Method for preparing white carbon black from polysilicon byproduct silicon tetrachloride

A silicon tetrachloride and white carbon black technology, applied in the direction of silicon oxide, silicon dioxide, etc., can solve the problems of weakening product binding force, long reaction process, and low activity of white carbon black, so as to improve resource utilization and product quality. The quality, production equipment and process are simple to operate, and the effect of realizing environment-friendly production

Inactive Publication Date: 2013-08-14
安徽祥源科技股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The shortcomings of this gas phase method are: high raw material prices, long reaction process, high energy consumption in the production process, and high product prices, which are limited
The shortcomings of this precipitation method are: the activity of the prepared white carbon black is not high, the particles are not easy to control, the affinity is poor, the reinforcing performance is low, and the hydrophilic groups on the surface of the particles are seriously bonded, which weakens the binding force of the product. Production of low-grade products, narrow product application range, and small market capacity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing white carbon black from polysilicon byproduct silicon tetrachloride

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] 1) Put silicon tetrachloride into the hydrolysis reaction kettle, carry out the hydrolysis reaction at 30°C and normal pressure for 1 hour, filter the silicic acid gel and send it to the drum reactor, and HCl gas passes through the primary and secondary acid recovery kettles Water is absorbed and made into hydrochloric acid for subsequent use;

[0019] 2) From the feeding tank, add sodium sodium into the drum reactor, control the mass ratio of silicic acid gel and sodium sodium to 1:2, so that the alkali modulus of foam is 2, add water to the drum reactor, water The mass is 20% of the sum of the mass of silicic acid gel and sodium naphthalene, the temperature is raised to 40°C, the drum reactor is turned on and mixed for 1 hour, and the insoluble impurities are separated by filtration to obtain a clear liquid;

[0020] 3) Send the clear liquid into the precipitation reaction kettle, add sodium dodecylbenzenesulfonate dispersant, the consumption of sodium dodecylbenzenes...

Embodiment 2

[0022] 1) Put silicon tetrachloride into the hydrolysis reaction kettle, carry out the hydrolysis reaction at 50°C and normal pressure for 2 hours, filter the silicic acid gel and send it to the drum reactor, and HCl gas passes through the primary and secondary acid recovery kettles Water is absorbed and made into hydrochloric acid for subsequent use;

[0023] 2) From the feeding tank, add sodium sodium to the drum reactor, control the mass ratio of silicic acid gel and sodium sodium to 1:1, so that the alkali modulus of the foam is 3, and add water to the drum reactor. The mass is 50% of the sum of the mass of silicic acid gel and sodium naphthalene, the temperature is raised to 60°C, the drum reactor is turned on for a mixed reaction for 2 hours, and the insoluble impurities are separated by filtration to obtain a clear liquid;

[0024] 3) Send the clear liquid into the precipitation reaction kettle, add sodium dodecylbenzenesulfonate dispersant, the consumption of sodium do...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for preparing white carbon black from polysilicon byproduct silicon tetrachloride comprises the following steps: introducing silicon tetrachloride into a hydrolysis reaction kettle to conduct hydrolysis reaction and to obtain silicagel and HC1 gas; adding silicagel and sodium silicate into a rotary drum reactor, then adding water to the rotary drum reactor, starting the rotary drum reactor for mixing reaction, separating insoluble impurities, and obtaining clear solution; introducing the clear solution into a precipitation reaction kettle, adding sodium dodecylbenzene sulfonate dispersing agent, adjusting pH value to 8-9, after curing, continuously adjusting pH value to 3.0-5.0, ageing, water washing excessive acid solution, filtering and separating to obtain white carbon black with physical crystal water, then drying and grinding to obtain the product. The invention can most effectively utilize silicagel, has short technical process, relatively simple production equipment and technical operation and can realize industrialized production easily. The white carbon black obtained by the method provided by the invention has high viscosity and intensity, good heat resistance and acid resistance, and other indexes thereof can reach the technical requirement.

Description

technical field [0001] The invention relates to a method for preparing white carbon black from silicon, in particular to a method for preparing white carbon black by utilizing polycrystalline silicon by-product silicon tetrachloride. Background technique [0002] Polysilicon is the main raw material required by the electronics industry and the photovoltaic industry. However, the production of polysilicon produces large amounts of silicon tetrachloride. Silicon tetrachloride is a highly toxic substance, which has a strong irritant effect on the eyes and upper respiratory tract, and seriously pollutes the environment. Therefore, how to effectively use silicon tetrachloride to turn waste into treasure, improve polysilicon production capacity, and realize sustainable polysilicon industry has become a hot topic for enterprises and scholars in recent years. At present, the relatively mature silicon tetrachloride processing technology is as follows: 1. Convert silicon tetrachlori...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B33/12
Inventor 许晓光
Owner 安徽祥源科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com