Ti-Al series intermetallic compound alloy

A technology of intermetallic compounds and alloys, applied in the field of titanium alloys

Active Publication Date: 2010-01-06
攀枝花市银江金勇工贸有限责任公司
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, the present invention also solves the technical problem of producing Ti-Al intermetallic compound alloy products by smelting vanadium-titanium raw materials with high impurity content in Panxi area, thereby rewriting the problem that titanium alloys cannot be produced due to the high impurity content of Panxi titanium-containing raw materials. History, filling the gaps in the country

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] A kind of Ti 3 Al-based alloy Ti-22Al-20Nb-5V is characterized in that: 100Kg of titanium-containing raw materials in Panxi area is equipped with auxiliary materials with the following weight ratio:

[0053] Metal aluminum 75Kg, quicklime 25Kg, potassium chlorate 20Kg, calcium-sodium treatment agent 3Kg, containing Nb 2 o 5 45kg of 99% niobium oxide, containing V 2 o 5 10kg of 99% vanadium pentoxide.

[0054] The calcium-sodium treatment agent is a mixture of fluorite and sodium carbonate in a weight ratio of 1:1.

[0055] The concrete process step of described alloy preparation is as follows:

[0056] Based on 2 tons of titanium-containing raw materials, the raw materials and various auxiliary materials are weighed according to the above weight ratio, and the titanium raw materials from Panxi area are added to the rotary furnace. The silo is sent into the mixer and mixed evenly, and then from the batching silo, quicklime, calcium-sodium series treatment agent, ni...

Embodiment 2

[0061] A kind of Ti 3 Al-based alloy Ti-25Al-17Nb is characterized in that: 100Kg of titanium-containing raw materials in Panxi area is equipped with auxiliary materials with the following weight ratio:

[0062] Metal aluminum 95Kg, quicklime 25Kg, potassium chlorate 20Kg, calcium-sodium treatment agent 3Kg, containing Nb 2 o 5 40kg of 99% niobium oxide.

[0063] The calcium-sodium treatment agent is a mixture of fluorite and sodium carbonate in a weight ratio of 1:1.

[0064] The concrete process step of described alloy preparation is as follows:

[0065] Based on 2 tons of titanium-containing raw materials, the raw materials and various auxiliary materials are weighed according to the above weight ratio, and the titanium raw materials from Panxi area are added to the rotary furnace. The silo is sent into the mixer and mixed evenly, and then niobium oxide, quicklime, calcium-sodium treatment agent, metal aluminum, and potassium chlorate are sequentially added from the bat...

Embodiment 3

[0070] A TiAl-based alloy Ti-46A1-5Nb-2V-2Si is characterized in that: 100Kg of titanium-containing raw materials in Panxi area is equipped with auxiliary materials with the following weight ratio:

[0071] Metal aluminum 115Kg, quicklime 25Kg, potassium chlorate 22Kg, calcium-sodium treatment agent 3Kg, containing Nb 2 o 5 99% niobium oxide 12kg, containing V 2 o 5 5kg of 99% vanadium pentoxide and 3kg of silicon raw material.

[0072] The calcium-sodium treatment agent is a mixture of fluorite and sodium carbonate in a weight ratio of 1:1.

[0073] The concrete process step of described alloy preparation is as follows:

[0074] Based on 2 tons of titanium-containing raw materials, the raw materials and various auxiliary materials are weighed according to the above weight ratio, and the titanium raw materials from Panxi area are added to the rotary furnace. The bin is sent into the mixer to mix well, and then niobium oxide and vanadium pentoxide, calcareous metallurgical...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a Ti-Al series intermetallic compound alloy which is smelted from a raw material containing titanium in the Panxi area. Per 100Kg of the raw material containing titanium of the Panxi area contains the following auxiliary materials: 75-115Kg of metallic aluminum, 15-25Kg of calcareous metallurgical auxiliary material, 18-28Kg of potassium chlorate and 1.5-3.5Kg of calcium-sodium series treating agent and can also contain any one or a combination of the following two auxiliary materials: 3-10Kg of vanadium series raw material, 12-45Kg of columbium series raw material, 4-6Kg of carbon raw material or 3-4Kg of silicon raw material. The invention has stable raw material source and safe and reliable production process, and a prepared Ti-Al series intermetallic compound alloy product has stable product quality and can meet the technology and quality requirements on Ti-Al series intermetallic compounds of the modern industry. Meanwhile, the invention also solves the technical problem of smelting the Ti-Al series intermetallic compound alloy product by using a vanadium-titanium raw material with a high impurity content of the Panxi area, thereby rewriting the history that the raw material containing titanium of the Panxi area cannot be used for producing titanium alloy because of the high impurity content and filling a domestic blank.

Description

technical field [0001] The invention relates to a titanium alloy, in particular to a Ti-Al intermetallic compound produced by smelting titanium-containing raw materials in Panxi area. Background technique [0002] Titanium alloy has the characteristics of high strength, good medium temperature performance, corrosion resistance, non-magnetic, good welding performance, etc. It is an important light metal material. In recent years, new titanium alloys newly developed by various countries in the world include aerospace titanium alloys, marine titanium alloys, biological titanium alloys, intermetallic compound engineering alloys, etc. It has been widely used in aerospace and weaponry, including military and civil aircraft, aero engines, missiles, ships, integrated nuclear reactors, light artillery, etc. [0003] Titanium-containing alloy materials include high, medium and low titanium alloy materials and composite titanium alloys. The main raw materials for production are titani...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C14/00C22C21/00C22C30/00
Inventor 何金勇杨保祥宋国菊张森文光兴
Owner 攀枝花市银江金勇工贸有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap