Granular material for cigarette filter stick and preparation method of granular material

A technology of granular materials and cigarette filter rods, applied in e-liquid filter elements, applications, tobacco, etc., can solve problems affecting cigarette smoking, unstable application effects, complex production processes, etc., achieve high retention rate, avoid loss, enhance the combined effect

Active Publication Date: 2012-12-26
YUNNAN SHENBOYUAN BIOLOGICAL TECH
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The present invention aims to solve the problems of complex production process of existing cigarette filter rod additives, affecting the taste of cigarettes, unstable application effect, etc., and provides a product with high adsorption performance, which can effectively reduce the amount of tar in cigarettes and the content of harmful substances in cigarette smoke. Particulate material for cigarette filter rods without affecting the taste of cigarettes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: a kind of granular material for cigarette filter stick and preparation method thereof, this granular material is mainly formed by compounding of degummed hemp fiber powder, microcrystalline cellulose, nano-calcium carbonate, water-soluble chitosan and tobacco extract, each 100 catties of granular material is made through the following steps:

[0023] Step 1, material mixing: get 30kg fiber length and be the degummed hemp fiber powder of 0.8mm, the microcrystalline cellulose of 35kg particle size 60um, the nano calcium carbonate of 20kg and 0.5kg degree of deacetylation be 90% water-soluble chitosan Mix the powdery materials, after stirring evenly, add 34.2kg of clear water, put into the flour mixing equipment and mix evenly to obtain wet materials;

[0024] Step 2, granule molding: put the wet material into the extrusion spheronization equipment for granulation, and obtain round granules with a rough surface and a diameter of 0.5 mm;

[0025] Step 3, dryin...

Embodiment 2

[0030] Embodiment 2: a kind of granular material for cigarette filter rod and preparation method thereof, this granular material is mainly formed by degumming hemp fiber powder, microcrystalline cellulose, nano-calcium carbonate, water-soluble chitosan and tobacco extract, each 100 catties of granular material is made through the following steps:

[0031] Step 1, material mixing: get 40kg fiber length and be the degummed hemp fiber powder of 0.6mm, the microcrystalline cellulose of 30kg particle size 40um, the nano-calcium carbonate of 16kg and the water-soluble chitosan of 90% deacetylation degree of 2.8kg Mix the powdery materials, after stirring evenly, add 26.64kg of clear water, put into the flour mixing equipment and mix evenly to obtain wet materials;

[0032] Step 2, granule forming: put the wet material into the extrusion spheronization equipment for granulation, and obtain round granules with a rough surface and a diameter of 0.3 mm;

[0033] Step 3, drying: drying t...

Embodiment 3

[0037] Embodiment 3: a kind of granular material for cigarette filter stick and preparation method thereof, this granular material is mainly formed by compounding of degummed hemp fiber powder, microcrystalline cellulose, nano-calcium carbonate, water-soluble chitosan and tobacco extract, each 100 catties of granular material is made through the following steps:

[0038] Step 1, material mixing: get 50kg fiber length and be the degummed hemp fiber powder of 0.5mm, the microcrystalline cellulose of 25kg particle size 20um, the nano-calcium carbonate of 12kg and the water-soluble chitosan of 95% deacetylation degree of 2.5kg Mix the powdery materials, after stirring evenly, add 35.8kg of clear water, put into the flour mixing equipment and mix evenly to obtain wet materials;

[0039] Step 2, granule forming: put the wet material into the extrusion spheronization equipment for granulation, and obtain round granules with a rough surface and a diameter of 0.4 mm;

[0040] Step 3, dry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Fiber lengthaaaaaaaaaa
Particle sizeaaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses granular material for a cigarette filter stick and a preparation method of the granular material, relates to the cigarette filter stick and particularly relates to adsorption granular material added to tows of the cigarette filter stick and the preparation method of the adsorption granular material. The invention is characterized in that the granular material is prepared by unglued jute fiber powder, microcrystalline cellulose, nanometer calcium carbonate, water-soluble chitosan and tobacco extract through the procedures of material mixing, granule forming, drying, preparing tobacco extract and granule scenting. The granular material for the cigarette filter stick and the preparation method have the advantages that the adsorption performance is high, the retention rate is high, the safety high, the bonding force is high, and selective adsorption is realized.

Description

technical field [0001] The invention relates to a cigarette filter rod, in particular to an adsorption particle material added to a cigarette filter rod tow and a preparation method thereof. technical background [0002] Smoking is harmful to health, which is the consensus of today's society. With the continuous improvement of health awareness of cigarette consumers, their demand for cigarette products tends to be more low-harm, safety, health and other aspects. The main purpose of cigarette "harm reduction and tar reduction" is to develop low-tar and low-hazard products that meet the needs of consumers, meet the psychological and physical needs of cigarette consumers, and minimize the harm caused by cigarettes to consumers' health . [0003] As an important part of cigarettes, cigarette filter rods can reduce harm and coke by adjusting the length of the filter rods, tow specifications and ventilation dilution, but it has a relatively large negative impact on the smoking...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A24D3/10A24D3/16A24D3/06
Inventor 郑屹杨绍文阚迎
Owner YUNNAN SHENBOYUAN BIOLOGICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com