High-quality pavement petroleum asphalt material and preparation method thereof
A kind of road petroleum asphalt, high-quality technology, used in building insulation materials, building components, construction and other directions, can solve the problem of high-grade road construction that cannot meet heavy load, large traffic volume, lack of high-quality road petroleum asphalt production technology, and high asphaltene content. Advanced problems, to achieve excellent technical performance and road performance, improve the use value, improve the effect of low temperature performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0028] Example 1:
[0029] The preparation method of the high-quality road petroleum asphalt material of the present invention is as follows:
[0030] 1). Under the condition of 120-200℃, heat 89 parts by mass of the main mixed asphalt to a molten state, pump into the batching tank, add 1 part by mass of the polymer crosslinking agent at 135℃-140℃, and stir for 30min , After mixing uniformly, perform three-level high-speed shearing through the shearing machine;
[0031] 2), pump into the blending tank, add 10 parts by mass of the blended asphalt and mix evenly;
[0032] 3). Add 0.1 part of mass heat stabilizer, stir for 30min, and further grind it by colloid mill after uniformity to obtain high-quality road petroleum asphalt.
[0033] The main bitumen used refers to the vacuum residue of the residual oil and heavy crude oil after deep drawing under vacuum. The content of its four components is: asphaltene 30%. Aromatic content> 15%. The blended asphalt used refers to the ordinary ro...
Example Embodiment
[0038] Example 2:
[0039] The preparation method of the high-quality road petroleum asphalt material of the present invention is as follows:
[0040] 1) Under the condition of 120-200℃, heat 90 parts by mass of the main asphalt to the molten state, pump it into the batching tank, add 1.2 parts by mass of the polymer crosslinking agent at 140℃-145℃, and stir for 35min , After mixing uniformly, perform three-level high-speed shearing through the shearing machine;
[0041] 2). Pump into the blending tank, add 8 parts by mass of the blended asphalt and mix evenly;
[0042] 3). Add 0.05 parts by mass of heat stabilizer, stir for 35 minutes, and further grind through colloid mill after uniformity to obtain high-quality road petroleum asphalt.
[0043] The main bitumen used refers to the vacuum residue of the residual oil and heavy crude oil after deep drawing under vacuum. The content of its four components is: asphaltene 30%. Aromatic content> 15%. The blended asphalt used refers to the...
Example Embodiment
[0048] Example 3:
[0049] The preparation method of the high-quality road petroleum asphalt material of the present invention is as follows:
[0050] 1) Under the condition of 120-200℃, heat 87 parts by mass of the main asphalt to the molten state, pump it into the batching tank, add 0.9 parts by mass of polymer crosslinking agent under the condition of 135℃-140℃, and stir for 30min , After mixing uniformly, perform three-level high-speed shearing through the shearing machine;
[0051] 2). Pump into the blending tank, add 12 parts by mass of blended asphalt and mix evenly;
[0052] 3). Add 0.1 parts by mass of heat stabilizer, stir for 20-40 minutes, and then further grind through colloid mill after uniformity to obtain high-quality road petroleum asphalt.
[0053] The main bitumen used refers to the vacuum residue of the residual oil and heavy crude oil after deep drawing under vacuum. The content of its four components is: asphaltene 30%. Aromatic content> 15%. The blended asphal...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap