Ultraviolet (UV) offset tin printing ink and method for preparing same

A printing and ink technology, which is applied in the field of UV offset printing iron ink and its preparation, can solve the problems of high viscosity, use, ink fluidity, and poor transferability, etc.

Inactive Publication Date: 2013-03-13
东莞市佳烨化工科技有限公司
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Metal printing is basically carried out in the form of offset printing. Metal printing ink has the printing suitability and printing effect of offset printing ink. Due to the printing adaptability and printing effect of the non-permeable body of the metal plate, the existing metal printing ink It has the characteristics of resistance to mechanical processing, and its properties are characterized by high viscosity and low fluidity. However, this is very unfavorable to the transfer of ink during printing, so it is necessary to improve the printing adaptability of metal printing iron ink
[0003] The Chinese invention patent application with appl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] A UV offset printing iron printing ink, consisting of the following raw materials in parts by weight: 28 parts of urethane acrylate, 20 parts of polyester acrylate, 2 parts of TPGDA, 5 parts of TMPTA, 1 part of HDDA, 14 parts of yellow pigment powder, 1 part of urethane Ester copolymer solution, 0.2 parts of modified polysiloxane copolymer solution, 1 part of silicone leveling agent, 1 part of 2-methyl-1-[4-(methylthio)phenyl]-2- (4-morpholino)-1-propanone, 0.2 parts of organic fluorine-modified acrylate polymer.

[0065] The preparation method of a kind of UV offset printing iron printing ink of the present embodiment comprises the following method steps: a, polyurethane acrylate, polyester acrylate are added by weight in the batching tank and stirred evenly, and the stirring time is 25min; b, step a Add the yellow pigment powder and the modified polysiloxane interpolymer solution in parts by weight to the material mixed in the middle under low-speed stirring, and cont...

Embodiment 2

[0068] A kind of UV offset printing iron printing ink, is made up of the raw material of following parts by weight: 38 parts of polyurethane acrylate, 30 parts of polyester acrylate, 10 parts of TPGDA, 12 parts of TMPTA, 9 parts of HDDA, 22 parts of yellow pigment powder, 3 parts of amino methyl Ester copolymer solution, 1.2 parts of modified polysiloxane copolymer solution, 4 parts of silicone leveling agent, 3 parts of 2-methyl-1-[4-(methylthio)phenyl]-2- (4-morpholino)-1-acetone, 1.5 parts of organic fluorine-modified acrylate polymer.

[0069] The preparation method of a kind of UV offset printing iron printing ink of the present embodiment, comprises the following method steps: a, polyurethane acrylate, polyester acrylate are added in batching tank by weight and stirred evenly, and stirring time is 30min; b, step a Add the yellow pigment powder and the modified polysiloxane interpolymer solution to the mixed material in the state of low-speed stirring, and continue to sti...

Embodiment 3

[0072] A kind of UV offset printing iron printing ink, is made up of the raw material of following parts by weight: 30 parts of polyurethane acrylate, 22 parts of polyester acrylate, 4 parts of TPGDA, 6 parts of TMPTA, 3 parts of HDDA, 16 parts of red pigment powder, 1 part of carbamate Ester copolymer solution, 0.4 parts of modified polysiloxane copolymer solution, 1 part of silicone leveling agent, 1 part of 2-methyl-1-[4-(methylthio)phenyl]-2- (4-morpholino)-1-propanone, 0.4 parts of organic fluorine-modified acrylate polymer.

[0073] The preparation method of a kind of UV offset printing iron printing ink of the present embodiment comprises the following method steps: a, polyurethane acrylate, polyester acrylate are added by weight in the batching tank and stirred evenly, and the stirring time is 28min; b, step a Add the red pigment powder and the modified polysiloxane interpolymer solution by weight to the mixed material in the low-speed stirring state, continue to stir ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of ink, and in particular relates to an ultraviolet (UV) offset tin printing ink and a method for preparing the same. The UV offset tin printing ink consists of the following raw materials in parts by weight: 28-38 parts of urethane acrylate, 20-30 parts of polyester acrylate, 2-10 parts of 2-propenoic acid, 1, 1'-[(1-methyl-1, 2-ethanediyl) bis [oxy(methyl-2, 1-ethanediyl)]] ester (TPGDA), 5-12 parts of trimethyl propane triacrylate (TMPTA), 1-9 parts of hexanediol diacrylate (HDDA), 14-22 parts of pigment powder, 1-3 parts of dispersing agent, 0.2-1.2 parts of organic silicon defoamer, 1-4 parts of organic silicon flatting agent, 1-3 parts of photoinitiator and 0.2-1.5 parts of adhesion promoter. The UV offset tin printing ink has low adhesiveness, improved fluidity, good ink flexibility, good transfer printing performance and good adaptability to metal product printing.

Description

technical field [0001] The invention relates to the technical field of inks, in particular to a UV offset iron printing ink and a preparation method thereof. Background technique [0002] Since the introduction of German-made platform printing machines in my country in 1900, metal printing has started. Metal printing is mainly used in packaging containers to convey the information of the items in the packaging, and to increase the added value through the effect of color and packaging. Metal printing is basically carried out in the form of offset printing. Metal printing ink has the printing suitability and printing effect of offset printing ink. Due to the printing adaptability and printing effect of the non-permeable body of the metal plate, the existing metal printing ink It has the characteristics of resistance to mechanical processing, and its properties are characterized by high viscosity and low fluidity. However, this is very unfavorable to the transfer of ink during ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/10C09D11/101C09D11/107
Inventor 尹文科
Owner 东莞市佳烨化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap