by being mixed with other type benzene-oxaxine midbody or phenolic resin or epoxy resin; an obtained solidified product has higher thermal resistance, and the phosphor-containing flameproofing benzene-oxaxine midbody is applicable to the production of structural material, flameproofing material, electric insulation material, electronic encapsulation material, ablation resistance material or braking material with high capacities which are used at the temperature higher than 180 DEG C.

Description

technical field [0001] The invention belongs to the technical field of thermosetting resin preparation, and in particular relates to a preparation method of a dihydric phenol type phosphorus-containing highly flame-retardant benzoxazine resin. Background technique [0002] Benzoxazines are a class of six-membered heterocyclic compounds synthesized by polycondensation reactions of phenolic compounds, amine compounds and formaldehyde. They were initially discovered in the Mannich reaction, and undergo ring-opening polymerization under the action of heating or catalysts to form nitrogen-containing and similar Network structure of phenolic resin. As a new type of phenolic resin, benzoxazine resin not only has the thermal properties, mechanical properties, and electrical properties of traditional phenolic resins, but also has excellent processing properties: no small molecules are released during the forming and curing process, and the volume is close to zero shrinkage , which h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G73/06C08G79/02C09K21/14C08G79/04
Inventor 鲁在君门薇薇张洪春王赐明孟凡君
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap