Surface spraying film agent for plant
A technology of plant and film agent, applied in the direction of plant preservation, botany equipment and methods, fertilization device, etc., can solve the problems of single function of inorganic salt film, affect plant photosynthesis, unfavorable plant growth, etc., and improve disease resistance , Improve self-growth and reduce environmental pollution
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0016] Example 1
[0017] 1. First, add 350Kg of water to a 500L reactor, and add 50kg of hydroxypropyl methylcellulose under stirring to dissolve completely. Then add 300Kg of water into a 1000L reactor, heat it to 70℃, add 30Kg of gelatin under stirring, and after it is completely dissolved, add 10Kg of sodium lauryl sulfonate and 100Kg of sodium humate, and then add the above 400Kg after cooling. Hydroxypropyl methyl cellulose aqueous solution, 80Kg polyvinyl acetate emulsion, 20Kg nano white carbon black and 60Kg lauryl alcohol polyoxyethylene ether were stirred for 1h to obtain a black-brown homogeneous suspension, the pH value of the material was 7.6, and the viscosity (painted- 4 cups, 25℃) 94s, packaged into products.
Example Embodiment
[0018] Example 2
[0019] First, add 300Kg of water into a 500L reactor, and add 30Kg of hydroxypropyl methylcellulose under stirring to dissolve completely. Then add 350Kg of water into the 1000L reactor, heat to 80℃, add 20Kg of gelatin under stirring, and after it is completely dissolved, add 1OKg of sodium octylsulfonate, 120Kg of ammonium humate, and then add the above 330Kg of hydroxypropyl after cooling. Methyl cellulose aqueous solution, 11OKg polyvinyl acetate emulsion, 1OKg nano white carbon black and 50Kg lauryl alcohol polyoxyethylene ether, stir for 1.5h to obtain a dark brown uniform suspension, the pH value of the material is 6.8, the viscosity (coating-4 cups) , 25℃) 76s, packaged into products.
Example Embodiment
[0020] Example 3
[0021] In order to understand the preventive effect of the film of the present invention on apple tree rot and provide a scientific basis for future promotion and application, in 2006, the film of the present invention was used in the 13-year-old red Fuji orchard of Zhang Haifang, Beixin Township, Linyi County. The lesion test is compared with the related drugs and the water is used as the control. The test results are shown in the following table:
[0022] Table 1 Summary of the field test of the plant protective film of the present invention to control fruit tree rot
[0023]
[0024] It can be seen from Table 1 that the control effect of the plant protective film agent of the present invention on apple tree rot disease can reach 94.15%, which is significantly higher than other agents. The callus after applying the film of the present invention grows obviously, the lesions heal quickly, and there is no adverse effect on the growth and development of the tree.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap