Water swellable waterproof membrane and preparation method thereof
A water-swelling, waterproof membrane technology, applied in the direction of chemical instruments and methods, synthetic resin layered products, lamination devices, etc., can solve the problems of easy loss, difficult transportation, easy puncture of waterproof materials, etc., and achieve simple construction Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0031] The first step is to prepare the reinforced lining
[0032] First prepare a coating made of polyurea, and spray the coating evenly on the interlining cloth with a specification of 60 g / m2 woven from polyester threads to form an anti-leakage coating with a thickness of about 0.01 mm, and dry it for later use;
[0033] The second step is to prepare self-adhesive sheet
[0034] First, take 5 parts by weight of natural rubber, 10 parts by weight of water-soluble polyurethane prepolymer and 80 parts by weight of natural sodium bentonite, 1 part by weight of white wax oil as softener, 1 part by weight of petroleum Resin as a thickener and 1 weight part of magnesium hydroxide as a functional filler composed of a flame retardant and 0.5 weight part of anti-aging agent D are sequentially added to the internal mixer, mixed at 140 ° C for 15 minutes, and then filtered Machine filter glue; Then, join filter glue in the screw extruder that has been preheated and be extruded into th...
Embodiment 2
[0039] The first step is to prepare the reinforced lining
[0040] First prepare a paint made of polyurethane, and spray the paint evenly on the interlining cloth with a specification of 150 grams per square meter woven by polypropylene threads to form an anti-leakage coating with a thickness of 0.010-0.015 mm, and dry it for later use;
[0041] The second step is to prepare self-adhesive sheet
[0042] First, get 25 parts by weight of butyl rubber, 5 parts by weight of water-soluble polyurethane prepolymer and 70 parts by weight of calcium-based bentonite, 1.5 parts by weight of pine tar as softener, 1.5 parts by weight of rosin Thickener and 0.5 parts by weight of aluminum hydroxide are used as functional fillers composed of flame retardants and 2.0 parts by weight of anti-aging agent 4010A, sequentially added to the internal mixer, mixed at 80 ° C for 25 minutes, and then used in a rubber filter Filter glue; Then, join the filter glue into the preheated screw extruder and ...
Embodiment 3
[0047] The first step is to prepare the reinforced lining
[0048] First prepare a paint made of acrylic ester, and spray the paint evenly on the interlining cloth with a specification of 200 g / m2 woven by aramid fibers to form an anti-leakage coating with a thickness of 0.015-0.025 mm, and dry it for later use;
[0049] The second step is to prepare self-adhesive sheet
[0050] First, take 20 parts by weight of nitrile rubber, 20 parts by weight of sodium acrylate polymer water-absorbing resin and 30 parts by weight of sodium bentonite, 0.5 parts by weight of naphthenic oil as softener, 1.5 parts by weight of Rosin as a thickener and 1.5 parts by weight of hexabromocyclododecane as a functional filler composed of a flame retardant and 1.5 parts by weight of anti-aging agent D are sequentially added to the internal mixer, and after mixing at 130 ° C for 20 minutes Use a rubber filter machine to filter the glue; then, add the filter glue to a preheated screw extruder to extrude ...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap