Method for preparing coated paper

A technology of coated paper and pulp blending, which is applied in papermaking, coating, paper coating, etc., can solve the problems of lack of wood resources for papermaking, high wood utilization rate, and difficulty in beating, so as to improve the utilization efficiency of wood resources and reduce production cost effect

Active Publication Date: 2009-04-29
山东晨鸣纸业集团股份有限公司 +1
View PDF0 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantages: First, with the expansion of the scale of wood utilization industries such as papermaking, and the reduction of the area of ​​global industrial forests, wood resources for papermaking are gradually scarce, and it is necessary to develop high wood utilization rates, especially the development of inorganic raw materials to replace organic wood fiber raw materials Second, with the needs of social development, papermaking products need to develop new products with safety and anti-counterfeiting functions in addition to the original conventional products to meet the special needs of the society; third, papermaking is a high energy-consuming industry, and among them The beating of papermaking raw materials is the most energy-consuming process in the industrial chain. It is difficult to beating and consumes a lot of energy. The average power consumption per ton of pulp is 300-315kwh. A strategic issue that urgently needs to be resolved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing coated paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] (1) 1% of the active acicular wollastonite mineral fiber and 2% of the yellow colorless fluorescent fiber are mixed evenly to prepare the fiber batching by weight of the dry wood pulp, and it is used for subsequent use;

[0047] (2) Additives, whose components include: 25% CaCO by weight of the dry slurry 3 , 1.5% cationic starch, 1.2% alkyl ketene dimer, 0.07% cationic polyacrylamide and 0.2% polyaluminum chloride;

[0048] (3) Mix calcium carbonate, calcium sulfate, zeolite, sericite, smectite, urea-based resin, melamine-based resin, propylene-based resin, and vinylidene chloride-based resin to prepare paper pigments, and then add retention aids respectively , filter aids, paper strength additives, fixatives, internal sizing agents, dyes, optical brighteners, pH regulators, defoamers, color tone control agents, and slime-killing agents are mixed evenly to prepare auxiliary materials and set aside;

[0049] (4) Cationic starch paste, carboxymethyl cellulose, polyvinyl...

Embodiment 2

[0067] (1) 5% active acicular wollastonite mineral fibers and 0.8% yellow, red and blue colorless fluorescent fibers are mixed uniformly to prepare fiber ingredients by weight of absolute dry wood pulp, and are set aside;

[0068] (2) Additives, whose components include: 25% CaCO by weight of the dry slurry 3 , 0.9% cationic starch, 0.8% alkyl ketene dimer, 0.02% cationic polyacrylamide and 0.12% polyaluminum chloride, spare;

[0069] (3) Mix kaolin, melamine-based resin, propylene-based resin, and vinylidene chloride-based resin to prepare paper pigments, then add retention aids, filter aids, paper strength additives, fixatives, and internal sizing agents. Agents, dyes, fluorescent whitening agents, pH regulators, defoamers, color tone control agents, slimeicides, mixed evenly, prepared auxiliary materials, and set aside;

[0070] (4) Mix the oxidized starch paste and methyl cellulose evenly to obtain a surface sizing solution, which is set aside;

[0071] (5) Mix the groun...

Embodiment 3

[0087](1) 8% active acicular wollastonite mineral fibers and 0.9% red and blue colorless fluorescent fibers are mixed uniformly to prepare fiber ingredients by weight of the dry wood pulp, and are set aside;

[0088] (2) Additives, whose components include: 25% CaCO by weight of the dry slurry 3 , 1.0% cationic starch, 1.0% alkyl ketene dimer, 0.05% cationic polyacrylamide and 0.18% polyaluminium chloride, spare;

[0089] (3) Mix kaolin, calcined kaolin, calcium carbonate, calcium sulfate, barium sulfate, titanium dioxide, talc, zinc oxide, and polystyrene-based resin to prepare paper pigments, then add retention aids, filter aids, and paper Strength additives, fixatives, internal sizing agents, dyes, optical brighteners, pH regulators, defoamers, color tone control agents, and slime-killing agents are mixed evenly to prepare auxiliary materials and set aside;

[0090] (4) Mix amphoteric starch paste, methyl cellulose, polyvinyl alcohol, hide glue evenly, make surface sizing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
opacityaaaaaaaaaa
diameteraaaaaaaaaa
transparencyaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing enamel paper. Through the addition of cellulase, the preparation method effectively reduces energy consumption of pulping and improves pulp quality; a mineral fiber ingredient is used to replace wood fiber so as to save wood resource and simultaneously reduce production cost; and the prepared enamel paper has anti-counterfeit function.

Description

technical field [0001] The invention relates to a method for preparing coated paper. Background technique [0002] At present, the coated base paper is generally made of wood fiber. Among them, high-grade products, such as coated paper, are made of bleached chemical wood pulp of coniferous wood or hardwood bleached chemical wood pulp; Bleached chemical wood pulp of leaf wood or bleached chemical wood pulp of broad-leaved wood, plus a small amount of semi-chemical thermomechanical pulp, the coated base paper is filled with inorganic pigments, and the ash content of the base paper after burning (ISO1762: 2001) is average 10-20%. Its disadvantages: First, with the expansion of the scale of wood utilization industries such as papermaking, and the reduction of the area of ​​global industrial forests, wood resources for papermaking are gradually scarce, and it is necessary to develop high wood utilization rates, especially the development of inorganic raw materials to replace org...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/00C12S3/08D21H13/38D21H13/00
Inventor 陈洪国尹同远耿光林方辉张革仓赵亮王才喜
Owner 山东晨鸣纸业集团股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com