Method for producing insoluble sulfur by using liquid phase method

A liquid phase method, sulfur technology, applied in the preparation/purification of sulfur, etc., can solve the problems of poor thermal stability and dispersibility, high production cost, flammability and explosion, etc., to improve melting point and dispersibility, and ensure high thermal stability Sex, avoid flammable and explosive effects

Active Publication Date: 2011-04-20
朝阳明宇化工有限公司
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method has a high conversion rate of insoluble sulfur, but the reaction temperature is high, the consumption of raw materials is large, and the cost is high; it is flammable and explosive, the operation under pressure is dangerous, and the dust in the crushing process is high; and the thermal stability and dispersibility of the product All are poor; American Flex Company adopts the vaporization one-step method, which has high polymerization conversion rate, low sulfur consumption rate, high insoluble sulfur content, thermal stability and dispersibility in the product, but the melting temperature in the production process is as high as 550 ~600℃, high risk; moreover, the process is complex, the efficiency is low, and the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing insoluble sulfur by using liquid phase method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] 1) Melting aging: Add industrial sulfur with a purity ≥ 99.9% to a melting kettle with a capacity of 8T and melt it. When the temperature in the kettle reaches 340-350°C, keep it at a constant temperature for 30 minutes, and then spray FeCL3+HNO3+H20 quenching liquid Carry out quenching treatment, the weight percent of FeCL3 and HNO3 in quenching liquid is 2% and 0.4% respectively, then dry at 70~75 ℃ for 8~9 hours, obtain insoluble sulfur weight percentage content up to 40%, soluble sulfur weight content 60 items up to 60%;

[0019] 2) Extraction: extract 60 aged strips in an extraction tank with pure CS2 solvent for 3 times, each time for 50 minutes, so that the insoluble sulfur weight percentage after extraction is ≥ 95%, and the insoluble sulfur content reaches more than 90%. 90 bars with a soluble sulfur content of about 10%, the used CS2 solvent can be reused by distillation;

[0020] 3) Stabilization treatment: 0.75 kilograms of KCL, 1.225 kilograms of KCLO3 and...

Embodiment 2

[0025] 1) Melting aging: Add industrial sulfur with a purity ≥ 99.9% to a melting kettle with a capacity of 8T and melt it. When the temperature in the kettle reaches 340-350°C, keep it at a constant temperature for 30 minutes, and then spray FeCL3+HNO3+H20 quenching liquid Carry out quenching treatment, the weight percent of FeCL3 and HNO3 in quenching liquid is 2% and 0.4% respectively, then dry at 70~75 ℃ for 8~9 hours, obtain insoluble sulfur weight percentage content up to 40%, soluble sulfur weight content 60 items up to 60%;

[0026] 2) Extraction: extract 60 aged strips in an extraction tank with pure CS2 solvent for 3 times, each time for 40 minutes, so that the weight percentage of insoluble sulfur after extraction is ≥95%, and the insoluble sulfur content reaches more than 90%. 90 bars with a soluble sulfur content of about 10%, the used CS2 solvent can be reused by distillation;

[0027] 3) Stabilization treatment: 0.75 kilograms of KCL, 1.225 kilograms of KCLO3 a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for producing insoluble sulfur by using a liquid phase method, which comprises the following steps of: adding sulfur into a melting kettle, keeping for 30-40 min at a temperature of 340-350 DEG C, then spraying FeCl3, HNO3 and H2O quenching liquid for quenching; extracting aged 60 strip with a CS2 solvent for 3-4 times to ensure that the content of insoluble sulphur is not less than 95 percent, wherein the aged 60 strip is extracted for 40-50min each time; stabilizing an extractant for 20-40min by using a composite stabilizing agent prepared from KCl, KClO3 and acid water solution; drying for 30-40 min at a temperature of 70-80 DEG C to ensure that the water content is controlled below 0.5 percent; charging oil for absorbing by respectively using naphthenic oil and liquid rubber after drying; and crushing oil charged adsorbate to 100-180mu to obtain the insoluble sulfur. The insoluble sulfur prepared by using the method of the invention has the characteristics of high thermal stability, high content of insoluble sulphur, high dispersibility and high thinness. The method has the advantages of simple operation, high efficiency, low cost and high safety, and is suitable for industrialized production.

Description

technical field [0001] The invention relates to a method for preparing sulfur, in particular to a method for producing insoluble sulfur by a liquid phase method with high temperature stability. Background technique [0002] Insoluble sulfur (insoluble means insoluble in carbon disulfide, referred to as IS) is a macromolecule polymerized by hundreds of thousands or even millions of sulfur atoms. It belongs to inorganic polymers. It is a rubber vulcanizing agent with excellent performance. The surface of the finished product or semi-finished product does not spray frost and increases the adhesion, which is conducive to improving the operating environment. At the same time, it is also a good rubber vulcanization accelerator, which can accelerate the vulcanization speed and make the vulcanization even. At present, insoluble sulfur has been widely used in tire carcass rubber, buffer rubber, white sidewall rubber and the bonding rubber of skeleton materials, which can improve the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B17/12
Inventor 时宝成吴丽红
Owner 朝阳明宇化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com