Heat-resistant conductive polypropylene composite material and preparation method thereof

A composite material, polypropylene technology, applied in the field of heat-resistant conductive polypropylene composite material and its preparation, can solve the problems of reduced conductive synergistic effect, poor mechanical properties of the composite system, poor compatibility, etc., to improve the conductive effect, surface The effect of resistance reduction and workability improvement

Active Publication Date: 2012-09-19
KINGFA SCI & TECH CO LTD +1
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are defects such as poor compatibility between polypropylene and epoxy resin, poor mechanical pro

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-resistant conductive polypropylene composite material and preparation method thereof
  • Heat-resistant conductive polypropylene composite material and preparation method thereof
  • Heat-resistant conductive polypropylene composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention will be further described below through specific embodiments. The following examples are preferred implementation forms of the present invention, but the implementation manners of the present invention are not limited by the following examples.

[0026] In the formulas of the examples and comparative examples shown in Table 1 and Table 3: the selected polypropylene is PP HJ4045 produced by Korea Petrochemical Company; the compatibilizer is the maleic anhydride grafted polypropylene PC-1 produced by Guangzhou Baichen Company , the grafting rate is 0.5%; the carbon black is Cabot conductive carbon black VXC-500; the glass fiber is the alkali-free chopped glass fiber ESC13-4.5-508A produced by Jushi Group Co., Ltd.; the antioxidant is produced by Ciba The compound of hindered phenol antioxidant Irganox 1010 and organic phosphite Irganox 168, the ratio is 1:2.

[0027] Its preparation method: in parts by weight, take polypropylene, antioxidant and lubr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat-resistant conductive polypropylene composite material and a preparation method thereof; the heat-resistant conductive polypropylene composite material comprises components in parts by mass: 45-75 parts of polypropylene, 5-30 parts of glass fiber and 16-24 parts of conductive carbon black. The composite material takes polypropylene as matrix resin and is prepared by a one-step melt kneading method; the glass fiber and the conductive carbon black have an obvious conductive synergistic effect, so that the composite material has excellent rigidity, heat resistance and good electrical conductivity; and the surface resistance is not higher than 109W, so that the composite material can be applied to a package and a chip carrier with anti-static requirement as well as a motor vehicle and the information and communication industry with electromagnetic shielding requirement.

Description

technical field [0001] The invention relates to a polypropylene composite material, in particular to a heat-resistant and conductive polypropylene composite material and a preparation method thereof. Background technique [0002] Glass fiber reinforced polypropylene is added glass fiber and other additives to the original polypropylene matrix to improve the rigidity and heat resistance of the material and reduce shrinkage. Generally speaking, most of the glass fiber reinforced materials are mostly used in the structural parts of the product. It is a structural engineering material and expands the scope of use of polypropylene resin. [0003] Carbon black is the most commonly used conductive filler. The raw material is easy to obtain and light in weight. Its volume resistivity is about 0.1W cm. According to the filling amount, the resistivity of the composite material can be flexibly adjusted. Carbon black filled composite materials are easy to form and process, and have bee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/14C08L51/06C08L51/00C08K13/04C08K7/14C08K3/04
Inventor 苏娟霞叶南飚刘奇祥姜苏俊宁方林易庆锋龙杰明
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap