A functional material for preparing multifunctional healthy running water and its manufacturing method

A technology of a functional material and a manufacturing method, which is applied to the functional material for preparing multifunctional healthy living water and the manufacturing field thereof, can solve the problems of unreasonable application devices and the like, and achieve the effect of no peculiar smell and good taste.

Inactive Publication Date: 2012-02-01
上海豪斯整水器有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If it is easy to agglomerate, the application device is not reasonable enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A functional material for preparing multifunctional healthy running water and its manufacturing method
  • A functional material for preparing multifunctional healthy running water and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] (1) Component A. Black tablet formula:

[0053] Material Name Tourmaline Iron Powder Iron Tetroxide Magnesium Powder Copper Powder Zinc Powder Manganese Powder

[0054] Proportion (wt%) 60 8.0 8.0 9.0 7.0 6.0 2.0

[0055] Material particle size (μm) 0.5 30 30 30 30 30 30

[0056] (2). Component B white tablets formula:

[0057] Material name Medical stone Muyu stone Sake jade Sepiolite Biotite Slag Calcium sulfite Clay

[0058] Proportion (wt%) 20.0 15.0 20.0 15.0 7.0 2.0 1.0 20

[0059] Material particle size (μm) 30 30 30 30 30 30 30 30

[0060] In this example, black flakes and white flakes are used in combination (wt%) 75:25. They can be placed in the filter element respectively, the white piece is placed in the upper cavity, and the black piece is placed in the lower cavity. Then put the filter element in a water machine or a water cup to make purified, activated and mineralized functional water. Purification, activation and mineralization functional water t...

Embodiment 2

[0063] (1) Component A black tablet formula:

[0064] Material Name Tourmaline Iron Powder Tetroxide Magnesium Powder Copper Powder Zinc Powder Manganese Powder

[0065] Proportion (wt%) 52.0 8.0 8.0 8.0 8.0 9.0 7.0

[0066] Material particle size (μm) 0.5 30 30 30 30 30 30

[0067] (2). Component B white tablets formula:

[0068] Material name: medical stone, wood fish stone, wine jade, sepiolite, biotite, volcanic slag, calcium sulfite, clay

[0069] Proportion (wt%) 19.0 20.0 16.0 18.0 3.0 1.5 1.5 21.0

[0070] Material particle size (μm) 30 30 30 30 30 30 30 30

[0071] In this example, the black flakes and the white flakes are used in combination at a ratio of (wt%) 70:30, and other devices and application processes are the same as in Example 1. Purified, activated and mineralized functional water can also be obtained.

Embodiment 3

[0073] (1). Component A black tablet formula:

[0074] Material Name Tourmaline Iron Powder Iron Tetroxide Magnesium Powder Copper Powder Zinc Powder Manganese Powder

[0075] Proportion (wt%) 55.0 7.0 9.0 7.0 6.0 8.0 8.0

[0076] Material particle size (μm) 0.5 30 30 30 30 30 30

[0077] (2). Component B white tablets formula:

[0078] Material name: medical stone, wood fish stone, wine jade, sepiolite, biotite, volcanic slag, calcium sulfite, clay

[0079] Proportion (wt%) 19.5 20.0 15.0 16.0 4.0 3.0 0.5 22.0

[0080] Material particle size (μm) 30 30 30 30 30 30 30 30

[0081] In this example, black flakes and white flakes are used in combination in a ratio of (wt%) 72:28. Other devices and application processes are the same as in Example 1, but purified, activated and mineralized functional water can also be obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a functional material for preparing multifunctional healthy running water and a manufacturing method thereof. Composed of component A and component B, component A is composed of tourmaline, ferric oxide, zinc, copper, magnesium, iron, manganese powder and adhesive auxiliary materials, and is made by low-temperature tableting by special equipment ; Component B is a complex ion element, which is composed of medical stone, wood fish stone, fine wine jade, sepiolite, biotite, volcanic slag, calcium sulfite and clay, and is formed by sintering at high temperature; the preparation of component A : The materials are weighed in proportion, after mixing, heating, cooling, and ball milling to pulverize into micron-sized powders; adding binder to the mixed powder after ball milling and mixing; forming flakes with a punching machine; the prepared black The slices are sent to the heating furnace again to maintain a constant temperature; after cooling, they are packaged for later use. Preparation of component B: Weigh the materials according to the proportion and mix them one by one evenly, add the binder and mix them into agglomerates; inject the agglomerates into the tablet press machine to make sheets, and sinter them in a special sintering furnace after drying. Get the desired product. The water quality after being treated by the multi-functional healthy living water material prepared by the present invention has no toxic and harmful substances to the human body, and has no peculiar smell and good taste; the water body has moderate hardness and contains minerals and trace elements needed by the human body; the water body is weakly alkaline Nature, small molecular group water, the oxidation-reduction potential of water is reduced to a negative value at -200 ~ -550MV, and the nutritional and physiological functions of the water body are strong.

Description

technical field [0001] The invention relates to a functional material for preparing multifunctional healthy running water and a manufacturing method thereof. Background technique [0002] Water is the source of life and one of the three elements of human life activities. And health is the eternal theme pursued by human beings. Seeking a good healthy living water is an urgent pursuit. Over the years, domestic and foreign water experts have carried out a number of research experiments for this purpose, and achieved some outstanding results. Experts pointed out: "Water quality determines physical fitness, physical fitness determines health, and good water is the foundation of health." We must drink good water to drink health! [0003] What is good water? Experts at home and abroad agree that good water means that the water that people drink should be clean, safe, healthy and functional. It must meet the following conditions: it does not contain toxic and harmful substances...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C02F1/66C02F1/68
Inventor 姚鼎山陈效庄张丽
Owner 上海豪斯整水器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com