Automotive performance improving agent, preparation method and using method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of improving agent and performance, which is applied in the field of automobile performance improving agent, which can solve the problems of uneconomical durability, changing the chemical properties of oil products, eroding the secondary pollution of the engine, etc., and achieve the effects of saving fuel, improving automobile performance, and reducing exhaust emissions
Inactive Publication Date: 2009-10-28
YANTAI XINFA ENVIRONMENTAL SCI & TECHCO
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] Adding automotive performance improvers to the fuel tank, adding chemically will change the chemical properties of the oil and may cause engine erosion and secondary pollution problems
And with the loss of fuel, the car performance improver is also lost together, and needs to be added continuously with the addition of fuel, which is not economical and durable
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0022] Automobile performance improver, composed of the following substances processed by nanotechnology
[0023] According to mass percentage, silicon micropowder SiO 2 62%, titanium dioxide TiO 2 6%, Al 2 o 3 15%, Pd 4%, MgO 13%.
[0024] 1. Silica powder is made of natural quartz (SiO 2 ) or fused silica (natural quartz melted at high temperature and cooled amorphous SiO 2 ) Micropowder processed by multiple processes such as crushing, ball milling (or vibration, jet milling), flotation, pickling purification, high-purity water treatment, etc. Silica powder is a non-toxic, odorless, non-polluting inorganic non-metallic material. It has good temperature resistance, acid and alkali corrosion resistance, poor thermal conductivity, high insulation, low expansion, stable chemical properties, and high hardness.
[0025] 2. Titanium dioxide, scientific formula: TiO 2 , white powder, non-toxic, extremely stable chemical properties, almost no interaction with any substanc...
Embodiment 2
[0049] The difference between this embodiment and embodiment 1 is that
[0050] Automobile performance improver, composed of the following substances processed by nanotechnology
[0051] According to mass percentage, SiO 2 50%, TiO 2 2%, Al 2 o 3 25%, Pd 7%, MgO 16%.
Embodiment 3
[0053] The difference between this embodiment and embodiment 1 is that
[0054] Automobile performance improver, composed of the following substances processed by nanotechnology
[0055] According to mass percentage, SiO 2 70%, TiO 2 1%, Al 2 o 3 19%, Pd 2%, MgO 8%.
[0056] The above products have been tested by several testing agencies of the Ministry of Communications and tested by hundreds of gasoline and diesel vehicles of actual users. Statistics show that they can save fuel by 12-15%, reduce noise and reduce pollution by more than 90-95%. Car dynamics increased by 10-15%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
melting point
aaaaa
aaaaa
hardness
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to an automotive performance improving agent, a preparation method and a using method thereof, which belong to the technical field of automotive performance improving agents. The automotive performance improving agent consists of the following substances which are processed through nanotechnology by weight percentage: 50 to 70 percent of SiO2, 1 to 6 percent of TiO2, 15 to 25 percent of Al2O3, 2 to 7 percent of Pd, and 8 to 16 percent of MgO. The preparation method comprises the following steps: 1, adopting the nanotechnology to process the SiO2, the TiO2, the Al2O3, the Pd and the MgO into 80 to 200 nano-particles respectively; and 2, mixing the nano-particles according to mass percent. The using method comprises the following steps: 1, adding the improving agent into an engine water tank according to a ratio that 2 liters of automobile air displacement corresponds to 120-160 milliliters of an improving agent solution; and 2, starting an engine until the water temperature in the water tank is over 30 DEG C. The automotive performance improving agent and the methods have the advantages of economy, environmental protection and improvement on the automotive performance, and achieve the aims of reducing exhaust emissions, saving fuels, reducing noises and increasing power, and the detections show that the fuel-efficient rate reaches between 12 and 15 percent, the noise reduction rate and the pollution discharge reduction rate reach between 90 and 95 percent, and the automobile dynamic quality is improved by 10 to 15 percent.
Description
1. Technical field [0001] The invention relates to an automobile performance improver, a preparation method and a use method, and belongs to the technical field of automobile performance improvers. 2. Background technology [0002] At present, in order to save fuel and reduce environmental pollution, there are many automobile performance improvers, which are all added to the fuel tank. These automobile performance improvers have some problems while saving fuel and reducing pollution. [0003] Adding automotive performance improvers to the fuel tank, adding chemically will change the chemical properties of the oil and may cause engine erosion and secondary pollution problems. And along with the consumption of fuel oil, the vehicle performance improver is also lost together, needs to add continuously along with the addition of fuel oil, uneconomical and durable. 3. Contents of the invention [0004] The purpose of the present invention is to solve the problems in the above-...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more