Flame-retardant PC/ABS (Poly Carbonate/Acrylonitrile-Butadiene-Styrene) alloy containing no halogen-system flame retardant

A flame retardant, ABS resin technology, applied in the polymer field, can solve the problems of high price, poor processing fluidity, easy stress cracking, etc., and achieve the effects of low production cost, high flame retardant level, and good processing performance.

Inactive Publication Date: 2013-04-24
浙江赛日新材料科技有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polycarbonate (PC) is an engineering plastic with excellent performance, but it has disadvantages such as poor processing fluidity, easy stress cracking, sensitivity to notch, easy wear, poor chemical resistance, and high price, which make its application in many fields restricted. limit

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Weigh 100 kg of polycarbonate, 60 kg of ABS resin, 20 kg of flame retardant, 5 kg of chlorinated polyethylene, 4 kg of EVA and 1 kg of oleic acid, wherein the flame retardant is more than 8 kg Polyaryl phosphate, 3 kg of magnesium hydroxide, 2 kg of barium hydroxide and 7 kg of potassium fluorobutane sulfonate.

[0016] Put PC pellets and ABS pellets in a vacuum drying oven, dry PC pellets at 115°C for 5 hours to obtain dry PC pellets; dry ABS pellets at 80°C for 3 hours to obtain dry ABS pellets . After mixing dry PC pellets and ABS pellets, add flame retardant, chlorinated polyethylene, EVA and oleic acid, mix evenly, place in a twin-screw screw machine, and pelletize after melt extrusion to obtain PC / ABS alloy pellets. The temperature of each zone of the twin-screw screw machine is: zone 1 temperature: 220°C, zone 2 temperature: 230°C, zone 2 temperature: 230°C, zone 4 temperature: 235°C, zone 5 temperature: 230°C, zone 6 temperature: 230 ℃; twin-screw residence t...

Embodiment 2

[0018] Prepare PC / ABS alloy in the same manner as Example 1, except that the flame retardant is 8 kilograms of polyaryl phosphate, 5 kilograms of magnesium hydroxide and 7 kilograms of potassium fluorobutylsulfonate .

Embodiment 3

[0020] PC / ABS alloy was prepared in the same manner as in Example 1, except that the flame retardant was 8 kilograms of polyaryl phosphate, 5 kilograms of barium hydroxide and 7 kilograms of potassium fluorobutyl sulfonate .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a flame-retardant PC / ABS (Poly Carbonate / Acrylonitrile-Butadiene-Styrene) alloy containing no halogen-system flame retardant. The flame-retardant PC / ABS alloy comprises 80-150 parts of polycarbonate, 40-70 parts of ABS resin, 12-30 parts of flame retardant, 1-10 parts of compatilizer, 1-10 parts of toughening agent and 1-5 parts of lubricant. The flame-retardant PC / ABS alloy has the advantages of low production cost, good machining performance, high flame-retardant grade and environmental friendliness.

Description

technical field [0001] The invention relates to the field of macromolecules, in particular to a flame-retardant PC / ABS alloy without halogen-based flame retardants. Background technique [0002] Polycarbonate (PC) is an engineering plastic with excellent performance, but it has disadvantages such as poor processing fluidity, easy stress cracking, sensitivity to notch, easy wear, poor chemical resistance, and high price, which make its application in many fields restricted. limit. The performance of acrylonitrile-butadiene-styrene (ABS) is between engineering plastics and general-purpose plastics. In order to meet the fire safety requirements of PC / ABS alloys in practical applications, the research on halogen-free and environment-friendly PC / ABS alloy materials has become the focus in the field of flame retardancy. Contents of the invention [0003] The object of the present invention is to provide a flame-retardant PC / ABS alloy without halogen-based flame retardants. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08K3/22C08K5/523C08K5/42C08K13/02
Inventor 陈维君
Owner 浙江赛日新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap