Flame-retardant sound insulation composite material and sound insulation component

A composite material and sound insulation technology, applied in the direction of sounding equipment, instruments, etc., can solve problems such as rising cost, and achieve the effects of low cost, good constructability and high strength

Active Publication Date: 2011-07-20
深圳洛赛声学技术有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem solved by the present invention is: to provide a flame-retardant and sound-insulating composite material, which overcomes the technical problem that the sound-insulating material contains tungsten powder material in the prior art, which leads to a substantial increase in cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The components are uniformly mixed in the following proportions, kneaded on an open mill, and molded into a soft sheet of 2 mm. PVC (polymerization degree 1300): 25.5%, iron powder with a particle size of 38 microns: 51.1%, γ-(2,3-epoxypropoxy)propyltrimethoxysilane: 0.5%, stearic acid: 0.1% , calcium zinc composite stabilizer: 1%, dioctyl phthalate: 5.1%, triphenyl phosphite: 12.8%, zinc borate: 1.5%, molybdenum trioxide: 1.3%, antimony trioxide: 1.5% .

Embodiment 2

[0024] Mix the components uniformly in the following proportions, knead them on an open mill, and mold them into soft sheets of 2 mm; PVC (polymerization degree: 1300): 13.4%, chlorinated polyethylene (chlorine content: 40%): 13.4%, iron powder with a particle size of 38 microns: 53.4%, γ-(2,3-epoxypropoxy)propyltrimethoxysilane: 0.5%, stearic acid: 0.1%, calcium-zinc composite stabilizer: 1.1%, triphenyl phosphite: 13.4%, zinc borate: 1.6%, molybdenum trioxide: 1.3%, antimony trioxide: 1.6%.

[0025] Table 1 is the contrast result of comparative example and embodiment one and embodiment two:

[0026] Table 1

[0027] Performance

[0028] The present invention also provides a sound-insulating component, which is made of the above-mentioned flame-retardant and sound-insulating composite material. In the invention, the kneaded flame-retardant and sound-insulating composite material is made into a thin plate, and then the plate is used to make a sound-insulating compo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a flame-retardant sound insulation composite material. The flame-retardant sound insulation composite material comprises the following components in percentage by weight: 5 to 30 percent of PVC, 5 to 30 percent of chlorinated polyethylene, 15 to 80 percent of iron powder of which the grain diameter is 10 to 100 microns, 0.5 to 2 percent of coupling agent and 9.5 to 23 percent of aid. The invention provides the flame-retardant sound insulation composite material, which is prepared from the PVC, the chlorinated polyethylene, the iron powder with the grain diameter of 10to 100 microns, the coupling agent and the aid, has good flame-retardant sound insulation effect, and also has the characteristics of flame retardancy, innocuity, no lead, high strength, good construction property and low cost. Because the chlorinated polyethylene is particularly introduced into the material components of the flame-retardant sound insulation composite material, the using amount of a plasticizer of the material is reduced, and the composite material has better softness and can be widely applied to sound insulation treatment in the construction industry, decoration field and the like; and the sound insulation composite material can effectively reduce the noise, and the sound insulation index of the material can reach 25 to 32 decibels.

Description

technical field [0001] The invention relates to a composite material and a sound-insulating component, in particular to a flame-retardant and sound-insulating composite material and a sound-insulating component using the flame-retardant and sound-insulating composite material. Background technique [0002] With the development of social industrialization, the problem of noise pollution, one of the three major pollutions, is becoming more and more prominent. Noise can harm people's auditory system. If people are in a noisy environment for a long time, it will make people tired, deaf, and even endanger their lives. At the same time, noise will also accelerate the aging and damage of buildings and machine structures, and affect the accuracy and lifespan of equipment and instruments. Therefore, the prevention and control of noise has become one of the important issues to be solved urgently. [0003] The prevention and control of noise should take into account the acoustic syst...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G10K11/162C08L27/06C08L23/28C08K3/08C08K13/02
Inventor 万朝瑛刘韬吴文敬张勇
Owner 深圳洛赛声学技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com