Fiber bed core with good elasticity and preparation method thereof

A technology of resilience and fiber bed, applied in the field of bed core and its preparation, can solve the problems of coconut palm fiber being susceptible to moisture and mildew, poor air permeability and elasticity, harmful to human health, etc. , the effect of good air permeability

Inactive Publication Date: 2013-04-24
SUZHOU MOWEI NATURAL FIBER MATERIAL
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above-mentioned polyester fiber coconut palm board solves the problem of using glue and hard quality of the coconut palm mattress, the coconut palm fiber itself is susceptible to moisture, mildew, and long-term insect deterioration. Long-term use is harmful to human health, and the mattress is easily deformed, and the air permeability and Elasticity is also poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber bed core with good elasticity and preparation method thereof
  • Fiber bed core with good elasticity and preparation method thereof
  • Fiber bed core with good elasticity and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A fiber bed core with good resilience performance comprises an intermediate layer 2 and surface layers arranged on the upper surface and the lower surface of the intermediate layer 2, the surface layer is composed of the following components by weight percentage: 15% PLA fiber and 85% polyethylene terephthalate fiber, the middle layer 2 is composed of the following components by weight percentage: 60% coconut palm fiber, 20% jute fiber and 20% PP fiber.

[0037] Its preparation method comprises the following steps:

[0038]In the first step, each component is weighed according to the required ratio, opened and mixed, pre-laid, carded, air-laid, and needle-punched to prepare the non-woven layers of the upper surface layer 1 and the lower surface layer 3 respectively. The non-woven layer of surface layer 1 and lower surface layer 2 is made of 15% PLA fiber and 85% polyethylene terephthalate fiber, and the needle density is 44 punches / cm 2 ;

[0039] In the second step, ...

Embodiment 2

[0053] A fiber bed core with good resilience performance, comprising an intermediate layer 2 and a surface layer arranged on the upper surface of the intermediate layer 2, the surface layer is composed of the following components by weight percentage: 40% PP fiber and 60% poly Butylene phthalate fiber, the middle layer 2 is composed of the following components by weight percentage: 45% coconut palm fiber, 15% jute fiber and 40% ES fiber.

[0054] Its preparation method comprises the following steps:

[0055] In the first step, each component is weighed according to the required ratio, opened and mixed, pre-laid, carded, air-laid, and needle-punched to prepare the non-woven layers of the upper surface layer 1 and the lower surface layer 3 respectively. The non-woven layer of surface layer 1 is made of 40% PP fiber and 60% polybutylene terephthalate fiber, and the needle density is 150 punches / cm 2 ;

[0056] In the second step, according to the ratio of 45% coconut palm fiber...

Embodiment 3

[0070] A fiber bed core with good resilience performance, comprising an intermediate layer 2 and surface layers arranged on the upper surface and the lower surface of the intermediate layer 2, the surface layer is composed of the following components by weight percentage: 30% 4080 fiber and 70% Polytrimethylene terephthalate fiber, the middle layer 2 is composed of the following components by weight percentage: 30% coconut palm fiber, 30% hemp fiber and 40% ES fiber.

[0071] Its preparation method comprises the following steps:

[0072] In the first step, each component is weighed according to the required ratio, opened and mixed, pre-laid, carded, air-laid, and needle-punched to prepare the non-woven layers of the upper surface layer 1 and the lower surface layer 3 respectively. The non-woven layer of surface layer 1 and lower surface layer 3 adopts 30% 4080 fiber and 70% polypropylene terephthalate fiber, and the needle punching density in the needle punching process is 88 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fiber bed core with good elasticity which comprises at least one intermediate layer and surface layers arranged on the upper surface or the lower surface of the intermediate layer; the surface layers comprise the following components in percentage by weight: 15-40 percent of low-melting point fiber and 60-85 percent of polyester fiber; the intermediate layer comprises the following components in percentage by weight: 60-85 percent of brown hemp fiber and 15-40 percent of low-melting point fiber, wherein the brown hemp fiber consists of coconut fiber and fibrilia in ratio of (1-4):1. The invention also discloses a preparation method of the fiber bed core, which comprises the following steps of: respectively preparing all the layers, i.e. the upper surface layer, the lower surface layer and the intermediate layer, then paving all the layers in sequence and preparing the fiber bed core through the baking, cold-milling, cooling, cutting, inspecting and packaging processes. The fiber bed core and the preparation method thereof have the benefits that the technical problems of easiness in layered fracture, insufficient elasticity, bad air permeability, mustiness and insects existing in the existing bed mattress are solved; and due to the content ratio of the coconut fiber to the brown hemp fiber, the fiber bed core has better elasticity and certain hardness; and fiber bed core is particularly suitable for middle-aged and elderly people.

Description

technical field [0001] The invention relates to a bed core, in particular to a bed core with good rebound performance and certain hardness prepared by composite fibers and a preparation method thereof. Background technique [0002] At present, most of the palm fiber bed cores are made of traditional coconut palm mattresses. Coconut palm mattresses need to be bonded with a lot of glue. If they are used for a long time, they will cause harm to human health. Long worms deteriorate, and are easy to collapse and break, and are relatively hard, poor in elasticity, and have a narrow range of use. They are mostly suitable as filling materials for hard mattresses. [0003] Publication number is that the patent of CN102174729A discloses a kind of polyester fiber coir palm board, and it comprises three layers, and upper and lower two layers of material are identical, all are to adopt low-melting point two-component skin-core fiber and three-dimensional crimped round hollow fiber; The m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A47C27/12D04H1/4382D04H1/485D04H1/435D04H1/498D04H1/732
Inventor 刘国忠陈红武
Owner SUZHOU MOWEI NATURAL FIBER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products