Method for preparing high-temperature alloy GH4648 prills by adopting plasma auxiliary rotary electrode

A high-temperature alloy and auxiliary rotation technology, which is applied in the field of metal material preparation, can solve the problems such as the inability to meet the requirements of the laser three-dimensional forming process and the small ball diameter, and achieve the effect of smooth and clean surface of powder particles, small ball diameter and good sphericity

Inactive Publication Date: 2010-07-07
张建利
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the high-temperature alloy GH4648 metal pellets prepared by the existing foreign atomization method, which cannot meet the requirements of the laser three-dimensional forming process. The high-temperature alloy GH4648 metal ball can meet the needs of the National Institute of Aerospace Special Materials and Technology, the State Key Laboratory of Solidification Technology, and the laser three-dimensional forming process designed for special parts required in the fields of aviation and aerospace. Good, good monodispersity superalloy GH4648 metal pellet material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high-temperature alloy GH4648 prills by adopting plasma auxiliary rotary electrode
  • Method for preparing high-temperature alloy GH4648 prills by adopting plasma auxiliary rotary electrode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The method for preparing superalloy GH4648 metal pellets by using plasma-assisted rotating electrodes is implemented according to the following steps:

[0018] (1) Preparation of anode electrode rods: Refining the high-temperature alloy GH4648 metal into standard rods, and then finishing it into a plasma gun rotating electrode that can run at a high speed of 9000-12000 revolutions per second to prepare spherical powder The motor rod that runs smoothly in the dynamic seal of the equipment; the preparation process of the electrode rod is: a. According to the chemical composition of the actual material requirements, the superalloy GH4648 metal is mixed to obtain the melting and casting raw material; b. The qualified melting and casting raw material is vacuum smelted , to obtain an ingot-shaped billet with a relative density of more than 85%; c, hot forging the vacuum-melted ingot-shaped billet to obtain a superalloy GH4648 metal rod with a relative density greater than 98%;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing high-temperature alloy GH4648 metal spherical powder by adopting a plasma auxiliary rotary electrode centrifuging process. The method comprises the following steps of: generating a glow discharge plasma arc between a plasma auxiliary electrode and a consumption-type electrode made of rotary cylindrical high-temperature alloy GH4648 metal in a closed container protected by inert gas; forming droplets at one section of the high-temperature alloy GH4648 metal electrode close to the plasma arc by high temperature which is generated by the plasma arc; flinging the droplets out by centrifugal force; cooling the high-temperature alloy GH4648 metal droplets in air and solidifying into spheres in the inert atmosphere environment of the closed container; and collecting the high-temperature alloy GH4648 prills. The method changes process parameters so that high-temperature alloy GH4648 prills with an average sphere diameter from 0.05-1.2 mm and better monodispersity are obtained, have favorable degree of sphericity, lower malformed particle proportion and controllable sphere diameters and can be used in the field of a laser three-dimensional forming process for preparing special parts of an aerospace craft.

Description

technical field [0001] The invention relates to the technical field of metal material preparation, in particular to a method for preparing high-temperature alloy GH4648 metal pellets by using a plasma-assisted rotating electrode centrifugal process, and the prepared superalloy GH4648 metal pellets can be used for laser stereoforming and plasma coating processes . Structural materials used in the aerospace field. Background technique [0002] National Institute of Aerospace Special Materials and Technology, State Key Laboratory of Solidification Technology, laser three-dimensional molding process designed for special parts required in the fields of aviation and aerospace, requires a high temperature with small diameter, good sphericity, and good monodispersity Alloy GH4648 metal pellets are used as a functional special material. [0003] It is understood that there is no production of this kind of product in China at present, and there is a gas atomization process in foreig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/10
Inventor 张建利
Owner 张建利
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com