Non-chrome passivating agent for steel, zinc plates, aluminum and aluminum alloy pieces, zinc and zinc alloy

A chromium-free passivation agent, aluminum alloy technology, applied in the direction of metal material coating process, etc., can solve problems such as skin allergies

Inactive Publication Date: 2010-01-06
SHANGHAI PINXIN METALLURGY EQUIP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But long-term contact, some people have severe skin allergies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] The present invention is made up of following raw material by mass percentage:

[0067] Organic CS element compound 0.3%

[0068] Butyl carbamate resin 19%

[0069] r-Aminopropyltriethoxysilane 3.0%

[0070] Zirconium sodium double salt 0.9%

[0071] Acetic acid 0.8%

[0072] Glyceryl Silyl Ether 8.0%

[0073] Triammonium Phosphate 0.07%

[0074] Ethylene glycol butyl ether 1.8%

[0075] Polyethylene oxide 6.0%

[0076] Polyoxyethylene polyoxypropylene ether 0.07%

[0077] The balance is pure water.

Embodiment 2

[0079] The present invention is made up of following raw material by mass percentage:

[0080] Organic CS element compound 0.5%

[0081] Butyl carbamate resin 23%

[0082] r-Aminopropyltriethoxysilane 2.9%

[0083] Zirconium sodium double salt 1.3%

[0084] Acetic acid 0.6%

[0085] Glyceryl Silyl Ether 8.0%

[0086] Triammonium Phosphate 0.09%

[0087] Ethylene glycol butyl ether 3.0%

[0088] Polyethylene oxide 5.0%

[0089] Polyoxyethylene polyoxypropylene ether 0.05%

[0090] The balance is pure water.

Embodiment 3

[0092] The present invention is made up of following raw material by mass percentage:

[0093] Organic CS element compound 0.1%

[0094] Butyl carbamate resin 25%

[0095] r-Aminopropyltriethoxysilane 3.0%

[0096] Zirconium sodium double salt 1.0%

[0097] Acetic acid 0.5%

[0098] Glyceryl Silyl Ether 10.0%

[0099] Triammonium Phosphate 0.10%

[0100] Ethylene glycol butyl ether 1.0%

[0101] Polyethylene oxide 5.0%

[0102] Polyoxyethylene polyoxypropylene ether 0.02%

[0103] The balance is pure water.

[0104] The invention summarizes organic high molecular compounds containing various water-soluble high molecular compounds and water-soluble elements, which are mixed with water under certain process conditions to become a colorless, non-toxic, environmentally friendly, uniform, transparent and clear liquid. At room temperature, by rolling, brushing or spraying, the surface of steel, hot-dip galvanized sheet, coil or zinc, aluminum and its alloys is rapidly wette...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a non-chrome passivating agent for steel, zinc plates, aluminum and aluminum alloy pieces, zinc and zinc alloy, which consists of the following materials in percentage by mass: 0.1 to 0.5 percent of organic CS compound, 15 to 35 percent of butyl carbamate resin, 2.0 to 4.0 percent of r-aminopropyl triethoxysilane, 0.5 to 1.5 percent of sodium zirconium salt, 0.5 to 1.0 percent of acetic acid, 8.0 to 10.0 percent of glycerol silane ether, 0.05 to 0.10 percent of triammonium phosphate, 1.0 to 3.0 percent of butyl cellusolve, 3.0 to 8.0 percent of polyoxyethylene, 0.01 to 0.10 percent of polyoxyethylene polyoxypropylene ether, and the balance of pure water. The non-chrome passivating agent has the advantage that the non-chrome passivating agent is a surfactant with non-nickel, non-chrome, non-sodium nitrite, non-nitrate, non-fluorine ions, non-three strong acids and easy degradation.

Description

technical field [0001] The invention relates to a chemical reaction cross-linking film forming of metals, in particular to a chromium-free passivator for iron and steel, zinc plates, aluminum and aluminum alloy parts, and zinc and zinc alloys. Background technique [0002] The film-forming process of paint, or the film-forming mechanism, is nothing more than two types: one is that the solvent evaporates and the paint dries to form a film. It does not undergo a chemical reaction, it is a physical phenomenon. Examples include nitro lacquer and vinyl lacquer. The other is to form a film through chemical reaction cross-linking. [0003] To prevent all metals from corrosion and maximize their service life is a way to utilize the limited resources on the earth. This is a common mission and common pursuit of all human beings. [0004] Endowing metal with the best performance to meet the high requirements of people's use and decoration to the greatest extent is a major topic and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C22/48
CPCC23C2222/20
Inventor 胡惠新刘治年郁佩德邵志兴
Owner SHANGHAI PINXIN METALLURGY EQUIP