Synergistic limestone desulfuration absorbent

A limestone and absorbent technology, which is applied in the field of synergistic limestone desulfurization absorbent, can solve the problems of affecting the desulfurization effect, unstable coal sulfur content, and desulfurization system exceeding the design value, so as to reduce energy consumption and alleviate equipment calcium scale Effect

Inactive Publication Date: 2014-11-05
XINJIANG XINHENGFA ENVIRONMENTAL PROTECTION SCI & TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, 90% of domestic power plants use FGD wet desulfurization technology, but due to the limited solubility of limestone and unstable coal sulfur content, the desulfurization system often exceeds the design value, which affects the desulfurization effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A synergistic limestone desulfurization absorbent, consisting of the following components in parts by weight:

[0032] 90 parts of limestone, 6 parts of dolomite, 1 part of magnesium sulfate, 1 part of adipic acid, 2 parts of disodium adipate;

[0033] The content of calcium carbonate in the limestone is more than or equal to 93%;

[0034] The desulfurization absorbent is powdery white solid particles with a particle size of 325 mesh.

[0035] The preparation method is:

[0036] (1) Crush the above-mentioned limestone and dolomite to 2-3cm, mix them and add them to the Raymond mill through a belt conveyor;

[0037] (2) Mix the above-mentioned magnesium sulfate, adipic acid, and disodium adipate in the mixing tank in proportion, and then weigh the limestone and dolomite that are sent to the Raymond machine and step (1) through a belt conveyor weighing machine. Grinding stones together to a particle size of 325 mesh.

[0038] Tests have proved that the results of the ...

Embodiment 2

[0044] A synergistic limestone desulfurization absorbent, consisting of the following components in parts by weight:

[0045] 60 parts of limestone, 30 parts of dolomite, 6 parts of magnesium sulfate, 3 parts of citric acid, 4 parts of sodium citrate;

[0046] The content of calcium carbonate in the limestone is more than or equal to 93%;

[0047] The desulfurization absorbent is powdery white solid particles with a particle size of 400 mesh.

[0048] The preparation method is:

[0049] (1) Crush the above-mentioned limestone and dolomite to 2-3cm, mix them and add them to the Raymond mill through a belt conveyor;

[0050] (2) Mix the above-mentioned magnesium sulfate, citric acid, and sodium citrate in the mixing tank in proportion, then weigh them into the Raymond machine and powder them with the limestone and dolomite in step (1) Grind to a particle size of 400 mesh.

[0051] Tests have proved that the results of the desulfurization absorbent of the present embodiment a...

Embodiment 3

[0057] A synergistic limestone desulfurization absorbent, consisting of the following components in parts by weight:

[0058] 90 parts of limestone, 40 parts of dolomite, 10 parts of magnesium sulfate, 6 parts of succinic acid, 8 parts of sodium succinate;

[0059] The content of calcium carbonate in the limestone is more than or equal to 93%;

[0060] The desulfurization absorbent is powdery white solid particles with a particle size of 500 mesh.

[0061] The preparation method is the same as in Example 1.

[0062] Tests have proved that the results of the desulfurization absorbent of the present embodiment are as follows:

[0063] 1) Increase the desulfurization rate of FGD system by 8%;

[0064] 2) When the sulfur content of the coal used by the power plant exceeds the design value by 20%, the desulfurization rate can be maintained above 92%;

[0065] 3) Reduce the slurry circulation intensity by 26%, thereby reducing the energy consumption of the desulfurization system; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a synergistic limestone desulfuration absorbent. The synergistic limestone desulfuration absorbent comprises the following materials in parts by weight: 30-90 parts of limestone, 1-40 part(s) of dolomite, 1-10 part(s) of magnesium sulfate, 1-6 part(s) of organic polyatomic acid and 1-8 part(s) of organic polyatomic acid salt. The synergistic limestone desulfuration absorbent has the advantages that a desulfuration rate is improved, and when the content of coal sulfur components exceeds a design value by 20%, the desulfuration rate is above 90%; and the energy consumption of a desulfuration system is reduced, and the formation of equipment calcium scales in the desulfuration system is decelerated.

Description

technical field [0001] The invention relates to a desulfurization absorbent, in particular to a synergistic limestone desulfurization absorbent, which is applied to a wet flue gas desulfurization system of a power plant, that is, an FGD system, and belongs to the field of desulfurization absorbents. Background technique [0002] At present, 90% of domestic power plants use FGD wet desulfurization technology, but due to the limited solubility of limestone and unstable coal sulfur content, the desulfurization system often exceeds the design value, which affects the desulfurization effect. Contents of the invention [0003] In order to solve the above problems, the present invention designs a synergistic limestone desulfurization absorbent, which can maintain a desulfurization rate of more than 90% when the coal sulfur content exceeds the design value by 20%, ensuring the desulfurization effect. [0004] Technical scheme of the present invention is: [0005] A synergistic li...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D53/80B01D53/50
Inventor 郑刚张淑萍陈武生韩亚荣卢静华
Owner XINJIANG XINHENGFA ENVIRONMENTAL PROTECTION SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com