Hot melt polyester-polyamide, preparation method and application thereof
A polyester polyamide, hot-melt technology, applied in the field of composite material compatibilizers, can solve the problems of no separation method, environmental pollution, low recovery rate, etc., to promote sustainable development of resources and ecological environment, durable The effect of excellent performance and cost reduction of raw materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0050] Example 1
[0051] The recycled PET is crushed and air-dried to reduce the moisture to below 1.0%, and solids such as sand, stones, and metals are screened out; the nylon acid is crushed and air-dried to reduce the moisture to below 1.0%, and the sand, Solids such as stones and metals; add 400g of recycled PET and 150g of diethylene glycol amine to the flask, and use 500W microwave radiation for 40min to aminate the PET; add 170g of nylon acid to the flask, and use 500W microwave radiation for esterification; Add 1.3g of polycondensation catalyst monobutyl tin oxide and 1.3g of heat stabilizer trimethyl phosphate into the flask, and heat to a temperature of 220~240℃ to anhydrous distillation. At a temperature of 220~240℃, the vacuum degree is 300mHg Distill under reduced pressure for 0.5h, and then distill under reduced pressure under a vacuum of 90mmHg until the acid value is reduced to 1.7mgKOH / g. The melt material is pressed into a water tank in granular form while it i...
Example Embodiment
[0053] Example 2
[0054] The recycled PET is crushed and air-dried to reduce the moisture to below 1.0%, and solids such as sand, stones, and metals are screened out; the nylon acid is crushed and air-dried to reduce the moisture to below 1.0%, and the sand, Solids such as stones and metals; add 400g of recycled PET and 250g of diethylene glycol amine to the flask, and use 700W microwave radiation for 6min to aminate the PET; add 270g of nylon acid to the flask and use 700W microwave radiation for esterification reaction; Add polycondensation catalyst monobutyl tin oxide and antimony trioxide at a mass ratio of 1:1 blend 2.4g, heat stabilizer trimethyl phosphate and 2,6-di-tert-butyl-4-methylphenol 1.5g of the blend with a mass ratio of 1:1, heated to a temperature of 220~240℃ to anhydrous distillation, at a temperature of 220~240℃, vacuum degree of 350mHg vacuum distillation for 1h, and then vacuum degree Distill under reduced pressure at 100mmHg until the acid value drops to ...
Example Embodiment
[0056] Example 3
[0057] The recycled PET is crushed and air-dried to reduce the moisture to below 1.0%, and solids such as sand, stones, and metals are screened out; the nylon acid is crushed and air-dried to reduce the moisture to below 1.0%, and the sand, Solids such as stones and metals; add 400g of recycled PET and 200g of diethylene glycol amine to the flask, and use 600W microwave radiation for 30min to aminate the PET; add 220g of nylon acid to the flask, and use 600W microwave radiation for esterification reaction; Add 2.0 g of a blend of polycondensation catalyst antimony trioxide and tetrabutyl titanate in a mass ratio of 1:1, and heat stabilizer triphenyl phosphite 1.7 g. Heat to a temperature of 220-240°C to distill out without water , At a temperature of 220~240℃, vacuum degree of vacuum is 332mHg vacuum distillation 0.8h, then vacuum degree is 75mmHg vacuum distillation until the acid value drops to 2.1mgKOH / g, the melt material is pressed into granular form while...
PUM
Property | Measurement | Unit |
---|---|---|
Softening point | aaaaa | aaaaa |
Acid value | aaaaa | aaaaa |
Softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap