Green attapulgite polymer clay powder

Abstract

The invention discloses a green attapulgite polymer clay powder, which is prepared by using purified attapulgite clay, white bentonite, sepiolite, ferric oxide green, organic pigment green, calcium chloride, titanium dioxide anatase, sodium polyacrylate, sodium carboxymethylcellulose and sodium stearoyl lactate as raw materials through the steps of mixing the raw materials above; conveying the obtained mixture into a crusher to crush; then conveying the crushed mixture into a pulverizing mill to pulverize; and packaging the obtained product so as to obtain the finished product of the green attapulgite polymer clay powder. Green attapulgite polymer clay mud prepared by adding water and methyl silicone oil into the green attapulgite polymer clay powder has the advantages of high viscosity, good soft plasticity, low shrinkage rate, no baking in the process of hardening after air drying, no cracking, no corrosivity, and no greasy feeling. The invention is simple in production process, low in cost, easy to use, and beneficial for popularization; and the green attapulgite polymer clay powder is suitable for the field preparation of green attapulgite polymer clay mud.

Description

technical field [0001] The invention relates to pottery clay, in particular to a green attapulgite soft pottery powder. Background technique [0002] The soft clay supplied on the market is a lumpy soft clay after batching processing. The main raw materials of soft clay are polyvinyl chloride and calcium carbonate. It is easy to foam when making soft clay. If the temperature exceeds 200°C, it will not only burn and melt the finished product, but may even cause combustion, generating irritating and toxic fumes containing chlorine. The sales price of soft clay is high, which is not conducive to Promotional use. [0003] The Chinese patent publication number is: CN 101186736, open date: May 28, 2008, titled "a kind of soft clay and its preparation method", discloses: "a kind of soft clay and its preparation method, which consists of the following weight It is prepared from 15 parts: polyvinyl chloride paste resin 15-40, dizinc grease 20-55, calcium carbonate 15-35, plasticize...

AI Technical Summary

Problems solved by technology

[0004] The disadvantage of the above-mentioned patents is that the main raw materials of the soft clay produced by this technology are polyvinyl chloride paste resin, dizinc grease and calcium carbonate, and the adhesion is not good under normal temperature, which is not conducive to making molding. Dizinc grease belongs to poisonous substance

[0006] The disadvantage of the above-mentioned patent is that the main raw materials of the transparent texture resin clay produced by this technology are powdery ethylene-vinyl acetate copolymer and starch, and the powdery ethylene-vinyl acetate copolymer is irritating to the eyes and skin, so it is not suitable for It is used to produce raw materials for making handicrafts. This product requires a large amount of starch, which is not conducive to popularization and use.