Fluorosilicone rubber long-acting antifouling flashover coating for UHV and preparation method thereof

An anti-pollution flashover coating and fluorosilicone rubber technology, applied in the coating and other directions, can solve the problems of the flame retardant level being difficult to reach the FV-0 level, the flame retardant level is low, and cannot meet the requirements of hydrophobicity, etc., and achieve excellent hydrophobicity. and anti-pollution flashover capability, improving mechanical properties, and increasing anti-pollution flashover voltage

Active Publication Date: 2012-02-08
WUHAN NARI LIABILITY OF STATE GRID ELECTRIC POWER RES INST +1
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Before the present invention was proposed, the publication number: CN 1321712A "An RTV single-component hydrophobic long-lasting anti-fouling flashover coating", the coating added a small amount of single basic flame retardant, less than 40% of the solid content of the coating, The flame retardant level is very low, and it is difficult to reach the FV-0 level
[0008] In addition, the publication number: CN 1847339A "Preparation method of anti-fouling flashover coating", the coating uses silicone rubber as the main material, and the hydrophobic angle is 114°. Although the hydrophobicity meets the DL / T627-2004 standard, it cannot meet the requirements of UHV power transmission and transformation. and anti-icing requirements for hydrophobicity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorosilicone rubber long-acting antifouling flashover coating for UHV and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Nanoscale fumed silica (specific surface area 200m 2 / g), aluminum hydroxide, decabromodiphenyl ether, and iron red pigment were dried at 100°C for 24 hours; fluorosilicone rubber (viscosity 5500mPa s) 10, silicone rubber (viscosity 4500mPa s) 30, nanoscale gas phase Add white carbon black 6 to the CH tank mixer, take it out after stirring for 60 minutes; put it into a vacuum stirring reactor, and vacuumize it for 3 hours while stirring, the vacuum degree is -0.08MPa; take out the slurry and put it into a high shear disperser Add solvent halide 45 and disperse at low speed for 20 minutes; aluminum hydroxide 4, decabromodiphenyl ether 1, antioxidant tert-butylhydroquinone 0.06, leveling agent 3, pigment iron red 0.3 slowly add to the slurry being stirred , stirring for 3 hours; grinding for 2 hours; under the protection of nitrogen, add defoamer 0.2, catalyst dibutyltin dilaurate 0.04, and stir for 1 hour; take out the slurry and put it into an explosion-proof high-shear...

Embodiment 2

[0034] Nanoscale fumed silica (specific surface area 200m 2 / g), aluminum hydroxide, decabromodiphenyl ether, and iron red pigment were dried at 100°C for 24 hours; fluorosilicone rubber (viscosity 5500mPa s) 10, silicone rubber (viscosity 4500mPa s) 25, nanoscale gas phase Add white carbon black 6 to the CH tank mixer, take it out after stirring for 60 minutes; put it into a vacuum stirring reactor, and vacuumize it for 3 hours while stirring, the vacuum degree is -0.08MPa; take out the slurry and put it into a high shear disperser Add solvent halide 50 and disperse at low speed for 20 minutes; aluminum hydroxide 4, decabromodiphenyl ether 1, antioxidant tert-butyl hydroquinone 0.06, leveling agent 3, pigment iron red 0.3 slowly add to the slurry being stirred , stirring for 3 hours; grinding for 2 hours; under the protection of nitrogen, add defoamer 0.2, catalyst dibutyltin dilaurate 0.04, and stir for 1 hour; take out the slurry and put it into an explosion-proof high-shea...

Embodiment 3

[0036] Nanoscale fumed silica (specific surface area 200m 2 / g), aluminum hydroxide, decabromodiphenyl ether, and iron red pigment were dried at 100°C for 24 hours; fluorosilicone rubber (viscosity 5500mPa s) 5, silicone rubber (viscosity 4500mPa s) 25, nanoscale gas phase Add white carbon black 8 to the CH tank mixer, take it out after stirring for 60 minutes; put it into the vacuum stirring reactor, and vacuumize it for 3 hours while stirring, the vacuum degree is -0.08MPa; take out the slurry, put it into the high shear dispersion In the machine, add solvent haloalkane 55 and stir at low speed for 20 minutes; aluminum hydroxide 3, decabromodiphenyl ether 1, antioxidant tert-butyl hydroquinone 0.06, leveling agent 2, pigment iron red 0.3 slowly add to the stirring Slurry, stirring time 3 hours; grinding 2 hours; under the protection of nitrogen, add defoamer 0.2, catalyst dibutyltin dilaurate 0.04, stir for 1 hour; take out the slurry and put it into an explosion-proof high-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention provides a fluorosilicone rubber long-acting antifouling flashover coating for UHV and a preparation method thereof. The formula of the fluorosilicone rubber long-acting antifouling flashover coating (FRTV for short) is based on mass percentage, fluorosilicone rubber: 5-30 %; Silicone rubber: 10-30%; Nanoscale fumed silica: 4-8%; Composite flame retardant: 0.5-8%; Curing agent: 0.2-0.5%; Catalyst: 0.01-0.05%; Antioxidant: 0.02-0.08%; leveling agent: 2-8%; defoamer: 0.2-0.4%; pigment: 0.1-0.5%; solvent: 30-60%. The composite flame retardant is composed of inorganic aluminum hydroxide and organic decabromodiphenyl ether, wherein the inorganic aluminum hydroxide: 1-6%; the organic decabromodiphenyl ether: 0.5-3%. The coating provided by the invention has a simple preparation process, good weather resistance, oil resistance and longer service life.

Description

technical field [0001] The invention provides a fluorosilicone rubber long-acting anti-pollution flashover coating for UHV (hereinafter referred to as FRTV coating) and a preparation method thereof, which is applied to UHV substations and UHV line external insulation equipment, and belongs to the field of UHV external insulation antifouling . technical background [0002] my country has a vast territory, and energy resources are mostly distributed in the central, western and northern regions, while loads are mostly distributed in the eastern and southern regions. The biggest feature of the UHV power grid is large capacity and long-distance power transmission, which can realize a wide range of optimal allocation of energy resources and ensure reliable power supply. The State Grid Corporation of China takes the development goal of accelerating the construction of a strong and smart grid in combination with the national conditions of the country, and builds the UHV grid as the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/06C09D7/12C09D5/00
Inventor 杜忠东袁明仁谭进查宜萍郑志强叶春勇刘江钒董中强
Owner WUHAN NARI LIABILITY OF STATE GRID ELECTRIC POWER RES INST