A kind of aeration sheet and its preparation method

A kind of aeration film and aggregate technology, applied in the field of water treatment, can solve the problems of difficult control of the aperture of the aeration film, poor aeration effect, easy access of sewage to the air distribution pipeline, etc., and achieve short preparation cycle, low production cost, and aeration good air effect

Active Publication Date: 2016-02-03
RENCHSAND ECO ENVIRONMENT PROTECTION SCI & TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For this reason, the technical problem to be solved by the present invention lies in the difficulty of controlling the pore size of the existing aeration sheet, which leads to the poor aeration effect and the problem that the sewage easily enters the air distribution pipeline, and then provides a kind of aerator with good aeration effect, and the sewage is not easy to enter the pipeline. The aeration sheet provides a preparation method of the aeration sheet with low energy consumption and little environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The aeration sheet of the present invention includes aggregate particles and a hydrophobic binder coated on the aggregate particles, and pores that gas molecules can pass through and liquid water molecules cannot pass through are formed between adjacent aggregate particles, so The diameter of the pores is 0.001-0.5mm.

[0027] The aggregate particles in this embodiment are a mixture of quartz sand and slag at a weight ratio of 5:1, the particle size of the quartz sand is 0.0065-1 mm, and the particle size of the slag is 0.016-2 mm. The hydrophobic binder is a bisphenol A saturated polyester resin, and the hydrophobic binder accounts for 1% by mass of the aggregate particles.

[0028] The aeration sheet is made by the following method:

[0029] a. Mix aggregate particles with polyester resin bisphenol A saturated polyester resin in a weight ratio of 100:1 and pour into a mixer to stir evenly;

[0030] b. Pour the aggregate particles bonded with the hydrophobic binder...

Embodiment 2

[0033] The structure of the aerator in this embodiment is basically the same as that in Embodiment 1, and the differences are:

[0034] A layer of hydrophobic polytetrafluoroethylene is coated on the aggregate particles of the aeration sheet. The aggregate particles are a mixture of quartz sand and ceramsite at a weight ratio of 4:2, the particle size of the quartz sand is 0.65-2mm, and the particle size of the ceramsite is 0.036-0.45mm. The hydrophobic polytetrafluoroethylene is 8wt% of the aggregate particles.

[0035] The method that the hydrophobic polytetrafluoroethylene is coated on the aggregate particles is:

[0036] 1) Heating the hydrophobic polytetrafluoroethylene to a molten state;

[0037] 2) When the aggregate particles are heated to 210°C, add the hydrophobic polytetrafluoroethylene, stir and mix for 30 seconds, so that the hydrophobic polytetrafluoroethylene is evenly dispersed on the surface of the aggregate particles;

[0038] 3) Add hexamethylenetetramine...

Embodiment 3

[0046] In this embodiment, the aggregate particles that make up the aeration sheet are formed by mixing ceramsite and glass beads at a weight ratio of 2:1, the particle size of the ceramsite is 0.075-0.6mm, and the glass The particle size of the microbeads is 0.04-0.15mm. The aeration sheet includes aggregate particles and a hydrophobic binder arranged between the aggregate particles, and the diameter of pores between adjacent aggregate particles is 0.1-0.3mm.

[0047] Wherein, the hydrophobic binder is a fluorine-containing epoxy resin binder 2,2-bisphenol-based hexafluoropropane diglycidyl ether, and the hydrophobic binder accounts for 4% by mass of the aggregate particles .

[0048] The aeration sheet is made by the following method:

[0049]a. Pour the aggregate granules and the hydrophobic binder into a mixer at a ratio of 25:1 and stir evenly;

[0050] b. Pour the aggregate particles bonded with the hydrophobic binder into a forming mold;

[0051] c. The aeration ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an aeration sheet and a preparation method thereof, belonging to the technical field of water treatment. The aeration sheet is formed by bonding aggregate particles and a hydrophobic binder, and pores through which gas molecules can pass but liquid water molecules cannot pass are formed between adjacent aggregate particles. The preparation method of the aeration sheet does not require high-temperature sintering. It only needs to pour the aggregate particles coated with a hydrophobic binder into a molding mold, and place it at 5-120°C for 1-48 hours to cure, mold and demould to obtain the aeration sheet. Gas slices. The aeration sheet solves the technical problem that the hole diameter of the existing aeration sheet is difficult to control, which leads to poor aeration effect and the problems that sewage easily enters the air distribution pipeline. At the same time, the preparation method of the aeration sheet solves the problems of high energy consumption and serious environmental pollution of the existing aeration sheet.

Description

technical field [0001] The invention belongs to the field of water treatment, in particular to an aeration sheet and a preparation method thereof. Background technique [0002] In the aerobic process of water treatment, microporous aerators are often used to supply oxygen to the water to meet the oxygen demand of the aerobic process. At present, the common microporous aerators for sewage treatment adopt diaphragm microporous aerators. Among them, the aerators generally include rubber diaphragms and ceramic and corundum microporous aerators. The rubber diaphragm has many opening and closing micropores. When ventilating, the pressure air source enters the base of the aerator through the pipeline. Under the action of air pressure, the rubber diaphragm slightly bulges upwards and expands the rubber diaphragm. The micropores on the sheet, the gas passes through the micropores to form small bubbles, and provides dissolved oxygen to the sewage treatment tank for biochemical treatm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C02F3/02C04B26/10C04B26/12C04B26/16C04B26/18C04B26/32
CPCC02F3/20Y02W10/10
Inventor 秦升益陈梅娟秦安川赵卿魏拓窦明岳
Owner RENCHSAND ECO ENVIRONMENT PROTECTION SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com