Ethylene naphthalene and paradiazine dye and application thereof to dye-sensitized solar cells.

A technology of solar cells and dye sensitization, which can be used in different fields and can solve the problems of high cost and limited application

Inactive Publication Date: 2009-08-26
DALIAN UNIV OF TECH
View PDF0 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Currently the most used is M. The N3 and N719 dyes invented by the professor's research group are ruthenium complex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ethylene naphthalene and paradiazine dye and application thereof to dye-sensitized solar cells.
  • Ethylene naphthalene and paradiazine dye and application thereof to dye-sensitized solar cells.
  • Ethylene naphthalene and paradiazine dye and application thereof to dye-sensitized solar cells.

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Example 1: Synthesis of 3-diphenylamine-8,9-dicarboxy-acenaphthopyrazine

[0030] (1) Synthesis of 5-bromoacenaphthylquinone:

[0031]

[0032] In a 500mL two-necked flask, add 20g (109.8mmol) of acenaphthylquinone and 25.0mL of liquid bromine (466.8mmol), start stirring, control the temperature in an oil bath at 6070°C, and reflux the reaction solution. After 2h, stop the reaction and add hydrogen sulfite Sodium aqueous solution until the reaction solution is colorless. After diluting with water, filter under reduced pressure, and wash with water for several times for beating until pH=7.0. The filter cake was recrystallized four times in glacial acetic acid to obtain 5-bromoacenaphthoquinone as brown-yellow needle-like crystals with a yield of 90%. NMR 1 H NMR (400MHz, DMSO-d 6 )δ8.39(d, 1H), 8.21(d, 1H), 8.15(d, 1H), 8.04(t, 1H), 7.96(d, 1H); HRMS-EI(70eV) m / z.

[0033] (2) Synthesis of 5-diphenylamine-acenaphthenequinone:

[0034]

[0035] The reaction is...

Embodiment 2

[0043] Example 2: Synthesis of 3-diphenylamine-8,9-dicarboxy-acenaphthopyrazine-acene

[0044] (1) Synthesis of 3-diphenylamine-8,9-dicyano-acenaphthopyrazine-acene

[0045]

[0046] Synthetic method is substantially the same as (3) in embodiment 1, nuclear magnetic 1 HNMR ((CDCl 3 )): δ7.12-7.16(m, 6H), 7.32(t, 4H), 7.46(d, 1H), 7.62(t, 1H), 7.86(d, 1H), 8.36(d, 1H), 8.42 (d, 1H), 8.60 (d, 2H).FAB MS: m / e 471 (M + ).

[0047] (2) Synthesis of 3-diphenylamine-8,9-dicarboxy-acenaphthopyrazine-acene

[0048]

[0049] Synthetic method is substantially the same as (4) in embodiment 1, nuclear magnetic 1 HNMR ((DMSO-d 6 )): δ7.09-7.14(m, 6H), 7.35(t, 4H), 7.44(d, 1H), 7.30(t, 1H), 7.80(d, 1H), 8.38-8.41(m, 4H) .MS API-ES: [M-H] + (508, M / Z).

Embodiment 3

[0050] Example 3: Synthesis of 3-diphenylamine-8-carboxy-acenaphthopyrazine and 3-diphenylamine-9-carboxy-acenaphthopyrazine

[0051] (1) Synthesis of 3-diphenylamine-8-cyano-acenaphthopyrazine and 3-diphenylamine-9-cyano-acenaphthopyrazine

[0052]

[0053] The synthetic method is basically the same as (3) in Example 1, and what this reaction obtains is 3-diphenylamine-8-cyano-acenaphthopyrazine and 3-diphenylamine-9-cyano-acenaphthopyrazine The isomers of acene, the isomers cannot be separated by silica gel column, and the isomers can not be separated by NMR 1 HNMR showed that the ratio of isomers was about 1:1. NMR 1 HNMR (CDCl 3 ): δ7.10-7.16(m, 6H), 7.28-7.32(m, 4H), 7.45-7.48(m, 1H), 7.59(t, 1H), 7.83(d, 1H), 7.86-7.90(m , 1H), 8.25-8.28(m, 1H), 8.34-8.39(m, 2H), 8.54(s, 1H).FAB MS: m / e 446(M + ).

[0054] (2) Synthesis of 3-diphenylamine-8-carboxy-acenaphthopyrazine and 3-diphenylamine-9-carboxy-acenaphthopyrazine

[0055]

[0056] The synthetic method is b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the application field of photoelectric conversion materials in the fine chemistry industry, in particular to ethylene naphthalene and paradiazine dye and application thereof to dye-sensitized solar cells. The dye is characterized by taking ethylene naphthalene and paradiazine and derivatives thereof as a conjugated system, one end of the conjugated system is connected with adjacent dicarboxyl or a single carboxyl as electron withdraw group which is used to be absorbed on TiO2, and the other end thereof is connected with different electron-donating groups to form an electric push-pull type organic dye. As taking the ethylene naphthalene and paradiazine as the conjugated system ensures a fine plane structure, by connecting the conjugated system with the electron group and the electron-withdrawing group, electrons are easy to transfer in case of excited state and the dye is led to generate unique photoelectrochemical property, therefore enjoying fine application performance in dye-sensitized solar cells; in addition, the ethylene naphthalene and paradiazine dye features simple synthetic method and easily available raw materials, thus being capable of replacing noble metal photosensitive dyes with relatively high price and effectively reducing the cost of the dye-sensitized solar cells.

Description

technical field [0001] The invention belongs to the application field of photoelectric conversion materials in fine chemical industry, and specifically relates to a class of conjugated systems using acenaphthopyrazine and its derivatives, one end of which is connected to an adjacent dicarboxylic group or a single carboxyl group as an electron-withdrawing group, which is used to adsorb on TiO 2 The other end is connected with different electron-donating groups to form a class of electron push-pull dyes, and the application of the dyes in dye-sensitized solar cells. Background technique [0002] The dye-sensitized solar cell was developed in 1991 by M. A new type of device for converting solar energy into electrical energy proposed by the professor. Its composition is generally: a photoanode composed of a nanoporous oxide film adsorbed with a photosensitive dye and a transparent conductive substrate. between electrolyte and sealing material. This type of battery has the adv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09B57/00H01G9/20H01L51/42H01L51/46
CPCY02E10/542Y02E10/549
Inventor 崔京南孔志霞杨翠翠马廷丽周慧芝孙立成
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap