Ultra-thin steel structure fire-resistant coating material with multi-core structure

A steel structure, ultra-thin technology, applied in fireproof coatings, anti-corrosion coatings, epoxy resin coatings, etc., can solve the problems of unsightly appearance and frequent painting

Active Publication Date: 2012-06-13
天津宝宸恒远科技有限公司
View PDF8 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention solves the problem that the steel structure fireproof paint needs to be painted many times and is not beautiful in the prior art, and provides a composite steel structure fireproof decorative pain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-thin steel structure fire-resistant coating material with multi-core structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Fireproof antirust primer:

[0050] Potassium silicate resin: 12

[0051] Zinc powder: 50

[0052] Zinc oxide: 2

[0053] Titanium oxide: 5

[0054] Nickel oxide: 3

[0055] Bismuth oxide: 1

[0056] Sodium oxide: 0.2

[0057] Silica: 10

[0058] Alumina: 2

[0059] Dispersant: 0.8

[0060] Water: up to 100

[0061] Fireproof middle coat paint:

[0062] Melamine formaldehyde resin: 50

[0063] Expandable graphite composite phosphorus nitrogen flame retardant: 15

[0064] Titanium dioxide: 10

[0065] Talc: 8

[0066] Dispersant: 5

[0067] Thickener: 3

[0068] Water: add water to 100

[0069] Fireproof finish:

[0070] Hydroxy Acrylic: 15

[0071] Polyammonium phosphate: 20

[0072] Titanium dioxide: 20

[0073] Zinc Oxide: 8

[0074] Calcium carbonate: 12

[0075] Coalescent: 2

[0076] Water: Appropriate amount to 100

experiment example

[0077] Experimental example: actual construction example, the coating used for coating is the coating prepared in Example 1.

[0078] Primer layer: Brush the fireproof and antirust primer once, and the dry film thickness is 0.15mm.

[0079] Intermediate coat: Apply fireproof intermediate coat paint 3-4 times, with a total dry film thickness of 1.6mm.

[0080] Topcoat layer: apply fireproof topcoat 2 times, total dry film thickness 0.20mm

[0081] Total dry film thickness: 1.95mm

[0082] Fire resistance time limit: 2 hours (GB14907-2002)

[0083] Experimental results show that: the ultra-thin steel structure fire-resistant coating with multi-core structure of the present invention can form a fire-resistant coating with thinner coating thickness, higher fire-resistant time limit and good decorative effect on the steel structure, and It fully complies with the fire resistance standard of GB14907-2002.

[0084] The primer layer of this example swells at 580°C. The middle coa...

Embodiment 2

[0086] Fireproof antirust primer:

[0087] Sodium silicate resin: 15

[0088] Zinc Dust: 20

[0089] Zinc Oxide: 3

[0090] Titanium oxide: 10

[0091] Nickel Oxide: 1

[0092] Bismuth oxide: 5

[0093] Sodium oxide: 0.5

[0094] Silica: 8

[0095] Alumina: 8

[0096] Dispersant: 0.4

[0097] Thickening and leveling agent: 0.6

[0098] Water: up to 100

[0099] Fireproof middle coat paint:

[0100] Urea-formaldehyde resin: 10

[0101] Expandable graphite composite phosphorus nitrogen flame retardant: 35

[0102] Titanium dioxide: 20

[0103] Talc: 5

[0104] Water: up to 100

[0105] Fireproof finish:

[0106] Epoxy: 30

[0107] Polyammonium phosphate: 10

[0108] Titanium dioxide: 10

[0109] Zinc oxide: 10

[0110] Calcium carbonate: 10

[0111] Dispersant: 2

[0112] Wetting agent: 2

[0113] Coalescing aid: 0.5

[0114] Thickener: 2.5

[0115] Fungicide: 1

[0116] Water: Add appropriate amount to 100

[0117] The coating prepared in Example 2 wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to an ultra-thin steel structure fire-resistant coating material with a multi-core structure. The ultra-thin steel structure fire-resistant coating material is characterized by comprising three parts, i.e. an expandable fire-resistant antirust priming coat at high temperature, an expandable fire-resistant intermediate coat when contacted to fire and a fire-resistant finishing coat. In actual construction, at least one layer of fire-resistant antirust priming coat with a high-temperature expanding function, at least one layer of intermediate coat with an expanding function when contacted to fire and at least one layer of decorative finishing coat with flame retarding and smokeless performance are coated; the priming coat, the intermediate coat and the finishing coat are formed by compounding organic and inorganic materials; when a fire occurs, the intermediate coat and the finishing coat exert synergistic reaction, and thus, an effect that the priming coat carries out fire resisting and heat insulation and the finishing coat carries out inflame retarding and smoke purifying, is achieved. With the adoption of the ultra-thin steel structure fire-resistant coating material with the multi-core structure, provided by the invention, a fire-resistant coating with thinner coating thickness, longer fireproofing time limit and better decorative effect can be formed on a steel structure, and proved by experiments, the fireproofing standards of GB14907-2002 are fully met.

Description

technical field [0001] The invention relates to the field of architectural decoration, in particular to an ultra-thin steel structure fire-resistant coating with a multi-core structure. Background technique [0002] With the gradual increase of steel structure buildings and components in my country and the further implementation of the "Fire Protection Law of the People's Republic of China", fire-resistant coatings for steel structures have been more and more widely used. According to the classification of GB 14907-2002 "General Technical Conditions for Fireproof Coatings for Steel Structures", even the ultra-thin fireproof coatings for steel structures must have a coating thickness of 2mm. According to the calculation of existing high-solid coatings, the construction must also be painted It takes 8-10 times to reach the specified thickness, which brings considerable difficulty to the construction and affects the construction speed of the building. At the same time, today's...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/18C09D5/08C09D1/00C09D1/02C09D161/20C09D161/28C09D161/24C09D133/00C09D163/00C09D7/12B32B33/00
Inventor 张佐连贾纬民
Owner 天津宝宸恒远科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap