Film material for PE coated paper

A coating paper and coating technology, which is applied in the field of coating materials of matte coating paper, can solve problems such as poor adhesion, damage to the purity and consistency of the coating, achieve stable release force, improve bonding fastness, The effect of easy operation

Inactive Publication Date: 2012-09-12
SUZHOU SIDIKE NEW MATERIALS SCI & TECH
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high flatness of the coating layer and the poor adhesion between the release agent coating and the coating layer, when the release paper is attached to the film coated with a high-viscosity adhesive, it is easy to cause cracks on the release paper. The release agent coating is taken away by the adhesive with greater adhesion, thus forming a difficult-to-clean release agent coating area on the local surface of the film, destroying the overall purity and consistency of the film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: A coating material for coating paper

[0023] A coating material for coating paper, the raw material formula of the coating material is composed of the following materials in mass percentage:

[0024] Polymer 71.2%~90.8%;

[0025] Lubricant 0.2%~1.2%;

[0026] Fogging filler 9%~27.6%;

[0027] Wherein, the polymer is selected from polyethylene, polypropylene, polyvinyl chloride, polyethylene terephthalate, polybutylene terephthalate; the lubricant is selected from paraffin, white oil, hard Fatty acid, stearate; the filler is a solid particle with a particle size of 3-20 microns.

[0028] The preferred technical solution of the present invention, the fogging filler is at least one of calcium hydroxide, talcum powder and calcium sulfate.

[0029] The preferred technical solution of the present invention, the stearate comprises calcium stearate, magnesium stearate, zinc stearate and sodium stearate.

[0030] The preferred technical solution of the presen...

Embodiment 2 6

[0033] Embodiment two to six: a kind of coating material for coating paper

[0034] A coating material for coating paper, the raw material formula of the coating material is composed of the following materials in mass percentage:

[0035] polymer lubricant fog filler Embodiment two 71.2% 1.2% 27.6% Embodiment Three 90.8% 0.2% 9% Embodiment Four 85% 0.4% 14.6% Embodiment five 80% 0.5% 19.5% Embodiment six 75% 0.6% 24.4%

[0036] Note: 1. The percentage sign in the table indicates the mass percentage.

[0037] 2. Polymer: Example 2, polyethylene; Example 3, polypropylene; Example 4, PVC; Example 5, PET; Example 6, polypropylene and polyethylene according to the mass ratio of 1:1.

[0038] 3, lubricant: embodiment two, white oil; embodiment three, magnesium stearate; embodiment four, solid paraffin; embodiment five, white oil and stearic acid according to the mass ratio of 2: 1; embodiment six, Calcium stearate.

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

Disclosed is a film material for PE coated paper. Raw material formula of the film material is composed of 71.2-90.8% of a polymer, 0.2-1.2% of a lubricant and 9-27.6% of a fogging filler, wherein the polymer is selected from the group consisting of polyethylene, polypropylene, PVC and PET; and the filler is solid particles with the particle size being 3-20 micrometers. A fogging-surface release film with stable release force and good pressure-sensitive adhesive surface fogging effect can be produced, thus reaching low reflection effect of transfer adhesive surface. The production technology is simple, equipment investment cost is low and equipment is convenient to operate.

Description

technical field [0001] The invention relates to a coating material for coating paper, in particular to a coating material for matte coating paper. Background technique [0002] Coated paper, also known as anti-seepage paper, uses a laminating machine to heat-melt the laminating material (such as polyethylene, polypropylene) particles at high temperature and extrude them on the paper (substrate) to form a coating layer, which is then pressed together. , cooling, winding and other processes made of composite paper, the coating layer weight is generally about 20 grams to 25 grams per square meter. The main purpose of coated paper is to make release paper, and release paper is widely used to isolate the glue surface of the tape. The existing release paper is generally coated with a layer of release agent layer (the material used is mainly silicone oil) on the surface of the coated paper to obtain the release paper. However, due to the high flatness of the coating layer and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/04C08L23/10C08L27/06C08L67/02C08K5/01C08K5/09C08K5/098C08K3/36C08K3/22C08K3/34C08K3/30
Inventor 金闯周满意
Owner SUZHOU SIDIKE NEW MATERIALS SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com