Starch-based composite blown film and preparation process of same

A blown film, starch-based technology, applied in the field of starch-based composite blown film and its preparation, can solve the problems of small starch addition, poor processing performance, poor mechanical properties, etc., and achieve good compatibility and remarkable environmental protection , the effect of widely applied value

Inactive Publication Date: 2015-04-01
HUNAN UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the defects of small starch addition, poor mechanical properties and poor processability in the existing starch-plastic composite film materials, and provide a starch-based composite film with low cost, excellent mechanical properties and transparency, and simple processing. Blown film material and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Starch-based composite blown film and preparation process of same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The starch-based composite blown film material of this embodiment consists of base material tapioca starch, bamboo fiber, acetate-esterified tapioca starch, cellulose acetate, low-density polyethylene, linear low-density polyethylene and auxiliary plasticizer glycerin, reinforcing agent agar , nano-SiO 2 , coupling agent DL-171, stearic acid, antioxidant 1076, light stabilizer o-hydroxybenzophenone, processing lubricant liquid paraffin compounded; the content of tapioca starch in the base material is 40wt%, and acetate The content of starch is 15wt%, the content of bamboo fiber is 15wt%, the content of cellulose acetate is 10wt%, the content of low-density polyethylene is 12wt%, and the content of low-density linear polyethylene in the base material is 8wt%. The dosage of the softening agent glycerin is 30wt% of the starch, the dosage of the reinforcing agent agar is 5wt% of the starch, and the nano-SiO 2 The dosage is 2.5wt% of the starch, the dosage of auxiliary coup...

Embodiment 2

[0032] In this embodiment, the starch-based composite blown film material is made of base material cornstarch, acetate-esterified cornstarch, cotton fiber, cellulose acetate butyrate, low-density polyethylene, linear low-density polyethylene and auxiliary plasticizer glycerin. Reagent agar, nano-SiO 2 , coupling agent DL-171, stearic acid, antioxidant 1076, light stabilizer o-hydroxybenzophenone, and processing lubricant liquid paraffin; the content of corn starch in the base material is 55wt%, and the acetate The content of starch is 10wt%, the content of cotton fiber is 10wt%, the content of cellulose acetate butyrate is 5wt%, the content of low-density polyethylene is 10wt%, and the content of low-density linear polyethylene in the base material is 10wt%. The dosage of agent plasticizer glycerin is 30wt% of starch, the consumption of reinforcing agent agar is 8wt% of starch, nano-SiO 2 The dosage is 2.5wt% of starch, the dosage of auxiliary coupling agent DL-171 is 3wt% of...

Embodiment 3

[0040] The starch-based composite blown film material of this embodiment consists of base material tapioca starch, acetate-esterified tapioca starch, cotton fiber, cellulose acetate, low-density polyethylene, linear low-density polyethylene and auxiliary plasticizer glycerin, reinforcing agent agar , nano-SiO 2 , coupling agent DL-171, stearic acid, antioxidant 1076, light stabilizer o-hydroxybenzophenone, and processing lubricant liquid paraffin; the content of tapioca starch in the base material is 60wt%, and acetate The content of starch is 10wt%, the content of cotton fiber is 10wt%, the content of cellulose acetate butyrate is 5wt%, the content of low-density polyethylene is 10wt%, and the content of low-density linear polyethylene in the base material is 5wt%, Auxiliary plasticizer glycerin dosage is 30wt% of starch, the dosage of strengthening agent agar is 8wt% of starch, nano-SiO 2 The dosage is 2.5wt% of starch, the dosage of auxiliary coupling agent DL-171 is 3wt% ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a starch-based composite blown film material with a high starch content and a preparation process of the same. The starch-based composite blown film material is prepared from base materials comprising natural starch, acetylated starch, plant fibres, esterified cellulose and polyethylene resin, and appropriate auxiliaries comprising starch plasticizer glycerol, enhancer agar, nano-SiO2, coupling agent DL-171, stearic acid, antioxidant 1076, light stabilizer o-hydroxyl benzophenone, and processing lubricant liquid paraffin, and is prepared by adopting a melting-blowing process. The environment-friendly type starch-based composite blown film material disclosed by the invention has the following characteristics that the added amount of starch is high; the ratio of degradation constituents can achieve 80% of the weight of the film; the film is good in surface smoothness and transparency, and high in physical and mechanical properties; the processing equipment is low in requirements; the processing technique is simple; and the material is low in cost and easy to degrade, and is a green and environment-friendly type film material which can be widely applied.

Description

technical field [0001] The invention relates to a starch-based composite blown film and its preparation process, in particular to a method of producing high starch content with natural starch, acetate starch, natural plant fiber, esterified cellulose and polyethylene resin as matrix raw materials. Method for composite blown film material with high strength. Background technique [0002] Starch plastic composite film material has excellent performance. It not only retains the characteristics of plastic film in terms of mechanical properties, but also partially overcomes the defects of plastic non-degradable. Packaging film, shopping bags, etc. [0003] Due to the serious environmental pollution caused by plastic products, the world attaches great importance to the development of degradable materials. Starch, as a cheap and abundant agricultural product, has become the main raw material for the development of degradable materials. The starch-based film materials currently ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L3/02C08L3/06C08L97/02C08L1/12C08L1/14C08L23/06C08L23/08C08K13/02C08K5/053C08K3/36C08K5/09C08K5/132B29C49/04B29C49/78B29B9/06
Inventor 陈一刘文勇李祥刚曾广胜
Owner HUNAN UNIV OF TECH