Temperature adjustment coating and preparation thereof

A coating and temperature adjustment technology, applied in the direction of coating, latex paint, etc., can solve the problems of non-appearance, ineffective use of phase change potential, external leakage of phase change materials, etc., to achieve pollution prevention, stable adjustment of temperature range, high phase change The effect of changing enthalpy

Active Publication Date: 2009-01-21
CHINA BUILDING MATERIALS ACAD
View PDF0 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Now the coatings on the market are developing rapidly. With the call of the country for energy conservation and emission reduction, various environmental protection and energy-saving functional coatings have emerged, such as coatings with thermal insulation functions, coatings with heat insulation functions, and coatings with ant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Temperature adjustment coating and preparation thereof
  • Temperature adjustment coating and preparation thereof
  • Temperature adjustment coating and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The paint used in this embodiment is common paint, and the organic-inorganic composite phase change material is expanded perlite composite paraffin prepared by the above method.

[0037] Temperature adjustment coating preparation process:

[0038] Raw materials for producing coatings (all are commonly used raw materials in coating production, commercially available products):

[0039] Ingredients Mass (g)

[0040] water 200

[0041] Cellulose 2.5

[0042] PH regulator AMP-95 1

[0043] Propylene Glycol 5

[0044] Dispersant DP-270 2

[0045] Defoamer NXZ 8

[0046] Kaolin 100

[0047] Heavy calcium powder 150

[0048] Talc 35

[0049] Pure acrylic emulsion 100

[0050] Vinegar Acrylic Emulsion 70

[0051] Alcohol ester dodeca 2.5

[0052] Antifungal agent HF 4

[0053] Get 34 grams (5% of coating weight) by 1) the expanded perlite-octadecane that prepares, stir after mixing with 34 grams of pure acrylic emulsion;

[0054]Weigh water according to the requir...

Embodiment 2

[0059] The coating used in this embodiment is an anti-corrosion coating, and the organic-inorganic composite phase change material is attapulgite-composited octadecane (prepared from 3).

[0060] The preparation process is:

[0061] Raw materials for producing coatings (all are commonly used raw materials in coating production, commercially available products):

[0062] Ingredients Mass (g)

[0063] water 220

[0064] Cellulose 2.5

[0065] PH regulator AMP-95 1

[0066] Propylene Glycol 5

[0067] Dispersant DP-270 2

[0068] Defoamer NXZ 8

[0069] Kaolin 100

[0070] heavy calcium 150

[0071] Talc 35

[0072] Pure acrylic emulsion 100

[0073] Silicone acrylic emulsion 100

[0074] Alcohol ester dodeca 2.5

[0075] Antifungal agent HF 4

[0076] Functional components: Take 42 grams (6% of the paint weight) of attapulgite compound octadecane, mix it with 42 grams of silicone acrylic emulsion and stir evenly;

[0077] According to the method of Example 1, the r...

Embodiment 3

[0084] In this example, an organic-inorganic composite phase change material is added to the existing paint.

[0085] The preparation process is:

[0086] Paint: cbma common interior wall paint (commercially purchased)

[0087] Functional component: expanded perlite-liquid paraffin / octadecane (prepared from 2). Get 40 grams (5% of coating weight), mix with equal amount of pure acrylic emulsion (40 grams) and stir evenly;

[0088] Add 80 grams of prepared functional components and 40 grams of pure water into 800 grams of paint, and stir until the mixture is uniform to obtain a modified temperature-adjusted paint for ordinary paint.

[0089] Use the same method as Example 1 to carry out the performance test, the result: after standing for 24 hours, the coating does not have caking and precipitation;

[0090] Temperature adjustment function of coating: The test result of differential scanning calorimeter shows that this coating has obvious phase change material endothermic pea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides thermal control paint and a preparation method thereof, belonging to the building material filed. The thermal control paint which is novel functional paint is manufactured by adding organic and inorganic composite phase-change materials in common paint or functional paint, wherein the organic and inorganic composite phase-change materials are obtained by compounding expanded perlite, attapulgite, zeolite or sepiolite and paraffin or octadecane. The thermal control paint not only has the prior functions and the effect of beautifying the environment, but also has the phase-change thermal control function, can automatically adjust the indoor temperature, and improve the indoor comfort degree; in addition, the thermal control paint is the environment-friendly paint which is energy-saving and pollution-free.

Description

Technical field: [0001] The invention relates to the field of building energy-saving materials, in particular to coatings with a temperature-adjusting function. Background technique: [0002] In recent years, the energy shortage problem is one of the problems that the country urgently needs to solve. In the national "Eleventh Five-Year" scientific and technological research project, we attach great importance to the research work of energy-saving materials. Temperature-regulating phase change materials can absorb or release a large amount of latent heat during the phase change process, and can be widely used in the fields of heat storage and temperature control. In the past 20 years, they have developed rapidly in European and American countries. Phase change energy storage composite material is a kind of thermal functional composite material, which can store energy in its carrier in the form of phase change latent heat, and realize energy conversion between different space...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D7/12C09D5/02C09D133/04
Inventor 冀志江李海建王静侯国艳王晓燕王继梅
Owner CHINA BUILDING MATERIALS ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap