Method for preparing high-purity magnesium oxide by pyrolysis of magnesium chloride

A technology of magnesium oxide and magnesium chloride, applied in magnesium oxide and other directions, can solve the problems of high energy consumption of pyrolysis, complicated control of pyrolysis process, etc., and achieve the effects of short decomposition time, simple process, and increased concentration and temperature.

Inactive Publication Date: 2011-04-27
QINGHAI INST OF SALT LAKES OF CHINESE ACAD OF SCI
View PDF2 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0030] The method is simple in process, does not require other raw materials in the production process, and has high product quali

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0047] Embodiment 1 A method for preparing high-purity magnesium oxide by pyrolysis of magnesium chloride includes the following steps:

[0048] (1) After dissolving the salt lake bischofite with water, use barium chloride and a special resin for boron adsorption to remove B respectively 2 O 3 And SO 2- 4 , To obtain a magnesium chloride solution with a mass concentration of 29-32%; wherein each kg of bischofite consumes 15-20g of barium chloride.

[0049] (2) The magnesium chloride solution obtained in step (1) is concentrated in the pre-concentration container to a mass concentration of 38-41% and the solution temperature is 80-90°C, and then sprayed into the pyrolysis reaction through a pressure nozzle at a flow rate of 55L / h In the vessel, under the action of the nozzle pressure of 0.3MPa, contact with the gas at the temperature of 1200~1500℃; decompose under the conditions of decomposition temperature of 500℃, pressure of -60Pa, and decomposition time of 1~5s to obtain pyrolysi...

Example Embodiment

[0053] Embodiment 2 A method for preparing high-purity magnesium oxide by pyrolysis of magnesium chloride includes the following steps:

[0054] (1) After dissolving the old brine in water, use barium chloride and boron adsorption resin to remove B respectively 2 O 3 And SO 2- 4 , To obtain a magnesium chloride solution with a mass concentration of 29-32%; of which 15-20g barium chloride is consumed per kg of old brine.

[0055] (2) The magnesium chloride solution obtained in step (1) is concentrated in the pre-concentration container to a mass concentration of 38-41% and the solution temperature is 80-90°C, and then sprayed into the pyrolysis reaction through a centrifugal nozzle at a flow rate of 55L / h In the vessel, under the action of the nozzle pressure of 0.5MPa, it is in contact with the gas at the temperature of 1200~1500℃; the decomposition temperature is 500℃, the pressure is -80Pa, and the decomposition time is 1~5s. The product magnesium oxide and the main components wi...

Example Embodiment

[0059] Example 3 A method for preparing high-purity magnesium oxide by pyrolysis of magnesium chloride includes the following steps:

[0060] (1) After dissolving the salt lake bischofite with water, use barium chloride and a special resin for boron adsorption to remove B respectively 2 O 3 And SO 2- 4 , To obtain a magnesium chloride solution with a mass concentration of 29-32%; wherein each kg of bischofite consumes 15-20g of barium chloride.

[0061] (2) The magnesium chloride solution obtained in step (1) is concentrated in a pre-concentration container to a mass concentration of 38-41% and the solution temperature is 80-90°C, and then sprayed into the pyrolysis reaction through a pressure nozzle at a flow rate of 61L / h In the vessel, under the action of the nozzle pressure of 0.5MPa, contact with the gas at the temperature of 1200~1500℃; the decomposition temperature is 550℃, the pressure is -35Pa, and the decomposition time is 1~5s. The product magnesium oxide and the main co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing high-purity magnesium oxide by pyrolysis of magnesium chloride. The method comprises the following steps of: (1) dissolving salt lake bischofite or old brine, and then removing B2O3 and SO2<-4>, so as to obtain a magnesium chloride solution with the mass concentration of 29-32%; (2) preconcentrating the magnesium chloride solution, spraying the preconcentrated magnesium chloride solution into a pyrolysis reactor by virtue of a nozzle, decomposing under the conditions that the decomposition temperature is 500-650 DEG C, the pressure is -80 to -20Pa and the decomposition time is 1-5 seconds to obtain themolysis products of magnesium oxide and themolysis tail gas; and (3) sintering the pyrolysis product magnesium oxide sequentially subjected to hydration purifying, washing and filtering to obtain high-purity magnesium oxide with the MgO content of more than 99.0%. The invention has the advantages of simple process, low cost, high raw material decomposition rate, short decomposition time, high thermal efficiency and high thermal utilization ratio.

Description

technical field [0001] The invention relates to a method for preparing high-purity magnesium oxide in the technical field of inorganic chemical industry, in particular to a method for preparing high-purity magnesium oxide by pyrolyzing magnesium chloride using salt lake bischofite (brine) as raw material. Background technique [0002] Magnesium oxide is mainly used as a raw material for the preparation of ceramics, enamel, refractory crucibles and refractory bricks, and is also used as a filler for polishing agents, adhesives, coatings and paper, as an accelerator and activator for neoprene and fluorine rubber; and After mixing magnesium chloride and other solutions, it can be made into magnesium oxide water. In medicine, it is used as an antacid and laxative, for gastric and duodenal ulcer disease with hyperacidity; in the chemical industry, it is used as a catalyst and a raw material for the manufacture of magnesium salts. [0003] MgO≥99.0% is called high-purity magnesia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01F5/06
Inventor 火焱都永生韩继龙王世栋李明珍孙庆国周园
Owner QINGHAI INST OF SALT LAKES OF CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap