Method for preparing sintering-expanded haydite by taking red mud of Bayer process as main raw material

A main raw material, the technology of Bayer method, applied in the direction of solid waste removal, sustainable waste treatment, solid waste management, etc., can solve the problems of high difficulty and low degree of development and utilization, and achieve uniform internal pores and good vitrification degree Effect

Inactive Publication Date: 2009-09-23
GUILIN UNIVERSITY OF TECHNOLOGY
View PDF2 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with the high calcium and low alkali characteristics of sintered red mud (in general, SiO 2 19-26%, Fe 2 o 3 3-11%, Na 2 O1-4%, Al 2 o 3 4-10%, CaO 40-47%), Bayer process red mud has the characteristics of high iron, high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing sintering-expanded haydite by taking red mud of Bayer process as main raw material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0010] Grind Guangxi Pingguo Al Bayer process red mud, Guilin power plant fly ash, and waste glass (see Table 1 for its chemical composition) and pass through a 160-mesh sieve. Then according to the mass ratio, Bayer process red mud: fly ash: waste glass: starch: carbon powder: sodium hexametaphosphate = 50: 25: 20: 2: 2: 1, mix evenly, add 5% water of raw material quality , stirred for 5 minutes, and formed into balls after being stale for 20 minutes. After forming the balls, put the pellets into an oven and bake at 105°C for 2 hours. After drying, put them into a muffle furnace at 600°C for preheating for 10 minutes, then quickly move them to a high-temperature silicon-molybdenum furnace and bake at 1140°C for 10 minutes. The discharge ball is forced to cool.

[0011] The prepared incinerated ceramsite has a good degree of vitrification on the outer surface, relatively uniform internal pores, mainly closed pores, its water absorption rate is less than 1%, and its bulk densi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a sintering-expanded haydite by taking red mud of Bayer process as a main raw material, comprising the following steps of by taking the red mud of Bayer process, fly ash, wasted glass, starch, carbon powder and sodium hexametaphosphate as raw materials, respectively grinding the red mud of Bayer process, the fly ash and the wasted glass by a sieve of 160 meshes; proportioning and uniformly mixing the sieved raw materials by the following mass ratio: (50-60):(20-25):(15-20):2:2;1 for Bayer process, fly ash, wasted glass, starch, carbon powder and sodium hexametaphosphate respectively; adding the water of 5-10% by mass in the raw material, mixing the mixture for 5-10min, decaying the mixture for 20-30min and forming balls; baking the formed balls in an oven for 2-5h at the temperature of 105 DEG C; drying the balls and preheating the balls in a muffle for 10-30min at the temperature of 600 DEG C; after preheating, quickly moving and baking the balls in a high-temperature Si-Mo furnace for 10-30min at the temperature of 1100-1200 DEG C; and after finishing baking, opening the furnace door, taking out the balls and forcibly cooling the balls. The sintering-expanded haydite prepared by the method has fine vitrification degree on the external surface and uniform internal aperture and takes closed holes as main ones.

Description

technical field [0001] The invention relates to a method for preparing ceramsite with swelling performance as light aggregate by using Bayer process red mud (low-silicon and high-iron) as the main raw material. Background technique [0002] Ceramsite is one of the fastest growing new building materials in my country in recent years. In 1995, the annual output of ceramsite was only 2 million cubic meters, which reached 3 million cubic meters in 2000, and exceeded 5 million cubic meters in 2004, with an annual growth rate of 20%. It is expected to exceed 10 million cubic meters in 2010. Intumescent ceramsite is widely used in the construction field due to its low thermal conductivity, excellent thermal insulation performance, good sound absorption and sound insulation performance, high temperature resistance, anti-aging, acid and alkali resistance, no radioactivity, earthquake resistance, and good durability. . [0003] With the development of ceramsite, behind its heating t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B18/04B09B3/00
CPCY02W30/91
Inventor 谢襄漓王林江赵建新
Owner GUILIN UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap