UV photoluminescence ink

A technology of photoluminescence and luminescent powder, which is applied in the direction of ink, household utensils, fibrous fillers, etc., can solve the problems of poor friction resistance, environmental pollution, and solvent resistance, and achieve the adjustment of solubility and viscosity reduction performance, raw materials Inexpensive and easy to obtain, the effect of improving printing quality

Inactive Publication Date: 2013-03-20
HUNAN UNIV OF TECH +1
View PDF9 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of ZnS:Cu as the visible light excitation of luminescent material preparation, green UV photoluminescence ink, this ink solves the problem that the existin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Epoxy acrylic resin 27.0 wt%

[0025] Polyester acrylate resin 27.0 wt%

[0026] Diethylamine 4.0 wt%

[0027] Trimethylolpropane Triacrylate 1.5 wt%

[0028] Tripropylene glycol diacrylate 1.5 wt%

[0029] 1-Hydroxy-cyclohexyl-phenylmethanone 3.5 wt%

[0030] Modified yellow-green luminescent powder 33.0 wt%

[0031] Defoamer Foamex N 2.5 wt%.

[0032] First, 40.0 parts by weight of epoxy acrylic resin and 40.0 parts by weight of polyester acrylate resin are stirred and mixed to form a prepolymer; 2.5 parts by weight of trimethylolpropane triacrylate and 2.5 parts by weight of tripropylene glycol diacrylate are stirred and mixed to form dilute monomer. Then add 54.0 parts by weight of prepolymer, 4.0 parts by weight of diethylamine, 3.0 parts by weight of diluted monomer and 3.5 parts by weight of 1-hydroxy-cyclohexyl-phenyl ketone into the black mixing bucket with a cover, and stir at a low speed 20 minutes; finally add 33.0 parts by weight of modified yellow-g...

Embodiment 2

[0034] Epoxy acrylic resin 20.0 wt%

[0035] Polyester acrylate resin 20.0 wt%

[0036] Diethylamine 4.0 wt%

[0037] Trimethylolpropane Triacrylate 1.5 wt%

[0038] Tripropylene glycol diacrylate 1.5 wt%

[0039] 1-Hydroxy-cyclohexyl-phenylmethanone 3.5 wt%

[0040] Modified yellow-green luminescent powder 44.5 wt%

[0041] Defoamer Foamex N 5.0 wt%.

[0042] First, 30.0 parts by weight of epoxy acrylic resin and 30.0 parts by weight of polyester acrylate resin are stirred and mixed to form a prepolymer; 2.5 parts by weight of trimethylolpropane triacrylate and 2.5 parts by weight of tripropylene glycol diacrylate are stirred and mixed to form dilute monomer. Then add 40.0 parts by weight of prepolymer, 4.0 parts by weight of diethylamine, 3.0 parts by weight of diluted monomer and 3.5 parts by weight of 1-hydroxyl-cyclohexyl-phenyl ketone into a black mixing bucket with a cover, and stir at a low speed 20 minutes; finally add 44.5 parts by weight of modified yellow-gr...

Embodiment 3

[0044] Epoxy acrylic resin 17.0 wt%

[0045]Polyester acrylate resin 17.0 wt%

[0046] Diethylamine 4.5 wt%

[0047] Trimethylolpropane Triacrylate 1.5 wt%

[0048] Tripropylene glycol diacrylate 1.5 wt%

[0049] 1-Hydroxy-cyclohexyl-phenylmethanone 3.5 wt%

[0050] Modified yellow-green luminescent powder 50.0 wt%

[0051] Defoamer Foamex N 5.0 wt%.

[0052] First, 20.0 parts by weight of epoxy acrylic resin and 20.0 parts by weight of polyester acrylate resin are stirred and mixed to form a prepolymer; 2.5 parts by weight of trimethylolpropane triacrylate and 2.5 parts by weight of tripropylene glycol diacrylate are stirred and mixed to form dilute monomer. Then add 34.0 parts by weight of prepolymer, 4.5 parts by weight of diethylamine, 3.0 parts by weight of dilute monomer and 3.5 parts by weight of 1-hydroxyl-cyclohexyl-phenyl ketone into a black mixing bucket with a cover, and stir at a low speed 20 minutes; finally add 50.0 parts by weight of modified yellow-gree...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a UV photoluminescence ink, and belongs to the field of printing ink preparation. The UV photoluminescence ink is characterized in that modified ZnS:Cu is adopted as a luminescence material, a mixture of an epoxy acrylic acid resin and a polyester acrylate resin is adopted as a prepolymer, a mixture of trimethylolpropane triacrylate and tripropylene glycol diacrylate is adopted as a diluted monomer, a photoinitiator, an accelerator, an antifoaming agent and the like are matched, and uniform mixing is performed to obtain the finished product. The UV photoluminescence ink can be widely applicable for printing on securities, tax receipts, invoices, credit cards and other valuable bills.

Description

technical field [0001] The invention relates to a printing UV ink, that is, a UV photoluminescent ink used in the fields of commodity outer packaging, securities, tax invoices, invoices, credit cards and the like. Background technique [0002] Photoluminescent anti-counterfeiting ink has the characteristics of good concealment, bright colors, low cost and convenient implementation of anti-counterfeiting technology, and shows great application potential in the fields of securities, tax stamps, invoices, credit cards and other valuable notes. In recent years, a variety of photoluminescent anti-counterfeiting inks have been developed at home and abroad. For example, Chinese patent CN1544545A discloses a long afterglow luminous ink, Chinese patent CN1313364A discloses a luminous ink paint, Chinese patent CN1143659A discloses a universal color luminous ink, and Chinese patent CN1465631A discloses a non-emissive environmental protection energy storage Luminescent ink, Chinese pat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/10C09C1/04C09C3/12C09D11/03C09D11/101C09D11/107
Inventor 颜爱国刘浩梅薛继武石亮张馨宇武凡靖
Owner HUNAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap