Magnesium alloy surface conversion treatment liquid and treatment method thereof

A technology of conversion treatment and magnesium alloy, which is applied in the coating process of metal materials, etc., can solve the problems of coarse grains and wide cracks in the conversion film, and achieve the effects of increased density, good film density and excellent corrosion resistance

Active Publication Date: 2013-10-30
GUANGDONG INST OF NEW MATERIALS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In addition, the phosphate conversion coating commonly used on magnesium alloys has better corrosion resistance and is a good coating primer, but the conversion coating is prone to wide cracks and coarse grains.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium alloy surface conversion treatment liquid and treatment method thereof
  • Magnesium alloy surface conversion treatment liquid and treatment method thereof
  • Magnesium alloy surface conversion treatment liquid and treatment method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The composition and content of the magnesium alloy conversion treatment solution are phytic acid: 20g / l, calcium nitrate: 2g / l, sodium tartrate: 1g / l and ammonium metavanadate: 2g / l.

Embodiment 2

[0025] The composition and content of the magnesium alloy conversion treatment solution are phytic acid: 5g / l, calcium nitrate: 1g / l, sodium tartrate: 0.5g / l and ammonium metavanadate: 0.2g / l.

Embodiment 3

[0027] The composition and content of the magnesium alloy conversion treatment liquid are phytic acid: 45g / l, calcium nitrate: 3g / l, sodium tartrate: 0.2g / l and ammonium metavanadate: 1g / l.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to magnesium alloy surface conversion treatment liquid and a treatment method thereof. The magnesium alloy surface conversion treatment liquid comprises the following components of: 5 to 45 g / l of phytic acid, 0.1 to 3 g / l of calcium nitrate, 0.1 to 5 g / l of sodium tartrate and 0.1 to 3 g / l of ammonium metavanadate. The magnesium alloy surface conversion treatment method comprises the following steps of: performing mechanical pretreatment; deoiling and degreasing; performing acid washing; converting; and drying. The magnesium alloy surface conversion treatment liquid does not contain environmental pollution ingredients of chromium, fluorine and the like, the treatment method is simple and high in efficiency, and the compactness of film layers and the corrosion resistance and adhesive force of magnesium alloy organic coatings can be improved. The magnesium alloy surface conversion treatment liquid can be widely applied to the surface coating pretreatment of magnesium alloy castings, section bars and magnesium alloy products.

Description

technical field [0001] The invention relates to a surface conversion treatment liquid and a treatment method thereof, in particular to a magnesium alloy conversion treatment liquid and a conversion treatment method. Background technique [0002] Magnesium alloy has the characteristics of high specific strength and specific stiffness, good casting performance, excellent electrical shielding and damping performance, and recyclability. It is widely used in aerospace, automobiles and motorcycles, tools, electronic communications, optical instruments, computer manufacturing, etc. field. Since the electrode potential of the magnesium alloy is extremely negative (-2.36V), and the volume ratio of the natural oxide film to the metal itself is less than 1, it is not enough to protect the magnesium alloy matrix, and its corrosion resistance is poor. In order to improve the corrosion resistance of the magnesium alloy surface, many protective treatment methods have been developed, such ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/40
Inventor 宋东福戚文军赵雅情农登黄正华周楠郑开宏李林蔡畅王娟徐静王海艳王顺成
Owner GUANGDONG INST OF NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com