High-performance impact-resistance steel structure paint

A steel structure coating and anti-impact technology, applied in the direction of epoxy resin coating, coating, etc., can solve the problems of increasing the cost, affecting the progress of construction, wasting manpower and material resources, etc., and achieving the reduction of coating damage rate and environmental protection. Less impact and improved construction efficiency

Active Publication Date: 2014-03-12
SHANGHAI HILONG SHINE NEW MATERIAL
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the transportation process, the steel structure coated with the existing steel structure paint will be subjected to different degrees of collision and damage because it has to go through hoisting, truck transportation, or shipping, sea transportation, etc. Most of the coated steel structures need to be repainted or recoated after arriving at the destination, which not only wastes a lot of manpower and material resources, increases the cost, but also affects the progress of construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance impact-resistance steel structure paint
  • High-performance impact-resistance steel structure paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Embodiment 1 Preparation of high-performance impact-resistant steel structure coating

[0057] (1) Raw material ratio

[0058] Containing component A and component B, the mass percentage of the raw materials of the two components is:

[0059] Component A:

[0060] Epoxy resin 28.00%, using products from Hongchang Electronic Materials Co., Ltd. or Sinopec Yuehua Company;

[0061] Epoxy resin 1 8.00%, adopts the product of Shenzhen Jiadida Chemical Co., Ltd.;

[0062] Toughening resin 7.50%, provided by Hilong Petroleum Industry Group;

[0063] Thinner 22.65%, using commercially available conventional materials;

[0064] Dispersant 0.25%, using the product of Shuangrun Chemical Company;

[0065] Defoamer 0.34%, using the product of Shuangrun Chemical Company;

[0066]Leveling agent 0.58%, using the product of Shuangrun Chemical Company;

[0067] Fumed silica 0.80%, using commercially available conventional materials;

[0068] Potassium titanate whiskers 2.00%, pro...

Embodiment 2

[0087] Embodiment 2 Preparation of high-performance impact-resistant steel structure coating

[0088] (1) Raw material ratio:

[0089] Containing component A and component B, the mass percentage of the raw materials of the two components is:

[0090] Component A:

[0091] Epoxy resin 30.00%;

[0092] Epoxy resin 1 6.00%;

[0093] Toughening resin 6.00%;

[0094] Thinner 21.20%;

[0095] Dispersant 0.22%;

[0096] Defoamer 0.30%;

[0097] Leveling agent 0.52%;

[0098] Fumed silica 0.90%;

[0099] Potassium titanate whiskers 2.30%;

[0100] Montmorillonite 3.00%;

[0101] Titanium dioxide 13.00%;

[0102] Talc 6.53%;

[0103] Carbon black 0.03%;

[0104] Component B:

[0105] Phenolic modified epoxy resin curing agent 10.00%;

[0106] (the source of above raw material is with embodiment 1)

[0107] When the paint is used, the A component and the B component are used in combination according to the mass ratio A:B=9.00:1.

[0108] Stir component A and component B...

Embodiment 3

[0110] Embodiment 3 Preparation of high-performance impact-resistant steel structure coating

[0111] (1) Raw material ratio:

[0112] Containing component A and component B, the mass percentage of the raw materials of the two components is:

[0113] Component A:

[0114] Epoxy resin 25.00%;

[0115] Epoxy resin 1 9.00%;

[0116] Toughening resin 9.00%;

[0117] Thinner 20.00%;

[0118] Dispersant 0.20%;

[0119] Defoamer 0.20%;

[0120] Leveling agent 0.50%;

[0121] Fumed silica 0.60%;

[0122] Potassium titanate whiskers 2.00%;

[0123] Montmorillonite 1.00%;

[0124] Titanium dioxide 14.00%;

[0125] Talc 8.73%;

[0126] Carbon black 0.05%;

[0127] Component B:

[0128] Phenolic modified epoxy resin curing agent: 9.72%;

[0129] (the source of above raw material is with embodiment 1)

[0130] When the paint is used, the A component and the B component are used together according to the mass ratio A:B=9.29:1.

[0131] Stir component A and component B evenl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of coating technology in chemical technology, in particular to high-performance impact-resistance steel structure paint, which comprises a component A and a component B, wherein the component A and the component B are used in combination according to the mass ratio of the component A to the component B of (3-5):1. In the invention, dimer acid addition modified toughened epoxy resin is added with potassium hexatitanate whisker with a tunnel-like structure and phenolic aldehyde modified amine is used as a curing agent, so the paint has high mechanical performance, chemical performance and high impact resistance; besides high anticorrosion performance, the 200-micrometer-thick coating on carbon steel plate can resist 200kg.cm impact; a coating process is safe and exerts fewer influences on the environment; and the damage rate of coated steel pipes in a transport process is greatly reduced, supplementary coating or recoating times are reduced, labor and materials are saved, cost is lowered and construction efficiency is improved.

Description

technical field [0001] The invention relates to the technical field of coatings in chemical technology, in particular to the development of high-performance impact-resistant steel structure coatings. Background technique [0002] Steel structure coating is one of many coatings. It is suitable for corrosion protection of sewage, seawater, industrial water, oil, gas and other pipelines, as well as bridges, electric equipment, grids and various chemical equipment. It has a wide range of applications prospect. However, during the transportation process, the steel structure coated with the existing steel structure paint will be subjected to different degrees of collision and damage because it has to go through hoisting, truck transportation, or shipping, sea transportation, etc. Most of the coated steel structures need to be repainted or recoated after arriving at the destination, which not only wastes a lot of manpower and material resources, increases the cost, but also affect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D163/02C09D7/12
Inventor 张鹏珍丁武斌方军锋李明
Owner SHANGHAI HILONG SHINE NEW MATERIAL
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog