Fireproof cement foam insulation board
A fireproof insulation board and cement foaming technology, which is applied in the field of cement building materials, can solve the problems of complex production process, high cost, and difficulty in controlling the foaming effect, and achieve the effect of good heat preservation effect, fast time, and fine air bubbles
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0009] Example one
[0010] Take 1 kg of stearic acid, 0.1 kg of sodium carbonate, 1 kg of ammonia, 0.1 g of sodium fluoride, 1 kg of potassium hydroxide, and 85 kg of water to prepare a waterproofing agent.
[0011] Take 38kg of sulphoaluminate cement, 28kg of fly ash, 0.28kg of wood anti-cracking fiber, 2.9kg of water repellent, 0.55kg of calcium stearate, 0.18kg of polycarboxylic acid water reducing agent and 25kg of water and mix it, then add GM-A After stirring 2.0kg of foaming agent, quickly pour it into the template, and obtain it after curing and demoulding. It is cut and packaged as required. Among them, the wooden anti-cracking fiber uses polypropylene fiber, and the polycarboxylic acid water reducer uses the BRJ-T200 type polycarboxylic acid water reducer of Jiangsu Bai Ruiji New Material Co., Ltd.
[0012] The index of the prepared product is: the dry density is 220kg / m 3 , The foaming height is 33cm, the compressive strength is 0.65MPa, the bonding strength is 0.45M...
Example Embodiment
[0018] Example two
[0019] Take 5 kg of stearic acid, 0.5 kg of sodium carbonate, 5 kg of ammonia, 1 g of sodium fluoride, 5 kg of potassium hydroxide, and 95 kg of water to prepare a waterproofing agent.
[0020] Take 45kg of sulphoaluminate cement, 33kg of fly ash, 0.35kg of wood anti-cracking fiber, 3.5kg of water repellent, 0.75kg of calcium stearate, 0.25kg of polycarboxylic acid water reducing agent and 30kg of water and mix them, then add GM-A 3.0kg of foaming agent is stirred and quickly poured into the template, obtained after curing and demoulding, cutting and packaging as required.
[0021] The index of the prepared product is: the dry density is 250kg / m 3 , The foaming height is 37cm, the compressive strength is 0.85MPa, the bonding strength is 0.5MPa, the thermal conductivity is 0.45 w / (m?k), the water absorption (V / V) is 7%, and the combustion level is A1.
Example Embodiment
[0022] Example three
[0023] Take 3 kg of stearic acid, 0.3 kg of sodium carbonate, 3 kg of ammonia, 0.5 g of sodium fluoride, 3 kg of potassium hydroxide, and 90 kg of water to prepare a waterproofing agent.
[0024] Take 40kg of sulphoaluminate cement, 30kg of fly ash, 0.3kg of wood anti-cracking fiber, 3kg of water repellent, 0.6kg of calcium stearate, 0.2kg of polycarboxylic acid water reducing agent and 28kg of water and mix well, then add GM-A After stirring 2.5kg of foaming agent, quickly pour it into the template, and get it after curing and demoulding. It is cut and packaged as required.
[0025] The index of the prepared product is: the dry density is 230kg / m 3 , The foaming height is 35cm, the compressive strength is 0.7MPa, the bonding strength is 0.5MPa, the thermal conductivity is 0.45 w / (m?k), the water absorption (V / V) is 7%, and the combustion level is A1.
[0026] The product index determination is carried out in accordance with "GB8624-2006 Classification of Buildi...
PUM
Property | Measurement | Unit |
---|---|---|
Dry density | aaaaa | aaaaa |
Compressive strength | aaaaa | aaaaa |
Bond strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap