Cobalt salt adhesive for bonding nitrile rubber and copper/zinc frame and preparation method thereof

An adhesive and nitrile rubber technology, applied in the direction of adhesive additives, aldehyde/ketone condensation polymer adhesives, adhesives, etc. Convenience, obvious use effect, good dynamic mechanical properties

Inactive Publication Date: 2011-04-27
镇江泛华新材料科技发展有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in order to reduce the cost of rubber products, many rubber product manufacturers use a large amount of reclaimed rubber or reclaimed rubber powder in the formula of rubber products. Although the reclaimed rubber has been desulfurized, the rubber molecular chain is not completely linear. The powder is vulcanized mature rubber, which is almost completely reticulated, which makes the adhesive ability of the coated modified cobalt salt adhesive mainly chemically bonded and rubber as the carrier drop sharply, and cannot adapt to this type of rubber. The needs of product manufacturers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cobalt salt adhesive for bonding nitrile rubber and copper/zinc frame and preparation method thereof
  • Cobalt salt adhesive for bonding nitrile rubber and copper/zinc frame and preparation method thereof
  • Cobalt salt adhesive for bonding nitrile rubber and copper/zinc frame and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] Below in conjunction with specific embodiment, further illustrate the present invention, should be understood that these embodiments are only used to illustrate the present invention and are not intended to limit the scope of the present invention, after having read the present invention, those skilled in the art will understand various equivalent forms of the present invention All modifications fall within the scope defined by the appended claims of the present application.

[0020] A cobalt salt adhesive for bonding nitrile rubber with copper and zinc skeletons, including a composite adhesive, phenolic resin and auxiliary agents, the composite adhesive is composed of a main adhesive and a co-adhesive, wherein the main adhesive includes cobalt boroacylate and cobalt neodecanoate, the adhesion promoter is a compound organic salt containing nickel and vanadium, the phenolic resin includes a methyl donor and a methyl acceptor, and the auxiliary agent includes a toughening ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cobalt salt adhesive for bonding nitrile rubber and a copper / zinc frame and a preparation method thereof. The adhesive comprises a compound adhesive, phenolic resin and assistants, wherein the compound adhesive comprises a main adhesive and an auxiliary adhesive, wherein the main adhesive comprises cobalt borate and cobalt neodecanoate; the auxiliary adhesive is compound organic salt containing nickel and vanadium; the phenolic resin comprises a methylene donor and a methylene acceptor; and the assistants comprise toughening agents, activating agents, vulcanization activators, silane coupling agents and vulcanizing agents. The preparation method comprises the following steps: dispersing the compound adhesive in the carrier phenolic resin, and dissolving by a mixed solvent under the actions of the assistants to obtain adhesive cement, thereby obtaining the cobalt salt adhesive for bonding the nitrile rubber and the copper / zinc frame. The cobalt salt adhesive provided by the invention has the advantages of high thermal stability, favorable dynamic mechanical properties and low cost, can be directly coated, and is suitable for high-strength bonding of mixed rubberof nitrile rubber and regenerated rubber or regenerated rubber powder and a copper / zinc / copper alloy / zinc alloy / zinc plated / brass-plated frame.

Description

technical field [0001] The invention relates to an adhesive and a preparation method thereof, in particular to a nitrile rubber used for bonding the mixed rubber of nitrile rubber and reclaimed rubber or reclaimed rubber powder to copper, zinc, copper alloy, zinc alloy, galvanized, or brass-plated skeleton A cobalt salt adhesive for bonding with copper and zinc skeletons and a preparation method thereof. Background technique [0002] In the continuous production of large-scale rubber products such as steel radial tires, steel wire reinforced conveyor belts, and steel wire braided rubber hoses, the high-strength bonding of elastomers such as rubber and galvanized or brass-plated steel wire cord braided skeleton materials is usually bonded directly. Addition-type cobalt salt binders, direct-addition cobalt salt binders include cobalt stearate, solid cobalt naphthenate, cobalt neodecanoate, cobalt boroacylate, etc. These cobalt salt binders, especially cobalt boroacylate, have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J161/32C09J11/06
Inventor 吴明生严忠庆陈秀娟
Owner 镇江泛华新材料科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products