Easy-cutting untempered steel and method for manufacture thereof

A non-quenched and tempered steel, free-cutting technology, used in the metallurgical field to achieve the effects of good processing performance, reduced manufacturing costs, and good surface roughness

Inactive Publication Date: 2008-09-03
SHANDONG IRON & STEEL CO LTD
View PDF4 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the deficiencies of the prior art, the present invention provides a Ca-S composite free-cutting non-quenched and tempered steel with high cutting performance, which mainly solves the cutting performance problem of low-sulfur free-cutting non-quenched and tempered steel under high-speed cutting conditions, and is extremely Greatly improved mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easy-cutting untempered steel and method for manufacture thereof
  • Easy-cutting untempered steel and method for manufacture thereof
  • Easy-cutting untempered steel and method for manufacture thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0045] The technical solutions of the present invention will be specifically described below in conjunction with the embodiments and drawings, but are not limited thereto.

[0046] The Ca-S compound free-cutting non-quenched and tempered steel for cutting in the present invention is smelted by UHP (overpower electric furnace) + LF (extra-furnace refining) process, continuous casting casting slab-heating-rolling lumber-rolling controlled cooling process Production of steel. Embodiments 1-5 specifically illustrate how the present invention is implemented with the production process of Φ50mm steel.

[0047] The production process steps of Ca-S composite free-cutting non-quenched and tempered steel for cutting are as follows:

[0048] (1) Smelting and alloying, electric furnace smelting, tapping, LF refining outside the furnace. In order to ensure the form of easy-cutting inclusions in the steel, the smelting technology is adopted to add S wire to the steel first, then add Ca-Si...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a Ca-S composite free-cutting non-quenched and tempered steel for cutting which has high cutting property and the manufacturing method thereof. The steel is composed of 0.44% to 0.49% of C, 0.30% to 0.60% of Si, 1.20% to 1.50% of Mn, 0.08% to 0.12% of V, no more than 0.30% of Cr, Ni and Cu, 0.040% to 0.065% of S, no more than 0.035% of P, 0.001% to 0.010% of Ca, 0.01% to 0.03% of Al, and the balance Fe and unavoidable impurity. According to the method, the compositions of inclusion in steel are controlled by ladle argon blowing and Ca-S composite processing, casting blank is poured by continuous casting, the average temperature for heating billet in a heating furnace is 1180 DEG C to 1220 DEG C, the heating time is 2 to 3 hours, the rolling starting temperature is 1100 DEG C to 1150 DEG C, the rolling finishing temperature is 850 DEG C to 1000 DEG C, the cooling speed of the rolled steel is 1.5 DEG C per second to 2.5 DEG C per second, the cooling bed cooing in pile temperature is 600 DEG C to 700 DEG C. The steel has superior mechanical property and free-cutting property.

Description

technical field [0001] The invention belongs to the technical field of metallurgy and relates to a free-cutting non-quenched and tempered steel and a manufacturing method thereof, in particular to a Ca-S composite free-cutting non-quenched and tempered steel with high cutting performance and a manufacturing method thereof. Background technique [0002] Non-quenched and tempered steel is a mechanical structural steel that can meet the performance requirements without quenching and tempering treatment. Using this kind of steel to manufacture parts can save the quenching and tempering heat treatment process and equipment, and at the same time, avoid the waste products generated during the heat treatment process, reducing It reduces pollution and reduces energy consumption. This kind of steel is an energy-saving steel. my country is rich in resources such as vanadium and titanium, and the development of non-quenched and tempered steel is not only in line with my country's nation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/46C21C5/52B21B1/46
CPCY02P10/20
Inventor 王广连戈文英杜显彬翟正龙李猛郑桂芸张伟王学利何庆文张利平温建波张海霞姜艳东张春苗
Owner SHANDONG IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap