High density polyethylene (HDPE)-PA66 composite barrier material and preparation method thereof

A technology of barrier materials and pellets, which is applied in the field of HDPE-PA66 composite barrier materials and its preparation, can solve the problems that the barrier properties of blends cannot be improved, so as to reduce fuel leakage and ensure integrity and uniformity The effect of maintaining continuity and dispersion

Active Publication Date: 2014-12-03
HEFEI GENIUS NEW MATERIALS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the blending process, if the barrier resin is not stretched enough and is distributed in the matrix resin in the form of larger particles, or the barrier resin is broken into particles due to excessive shearing and does not form a sheet, The barrier properties of the blends were not improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Prepare materials according to the following components and contents:

[0027] Commercially available high-density polyethylene resin 50kg, nylon 66 flat yarn 40kg, maleic anhydride graft compatibilizer 10kg;

[0028] (2) melting the high-density polyethylene resin at 190°C to obtain a high-density polyethylene resin melt;

[0029] (3) The nylon 66 (PA66) flat yarn is drawn out from the creel, the tension is adjusted by the tension roller, and then enters the melt dipping die head, and the nylon 66 flat yarn is treated with the compatibilizer and the melt of the high-density polyethylene resin in the die head. The silk is dispersed and infiltrated, so that the nylon 66 flat silk is completely infiltrated;

[0030] (4) the obtained fully soaked nylon 66 flat yarn is cut into pellets of corresponding length after cooling;

[0031] (5) Send the pellets into the hollow blow molding machine, and blow molding to obtain the HDPE-PA66 composite single-layer barrier oil ta...

Embodiment 2

[0033] (1) Prepare materials according to the following components and contents:

[0034] Commercially available high-density polyethylene resin 70kg, nylon 66 flat yarn 25kg, maleic anhydride graft compatibilizer 5kg;

[0035] (2) melting the high-density polyethylene resin at 180°C to obtain a high-density polyethylene resin melt;

[0036] (3) The nylon 66 flat yarn is drawn out from the creel, the tension is adjusted by the tension roller, and then enters the melt dipping die head, and the nylon 66 flat yarn is dispersed in the die head with the melt of the compatibilizer and the high-density polyethylene resin and infiltration, so that the nylon 66 tapes are completely infiltrated;

[0037] (4) the obtained fully soaked nylon 66 flat yarn is cut into pellets of corresponding length after cooling;

[0038] (5) Send the pellets into the hollow blow molding machine, and blow molding to obtain the HDPE-PA66 composite single-layer barrier oil tank.

Embodiment 3

[0040] (1) prepare 88kg, nylon 66 flat yarn 10kg, maleic anhydride graft compatibilizer 2kg according to the following components and content;

[0041] (2) melting the high-density polyethylene resin at 170°C to obtain a high-density polyethylene resin melt;

[0042] (3) The nylon 66 flat yarn is drawn out from the creel, the tension is adjusted by the tension roller, and then enters the melt dipping die head, and the nylon 66 flat yarn is dispersed in the die head with the melt of the compatibilizer and the high-density polyethylene resin and infiltration, so that the nylon 66 tapes are completely infiltrated;

[0043] (4) the obtained fully soaked nylon 66 flat yarn is cut into pellets of corresponding length after cooling;

[0044] (5) Send the pellets into the hollow blow molding machine, and blow molding to obtain the HDPE-PA66 composite single-layer barrier oil tank.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high density polyethylene (HDPE)-PA66 composite barrier material and a preparation method thereof. The material comprises the following components by weight: 50 to 90 parts of high density polyethylene resin, 10 to 40 parts of nylon 66 ribbon-like filament and 0 part to 10 parts of compatilizer. Compared with the prior art, the nylon 66 resin for isolation in the product exists in the formation of the slice-shaped ribbon-like filament from beginning to end, maintains continuity and dispersibility of the nylon 66 ribbon-like filament as an isolation material in the particle material, and ensures completeness and evenness of the nylon 66 ribbon-like filament in a single-layer oil tank and obtained through the following blow molding process. Therefore, fuel oil can meet large resistance when penetrating through the wall of the oil tank due to the nylon 77 ribbon-like filament, so that fuel oil leakage of the fuel oil tank is reduced, and the isolation performance of the fuel oil tank is improved.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to an HDPE-PA66 composite barrier material and a preparation method thereof. Background technique [0002] As a commonly used packaging material, high-density polyethylene (HDPE) has many advantages: high stiffness, strength, hardness, creep resistance, gloss and moisture permeability resistance, good impact toughness, electrical insulation resistance, tear resistance, low temperature resistance, etc., but the resistance of HDPE 2 , CO 2 It has poor permeability and oil resistance, so it needs to be modified to meet the requirements of high barrier properties of packaging materials. [0003] At present, the methods used to improve the barrier properties of high-density polyethylene mainly include: surface treatment technologies such as fluorination, sulfonation or spraying on the surface of plastics; multi-layer co-extrusion technologies such as polyethylene layers, adhesi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L77/06C08L51/06C08L51/00
Inventor 肖玲玲
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com